Ni-based amorphous alloy ribbon was prepared by a single-roller melt-spinning technique. Palladium coating was found to enhance significantly the absorption/desorption behavior of hydrogen in amorphous alloy. The hydrogen permeability of a Pd-coated $(Ni_{60}Nb_{40}){_{100-X}}$TaX(x=5, 10) amorphous alloy was examined in the temperature range of $623{\sim}773K$, comparable with those of $Pd_{60}-Cu_{40}$ alloys. The permeated hydrogen flux was increased with increasing the temperature and the difference of hydrogen pressure between the feed side and permeates side of the membrane. The Ni-based amorphous alloys were characterized by X-ray diffractometry(XRD) and differential scanning calorimetry(DSC). The morphology of surface and roughness was observed by using scanning electron microscopy(SEM) and atomic force microscopy(AFM).

• Journal of the Korean Magnetics Society
• /
• v.25 no.3
• /
• pp.67-73
• /
• 2015

This is a basic research for improving soft magnetic property of Fe based nano crystalline alloy powder core. The main study is done around characteristics of permeability, core loss, and DC bias depending on amount of insulation coating agent and particle size. First, $Fe_{73.5}Si_{13.5}B_9Nb_3Cu_1$ amorphous alloy ribbon was fabricated by using the planar flow casting (PFC) device. Then, heat treatment and ball milling were done to obtain alloy powder. The amount of polyether imide (PEI) added to it was varied by 0.5, 1.0, 2.0, 2.5 wt% to have compression molding into $16ton/cm^2$. After going through crystalline heat treatment, the made toroidal nano crystalline powder core ($OD12.7mm^*ID7.62mm^*H4.75mm$) had smaller permeability as amount of insulation coating agent decreases. However, it was found out that core loss and DC bias characteristics have been improved. The reason for this results were expected to be because green density of power core decreases as amorphous alloy powder particles become smaller as amount of alloy powder insulation coating agent increases, it was determined that 1 wt% of insulation coating agent is appropriate. Also, for powder core made based on alloy powder size with amount of insulation coating agent fixed at 1 wt%, effective permeability and core loss were outstanding as particle size became bigger. However, characteristics of DC bias became worse as applied DC field increases. This is expected to be due to insulation effect, residual pores, or molding density of powder core resulting from thickness of coating on surface of alloy powder.

• 보존과학연구
• /
• s.32
• /
• pp.75-87
• /
• 2011

The materials analysis is important in conservation science for cultural assets since conservators can make appropriate decision of treatment and environment through understanding manufacturing, period and materials. Palsapumdo is the painting of Palsapum which was given by Yi Sun-shin from the emperor Shinjong in The Ming Dynasty. Palsapumdo painted with various pigments on the fabric has remained to adhere a sheet of lining paper. In this study, we carried out the fiber identification about the fabric and lining paper and the analysis of the pigments. This study identified a fabric and a lining paper and analised pigments for the painting. As a result of fabric analysis, it was confirmed as cotton because ribbon twists and shape of kidney bean in a cross section. After the analysis of lining paper, color changed to yellow by Graff "C" staining tests, and had short fiber and tracheid. Therefore, it is supposed to be a paper which is made of conifer pulp. In addition, the results of SEM-EDS, the pigments are indicated as Orpiment($As_2S_3$), Minium($Pb_3O_4$), Hematite($Fe_2O_3$), Emeraldgreen ($C_2H_3As_3Cu_2O_8$), Ultramarine [$2(Na_2O{\cdot}Al_2O_3{\cdot}2SiO_2){\cdot}Na_2S_2$], talc[$Mg_3Si_4O_{10}(OH)_2$], bariumsulfate($BaSO_4$) and brass.

• Korean Journal of Materials Research
• /
• v.5 no.7
• /
• pp.880-887
• /
• 1995

Melt spun YB $a_2$C $u_3$A $g_{15}$ and YbB $a_2$C $u_3$A $g_{x}$(x=5, 16 and 53) precursor alloy ribbons were oxidized at 263~322$^{\circ}C$, and heat-treated at 872~89$0^{\circ}C$ under 1.0atm oxygen pressure. In addition, about ten ribbons were stacked and coupled by pressing, and then followed the same heat treatment. YB $a_2$C $u_3$ $O_{7-{\delta}}$(1-2-3) or YbB $a_2$C $u_3$ $O_{7-{\delta}}$(1-2-3) phase was formed in both the ribbons and the multilayered specimens. The formed 1-2-3 phases were not texturized in all the ribbons, but slightly texturized in the multilayered specimens. $J_{c}$ was not achieved in all the ribbons at 77K and zero magnetic field. Among the multilayered specimens, YB $a_2$C $u_3$A $g_{15}$ and YbB $a_2$C $u_3$A $g_{16}$ showed $J_{c}$ of 260 and 180A/$\textrm{cm}^2$, respectively. YB $a_2$C $u_3$A $g_{15}$ and YbB $a_2$C $u_3$A $g_{16}$ are considered to be the appropriate compositions in producing textured superconducting oxides with improved $J_{c}$ by pressing. Onset critical temperature ( $T_{on}$ ) of the multilayered YB $a_2$C $u_3$A $g_{15}$ was 92K while those of YbB $a_2$C $u_3$A $g_{x}$(x=5 , 16 and 53) were 88~90K. , 16 and 53) were 88~90K.

• Journal of the Korean Magnetics Society
• /
• v.3 no.3
• /
• pp.201-207
• /
• 1993

Starting ingot of $Pr_{15}Fe_{77}B_{8}$ were prepared by vacuum induction melting under argon atmosphere. The ingot were induction melted in a quartz crucible and then ejected as a molten alloy throuth a 0.6 mrn orifice onto a rotating cop¬per wheel. An anisotropic magnet was prepared from ribbon by hot deformation techniques. A fully dense precursor magnet first made by pressing ribbons at $680^{\circ}C$ under a pressure of $21.8\;kg/mm^{2}$. A substantially oriented magnets were obtained by die-upset under various conditions. As the compression ratio increases, the $B_{r}$ value increases pronouncedly though $_{i}H_{c}$ decreases. Also, XRD analyses show increased diffraction peak from (006). From these results, it can be known that the magnetic easy axis was formed along the compression axis. As the die-upset speed increases, $_{i}H_{c}$ increases though $B_{r}$ decreases. The $B_{r}$ increases up to $750^{\circ}C$ of die-upset temperature and above this temperature decreases. The value of $4{\pi}M_{s}$ of the $Pr_{15}Fe_{77}B_{8}$ alloy prepared is found to be 11.8 KG. When the alloy was compressed by 0.8 under the die-upset speed of 0.05 m/sec at $750^{\circ}C$, $B_{r}$ was 11.0 KG indicating that the alloy has excellent magnetic anistropy. However, this alloy has some limitation because of low $_{i}H_{c}$.