• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.391-391
• /
• 2011

Crystalline silicon solar cell을 양산에 적용하기 위해 전면 전극의 패턴을 형성하는 방법으로 Ag paste를 이용한 screen printing이 가장 일반적으로 사용된다. 전면 전극의 패턴 형성 시, Finger의 width와 spacing은 Fill factor, JSC, VOC 등 태양전지의 중요 parameter들과 관련되어, 효율에 영향을 미치기 때문에, printing 시 Finger width와 spacing을 최적화하여 최대한의 효율을 내는 조건을 찾는 것이 바람직하다. 본 연구에서는 Finger width를 $30{\mu}m{\sim}100{\mu}m$, spacing을 $1.8{\mu}m{\sim}2.8{\mu}m$ 까지 가변하여 c-Si solar cell을 제작하였으며, 제작된 cell의 LIV를 측정을 통하여, 최적의 효율을 내는 조건을 찾고자 하였다. 그 결과 Finger width $30{\mu}m$, Finger spacing $1.8{\mu}m$의 조건에서 17.12%로 최고의 효율을 나타내었다.

• 한국태양에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.383-387
• /
• 2009

Multi-crystalline silicon surface etching without grain-boundary delineation is a challenging task for the fabrication of high efficiency solar cell. The use of sodium hydroxide - sodium hypochlorite (NaOH40% + NaOCl 12%) solution for texturing multi-crystalline silicon wafer surface in solar cell fabrication line is reported in this article. in light current-voltage results, the cells etched in NaOH 40% + NaOCl 12% = 1:2 exhibited higher short circuit current and open circuit voltage than those of the cells etched in NaOH 40% + NaOCl 12% = 1:1 solution. we have obtained 15.19% conversion efficiency in large area(156cm2) multi-Si solar cells etched in NaOH 40% + NaOCl 12% = 1:1 solution.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.10
• /
• pp.2909-2912
• /
• 2010

Hydrogenated microcrystalline silicon (${\mu}c$-Si:H) thin film for solar cells is prepared by plasma-enhanced chemical vapor deposition and physical properties of the ${\mu}c$-Si:H p-layer has been investigated. With respect to stable efficiency, this film is expected to surpass the performance of conventional amorphous silicon based solar cells and very soon be a close competitor to other thin film photovoltaic materials. Silicon in various structural forms has a direct effect on the efficiency of solar cell devices with different electron mobility and photon conversion. A Raman microscope is adopted to study the degree of crystallinity of Si film by analyzing the integrated intensity peaks at 480, 510 and $520\;cm^{-1}$, which corresponds to the amorphous phase (a-Si:H), microcrystalline (${\mu}c$-Si:H) and large crystals (c-Si), respectively. The crystal volume fraction is calculated from the ratio of the crystalline and the amorphous phase. The results are compared with high-resolution transmission electron microscopy (HR-TEM) for the determination of crystallinity factor. Optical properties such as refractive index, extinction coefficient, and band gap are studied with reflectance spectra.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.55 no.12
• /
• pp.565-569
• /
• 2006

Plasma enhanced chemical vapor deposition(PECVD) is a well established technique for the deposition of hydrogenated film of silicon nitride (SiNx:H), which is commonly used as an antireflection coating as well as passivating layer in crystalline silicon solar cell. PECVD-SiNx:H films were investigated by varying the deposition and annealing conditions to optimize for the application in silicon solar cells. By varying the gas ratio (ammonia to silane), the silicon nitride films of refractive indices 1.85 - 2.45 were obtained. The film deposited at $450^{\circ}C$ showed the best carrier lifetime through the film deposition rate was not encouraging. The film deposited with the gas ratio of 0.57 showed the best carrier lifetime after annealing at a temperature of $800^{\circ}C$. The single crystalline silicon solar cells fabricated in conventional industrial production line applying the optimized film deposition and annealing conditions on large area substrate of size $125mm{\times}125mm$ (pseudo square) was found to have the conversion efficiencies as high as 17.05 %. Low cost and high efficiency silicon solar cells fabrication sequence has also been explained in this paper.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.489-489
• /
• 2011

The effect of Si quantum dots for solar cell appications was investigated. The 5 ~ 10 nm Si nanoparticle was fabricated on p-type single and poly crystalline wafer by magnetron sputtering and laser irradiation process. Scanning electron microscopy (SEM), atomic force measurement (AFM) and transmission electron microscopy (TEM) images showed that the Si QDs array were clearly embedded in insulating layer ($SiO_2$). Photoluminesence (PL) measurements reliably exhibited bandgap transitions with every size of Si QDs. The photo-current measurements were showed different result with size of QD and number of superlattice.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.10
• /
• pp.754-759
• /
• 2013

Aluminum oxide($Al_2O_3$) film deposited by atomic layer deposition (ALD) is known to supply excellent surface passivation properties on crystalline Si surfaces. Since $Al_2O_3$ has fixed negative charge, it forms effective surface passivation by field effect passivation on the rear side in p-type silicon solar cell. However, $Al_2O_3$ layer formed by ALD process needs very long process time, which is not applicable in mass production of silicon solar cells. In this paper, plasma-assisted ALD(PA-ALD) was applied to form $Al_2O_3$ to reduce the process time. $Al_2O_3$ synthesized by ALD on c-Si (100) wafers contains a very thin interfacial $SiO_2$ layer, which was confirmed by FTIR and TEM. To improve passivation quality of $Al_2O_3$ layer, the deposition temperature was changed in range of $150{\sim}350^{\circ}C$, then the annealing temperature and time were varied. As a result, the silicon wafer with aluminum oxide film formed in $250^{\circ}C$, $400^{\circ}C$ and 10 min for the deposition temperature, the annealing temperature and time, respectively, showed the best lifetime of 1.6ms. We also observed blistering with nanometer size during firing of $Al_2O_3$ deposited on p-type silicon.

• Journal of the Korean Vacuum Society
• /
• v.21 no.1
• /
• pp.62-68
• /
• 2012

The conversion efficiency of solar cells depending on incident angle of light is important for building-integrated photovoltaics (BIPV) applications. The quantum efficiency is the ratio of the number of charge carriers collected by the solar cell to the number of photons of a given energy shining on the solar cell. The analysis of angle dependence of quantum efficiencies give more information upon the variation of power output of a solar cell by the incident angle of light. The variations in power output of solar cells with increasing angle of incidence is different for the type of cell structures. In this study we present the results of the quantum efficiency measurement of single-crystalline silicon solar cells and a-Si:H thin-film solar cells with the angle of incidence of light. As a result, as the angle of incidence increases in single-crystalline silicon solar cells, quantum efficiency at all wavelength (300~1,100 nm) of light were reduced. But in case of a-Si:H thin-film solar cells, quantum efficiency was increased or maintained at the angle of incidence from 0 degree to about 40 degrees and dramatically decrease at more than 40 degrees in the range of visible light. This results of quantum efficiency with increasing incident angle were caused by haze and interference effects in thin-film structure. Thus, the structural optimization considering incident angle dependence of solar cells is expected to benefit BIPV.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.365-365
• /
• 2010

In this paper, silicon nitride thin films with different silane and ammonia gas ratios were deposited and characterized for the antireflection and passivation layer of high efficiency single crystalline silicon solar cells. As the flow rate of the ammonia gas increased, the refractive index decreased and the band gap increased. Consequently, the transmittance increased due to the higher band gap and the decrease of the defect states which existed for the 1.68 and 1.80 eV in the SiNx films. The reduction in the carrier lifetime of the SiNx films deposited by using a higher $NH_3/SiH_4$ flow ratio was caused by the increase of the interface traps and the defect states in/on the interface between the SiNx and the silicon wafer. The silicon and nitrogen rich films are not suitable for generating both higher carrier lifetimes and transmittance. These results indicate that the band gap and the defect states of the SiNx films should be carefully controlled in order to obtain the maximum efficiency for c-Si solar cells.

• 한국태양에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.246-250
• /
• 2009

String & tabbing step in the crystalline PV module manufacturing process for the temperature directly affects solar cells. In fact, in the manufacture of PV modules tend to be temperature factor and the corresponding changes n the output shows the same characteristics. In this journal, it will be considered about thermal characteristics, especially changes of characteristic in high temperature of the solar cell through experiment that we measure electric output characteristics of solar cells after those are applied with high temperature changes for two seconds. And we can think about the possibility of efficiency improvements over looks in PV module manufacturing processes.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.12
• /
• pp.1015-1020
• /
• 2012

Resistance of the front electrode is the highest proportion of the ingredients of the series resistance in crystalline silicon solar cell. While resistance of the front electrode is decreased with larger area, it induces the optical loss, causing the conversion efficiency drop. Therefore the front electrode with high aspect ratio increasing its height and decreasing is necessary for high-efficiency solar cell in considering shadowing loss and resistance of front electrode. In this paper, we used the screen printing method to form high aspect ratio electrode by multiple printing. Screen printing is the straightforward technology to establish the electrodes in silicon solar cell fabrication. The several printed front electrodes with Ag paste on silicon wafer showed the significantly increased height and slightly widen finger. As a result, the resistance of the front electrode was decreased with multiple printing even if it slightly increased the shadowing loss. We showed the improved electrical characteristics for c-Si solar cell with repeatedly printed front electrode by 0.5%. It lays a foundation for high efficiency solar cell with high aspect ratio electrode using screen printing.