• Journal of the Korean Society for Heat Treatment
• /
• v.34 no.5
• /
• pp.233-238
• /
• 2021

The mechanical, anti-tarnishing, and corrosion characteristics of Yuggi (Cu-22wt%Sn) alloy are greatly affected by fraction of constituent phases according to heat treatment method. The Yuggi heat-treated at 750℃ has a β1' phase of 98% or more, which is a high-temperature disordered beta phase, on the other hand, cast Yuggi that Sn is solid-solutioned into Cu consists with α-phase over 60v/o. This difference of constituent phases of Yuggi may cause a difference in dissolution of Cu under antimicrobial test condition. Nonetheless, few studies have been conducted on the effect of fraction of constituent phases and constituent phases in antimicrobial activity. In addition, few studies have also been conducted on the suitable method measuring the antimicrobial activity of Yuggi. Hence, the purpose of this study is to provide an optimum measurement method of antimicrobial activity, and to evaluate quantitatively the effect of constituent phases on antimicrobial activity.

• Korean Journal of Materials Research
• /
• v.20 no.5
• /
• pp.267-270
• /
• 2010

Sn doped $In_2O_3$ (ITO) and ITO/Cu/ITO (ICI) multilayer films were prepared on glass substrates with a reactive radio frequency (RF) magnetron sputter without intentional substrate heating, and then the influence of the Cu interlayer on the methanol gas sensitivity of the ICI films were considered. Although both ITO and ICI film sensors had the same thickness of 100 nm, the ICI sensors had a sandwich structure of ITO 50 nm/Cu 5 nm/ITO 45 nm. The ICI films showed a ten times higher carrier density than that of the pure ITO films. However, the Cu interlayer may also have caused the decrement of carrier mobility because the interfaces between the ITO and Cu interlayer acted as a barrier to carrier movement. Although the ICI films had two times a lower mobility than that of the pure ITO films, the ICI films had a higher conductivity of $3.6{\cdot}10^{-4}\;{\Omega}cm$ due to a higher carrier density. The changes in the sensitivity of the film sensors caused by methanol gas ranging from 50 to 500 ppm were measured at room temperature. The ICI sensors showed a higher gas sensitivity than that of the ITO single layer sensors. Finally, it can be concluded that the ICI film sensors have the potential to be used as improved methanol gas sensors.

• Archives of design research
• /
• v.17 no.4
• /
• pp.241-250
• /
• 2004

In this research, the copper alloy plates C2200, C5210, C7701, C8113 were selected to make datum and to identify further usage of metal craft experimentation. For its experimentation, the general welding and TIG welding methods were researched; for 2nd experimentation, the Reticulation and Electroforming skill's differences in color and temperature were researched. With these methods 3 different kinds of works are introduced for sample studies. For this research, Dr. Lee, Dong-Woo who works in Poongsan Metal Co, supported 4 kinds of copper alloy metals. Which are Commercial bronze (Cu-Zn), Deoxidiged Copper(Cu-Sn-P), Nickel Silver (Cu-Ni-Zn), and White Bronze (Cu-Ni); they were applied partly and wholly by the method of Laminatin, Reticulation, Fusing, and Electroforming skills. In case of C2200, the brass, the A. C. TIG welding method is better under 2mm slight plate; the D.C. TIG welding is better upper 2mm plate; and 250~300$^{\circ}C$ is recommended for remain heat treatment. In case of C5210, not having Hydrogen in high temperature return period, doesn't need Oxygen in high temperature and hardening in comparative high temperature neither, it is good for welding. It contains Sn 2-9% ad P 0.03-0.4% generally; and in accordance with the growth rate of Sn contain amount, the harden temperature boundary become broad. In case of cold moment after welding, they are recommended that higher speed TIG welding, smaller melting site and less than 200$^{\circ}C$ for pre-heating temperature. In case of C7701, the 10-20% Ni, 15-30% Zn are widely used.. If it is upper 30% Zn, it become (${\alpha}+{\beta}$) system and adhesive power rate become lower, and the productivity become lower in low temperature but the productivity become higher in high temperature. Nickel Silver's resistance of electricity is well; and the heatproof and incorrodibility is good, too. Lastly, in case of C8113, good at persistence in salty and grind; high in strength of high temperature. In case of white brass, contain 10-30% Nickel and hardened in high temperature and become single phrase. For these reason, the crystallization particles easily become large, if the resistance become higher small amount of Pb, P, S separation rate become higher.

• Journal of the Microelectronics and Packaging Society
• /
• v.27 no.1
• /
• pp.17-24
• /
• 2020

As an interconnect scaling faces a technical bottleneck, the device stacking technologies have been developed for miniaturization, low cost and high performance. To manufacture a stacked device structure, a vertical interconnect becomes a key process to enable signal and power integrities. Most bonding materials used in stacked structures are currently solder or Cu pillar with Sn cap, but copper is emerging as the most important bonding material due to fine-pitch patternability and high electrical performance. Copper bonding has advantages such as CMOS compatible process, high electrical and thermal conductivities, and excellent mechanical integrity, but it has major disadvantages of high bonding temperature, quick oxidation, and planarization requirement. There are many copper bonding processes such as dielectric bonding, copper direct bonding, copper-oxide hybrid bonding, copper-polymer hybrid bonding, etc.. As copper bonding evolves, copper-oxide hybrid bonding is considered as the most promising bonding process for vertically stacked device structure. This paper reviews current research trends of copper bonding focusing on the key process of Cu-SiO₂ hybrid bonding.

• Journal of Powder Materials
• /
• v.13 no.5 s.58
• /
• pp.351-359
• /
• 2006

Ni based($Ni_{57}Zr_{20}Ti_{18}Si_2Sn_3$) bulk metallic glass(BMG) powders were produced by a gas atomization process, and ductile Cu powders were mixed using a spray drying process. The Ni-based amorphous powder and Cu mixed Ni composite powders were compacted by a spark plasma sintering (SPS) processes into cylindrical shape. The relative density varied with the used SPS mold materials such as graphite, hardened steel and WC-Co hard metal. The relative density increased from 87% to 98% when the sintering temperature increased up to $460^{\circ}C$ in the WC-Co hard metal mold.

• Progress in Superconductivity and Cryogenics
• /
• v.11 no.3
• /
• pp.1-5
• /
• 2009

It is important to predict AC loss in $Nb_3Sn$ and NbTi cable-in-conduit-conductor (CICC) reliably for the design and operation of large superconducting coils. The hysteresis loss in the superconducting filaments and coupling loss within strands and among strands in a cable or composite are dominant ac losses in superconducting magnets. The coupling loss in a superconductor can be characterized by identifying the coupling constant time $n{\tau}$. To reduce the coupling loss, all the strands (superconductor and Cu) in KSTAR (Korea Superconducting Tokamak Advance Research) are chromium plated with thickness of $l{\pm}0.5{\mu}m$. The ac losses of PF1, PF5 and PF6 coils has been measured by calorimetric method while applying trapezoidal current pulses with various ramp rate from 0.5 kA/s to 2 kA/s. The coupling time constants for $Nb_3Sn$ coils are $25{\sim}55$ ms and the values are not co-related with the coil size, the time constants for NbTi coil is 30 ms.

• Restorative Dentistry and Endodontics
• /
• v.22 no.1
• /
• pp.1-33
• /
• 1997

The objective of this study was to analyze the in vitro and in vivo corrosion products of low and high copper amalgams. The four different types of amalgam alloy used in this study were Fine cut, Caulk spherical, Dispersalloy, and Tytin. After each amalgam alloy and Hg were triturated according to the directions of the manufacturer by means of the mechanical amalgamator(Amalgam mixer. Shinhung Co. Korea), the triturated mass was inserted into a cylindrical metal mold which was 12mm in diameter and 10mm in height. The mass was condensed by 150Kg/cm compressive force. The specimen was removed from the mold and aged at room temperature for about seven days. The standard surface preparation was routinely carried out by emery paper polishing under running water. In vitro amalgam specimens were potentiostatically polarized ten times in a normal saline solution at $37^{\circ}C$(potentiostat : HA-301. Hukuto Denko Corp. Japan). Each specimen was subjected to anodic polarization scan within the potential range -1700mV to+400mV(SCE). After corrosion tests, anodic polarization curves and corrosion potentials were obtained. The amount of component elements dissolved from amalgams into solution was measured three times by ICP AES(Inductive Coupled Plasma Atomic Emission Spectrometry: Plasma 40. Perkim Elmer Co. U.S.A.). The four different types of amalgam were filled in occlusal and buccal class I cavities of four human 3rd molars. After about five years the restorations were carefully removed after tooth extraction to preserve the structural details including the deteriorated margins. The occlusal surface, amalgam-tooth interface and the fractured surface of in vivo amalgam corrosion products were analyzed. In vivo and in vitro amalgam specimens were examined and analyzed metallographically by SEM(Scanning Electron Microscope: JSM 840. Jeol Co. Japan) and EDAX(Energy Dispersive Micro X-ray Analyser: JSM 840. Jeol Co. Japan). 1. The following results are obtained from in vitro corrosion tests. 1) Corrosion potentials of all amalgams became more noble after ten times passing through the in vitro corrosion test compared to first time. 2) After times through the test, released Cu concentration in saline solution was almost equal but highest in Fine cut. Ag and Hg ion concentration was highest in Caulk spherical and Sn was highest in Dispersalloy. 3) Analyses of surface corrosion products in vitro reveal the following results. a)The corroded surface of Caulk spherical has Na-Sn-Cl containing clusters of $5{\mu}m$ needle-like crystals and oval shapes of Sn-Cl phase, polyhedral Sn oxide phase. b)In Fine cut, there appeared to be a large Sn containing phase, surrounded by many Cu-Sn phases of $1{\mu}m$ granular shapes. c)Dispersalloy was covered by a thick reticular layer which contained Zn-Cl phase. d)In Tytin, a very thin, corroded layer had formed with irregularly growing Sn-Cl phases that looked like a stack of plates. 2. The following results are obtained by an analysis of in vivo amalgam corrosion products. 1) Occlusal surfaces of all amalgams were covered by thick amorphous layers containing Ca-P elements which were abraded by occlusal force. 2) In tooth-amalgam interface, Ca-P containing products were examined in all amalgams but were most clearly seen in low copper amalgams. 3) Sn oxide appeared as a polyhedral shape in internal space in Caulk spherical and Fine cut. 4) Apical pyramidal shaped Sn oxide and curved plate-like Sn-Cl phases resulted in Dispersalloy. 5) In Tytin, Sn oxide and Sn hydroxide were not seen but polyhedral Ag-Hg phase crystal appeared in internal space which assumed a ${\beta}_l$ phase.

• Journal of Welding and Joining
• /
• v.34 no.5
• /
• pp.70-76
• /
• 2016

In this study, Microstructure and tensile properties in arc brazed joints of 1000MPa grade DP steel using Cu-Si insert metal were investigated. The fusion zone was composed of Cu phase which solidified a little Fe and Si. The former phase formed due to dilute the edge of base material by arc, although Fe was not solid solution in Cu at the room temperature. Cu3Si particles formed by crystallization at $1100^{\circ}C$ during faster cooling. After the tensile shear test, there are no differences between the brazed joint efficiencies. The maximum joint efficient was about 37% compared to strength of base metal. It is better than that of arc brazed joint of DP steel using Cu-Sn filler metal. Fracture position of all brazing conditions was in the fusion zone. Crack initiation occurred at three junction point which was a stress singularity point of upper sheet, lower sheet and the fusion zone. And then crack propagated across the fusion zone. The reason why the fracture occurred at fusion zone was that the hardness of fusion zone was lower than that of base material and heat affected zone. The correlation among maximum load and hardness of fusion zone and EST at fractured position was $R^2=0.9338$. Therefore, this means that hardness and EST can have great impact on maximum load.

• Journal of Welding and Joining
• /
• v.32 no.6
• /
• pp.75-81
• /
• 2014

Usage of heavy metal element (Pb, Hg and Cd etc.) in electronic devices have been restricted due to the environmental banning of the European Union, such as WEEE and RoHS. Therefore, it is needed to develop the Pb-free solder plated ribbon in photovoltaic (PV) module. This study described that degradation characteristics of PV module under damp heat (DH, $85^{\circ}C$ and 85% R.H.) condition test for 1,000 h. Solar cell ribbons were utilized to hot dipping plate with Pb-free solder alloys. Two types of Pb-free solder plated ribbons, Sn-3.0Ag-0.5Cu (SAC305) and Sn-48Bi-2Ag, and an electroless Sn-40Pb solder hot dipping plated ribbon as a reference sample were prepared to evaluate degradation characteristics. To detect the degradation of PV module with the eutectic and Pb-free solder plated ribbons, I-V curve, electro-luminescence (EL) and cross-sectional SEM analysis were carried out. DH test results show that the reason of maximum power (Pm) drop was mainly due to the decrease fill factor (FF). It was attributed to the crack or oxidation of interface between the cell and the ribbon. Among PV modules with the eutectic and Pb-free solder plated ribbon, the PV module with SAC305 ribbon relatively showed higher stability after DH test than the case of PV module with Sn-40Pb and Sn-48Bi-2Ag solder plated ribbons.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.1
• /
• pp.1-8
• /
• 2017

Catalytic synthesis and properties of ${\beta}-Ga_2O_3$ nanowires grown by metal organic chemical vapor deposition are reported. Au, Ni and Cu catalysts were suitable for the growth of $Ga_2O_3$ nanowires under our experimental conditions. The $Ga_2O_3$ nanowires grown by using Au, Ni and Cu catalysts showed different growth rates and morphologies in each case. We found the $Ga_2O_3$ nanowires were grown by the Vapor-Solid (VS) process when Ni was used as a catalyst while the Vapor-Liquid-Solid (VLS) was a dominant process in case of Au and Cu catalysts. Also, we found nanowires showed different optical properties depend on catalytic metals. On the other hand, for the cases of Ti, Sn and Ag catalysts, nanowires could not be obtained under the same condition of Au, Cu and Ni catalytic synthesis. We found that these results are related to the different characteristics of each catalyst, such as, melting points and phase diagrams with gallium metal.