• Proceedings of the Korean Magnestics Society Conference
• /
• 1996.10a
• /
• pp.54-55
• /
• 1996

• Proceedings of the Korean Magnestics Society Conference
• /
• 1996.10a
• /
• pp.56-57
• /
• 1996

• Proceedings of the Korean Magnestics Society Conference
• /
• 1997.11a
• /
• pp.116-117
• /
• 1997

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1993.11a
• /
• pp.54-55
• /
• 1993

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1993.11a
• /
• pp.56-57
• /
• 1993

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1994.04c
• /
• pp.16-17
• /
• 1994

• Journal of the Korean Society for Precision Engineering
• /
• v.16 no.12
• /
• pp.71-77
• /
• 1999

In this study, Cu ferrite was machined with cermet tool to clarify the machinability. The main conclusions obtained were as follows. The tool wear becomes the smallest at the cutting speed of 90m/min with the depth of cut of 0.2mm. The surface roughness becomes larger with increasing the cutting speed and the chamfer angle. The tool with the chamfer angle of $15{\circ}$ shows the best performance. The surface roughness increases almost proportionally with the increase of the chip size. The tool wear decreases with increasing feed in the depth of cut not more than 0.2mm.

• Korean Journal of Materials Research
• /
• v.5 no.5
• /
• pp.512-517
• /
• 1995

EMI 대책용 전자파 흡수체로 알려진 cu-Ni-쿠 페라이트를 분말야금법으로 제조하여, 성형압력과 소결온도의 변화에 따른 미세조직을 과낯ㄹ하고, 투과반사법으로 전자파 흡수능을 측정하여 조직과의 관계로 검토하였다. 하소는 공기중에서 90$0^{\circ}C$로 2시간동안 행하는 것이 최적이었다. 미세조직과 입자의 크기는 성형압과 소결온도로 제어할 수 있다. 100Mpa로 성형한 것이 치밀하고, 전자파 흡수특성이 우수하였다. 복소유전율과 복소투자율은 기공도와 소결밀도에 영향을 받았다. 전자파흡수능은 밀도보다는 입자의 크기에 더 큰 영향을 받았다.

• Proceedings of the KIEE Conference
• /
• 2000.07c
• /
• pp.1652-1654
• /
• 2000

고상반응법을 이용하여 $Ni_{0.6-x}Cu_{x}Zn_{0.4}Fe_{2}O_4$(x=0, 0.1, 0.2, 0.3) ferrite 분말을 제조하고 1200$^{\circ}C$에서 열처리하여 Cu 첨가에 따른 입자변화와 전자파흡수 특성과의 관계를 조사하였다. Ni를 Cu로 0.1 mol 치환했을 때 까지는 포화자화 및 전자파흡수능이 치환하지 않았을 때와 거의 비슷하였으나, 그 이상 첨 가시는 직선적으로 감소하였다.

• Journal of the Korean Magnetics Society
• /
• v.17 no.6
• /
• pp.232-237
• /
• 2007

We have synthesized the low temperature sintered of Ni-Zn-Cu ferrite with nonstoichiometric composition a little deficient in $Fe_2O_3$ from $(Ni_{0.2}Cu_{0.2}Zn_{0.6})_{1+x}(Fe_2O_3)_{1-x}$. For low loss and acceleration of grain growth $TiO_2$ and $Li_2CO_3$ was added from 0.25 mol% to 1.0 mol%. The mixture of the law materials was calcinated and milled. The compacts of toroidal type were sintered at different temperature $(875^{\circ}C,\;900^{\circ}C,\;925^{\circ}C\;950^{\circ}C)$ for 2 hours in air followed by an air cooling. Then, effects of composition and sintering temperatures on the physical properties such as density, resistivity, magnetic induction, coercive force, initial permeability, and quality factor of the Ni-Zn-Cu ferrite were investigated. The density of the Ni-Zn-Cu ferrite was $4.85\sim5.32g/cm^3$, resistivity revealed $10^8\sim10^{12}\Omega-cm$. The magnetic properties obtained from the aforementioned Ni-Zn-Cu ferrite specimens were 1,300 gauss for the maximum induction, 4.5 oersted for the coercive force, 275 for the initial permeability, and 83 for the quality factor. The physical properties indicated that the specimens could be utilized as the core of high frequency range (involved microwave range) communication and deflection yoke of T.V.