• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.2
• /
• pp.37-45
• /
• 2008

In this study, reliabilities of Cu (60 um)/SnAg (20 um) double-bump flip chip assemblies were investigated for the flip chip interconnections on organic substrates with 100 um pitch. After multiple reflows at $250^{\circ}C\;and\;280^{\circ}C$, bump contact resistances were almost same regardless of number of reflows and reflow temperature. In the high temperature storage test, there was no bump contact resistance change at $125^{\circ}C$ up to 2000 hours. However, bump contact resistances slightly increased at $150^{\circ}C$ due to Kirkendall voids formation. In the electromigration test, Cu/SnAg double-bump flip chip assemblies showed no electromigration until about 600 hours due to reduced local current density. Finally, in the thermal cycling test, thermal cycling failure mainly occurred at Si chip/Cu column interface which was found out the highest stress concentration site in the finite element analysis. As a result, Al pad was displaced out under thermal cycling. This failure mode was caused by normal compressive strain acting Cu column bumps along perpendicular direction of a Si chip.