• Progress in Superconductivity and Cryogenics
• /
• v.1 no.2
• /
• pp.15-19
• /
• 1999

For large scale applications of high temperature superconductor (HTS) such as transmission cables, motors and generators, long length of flexible HTS conductor is required. Currently, Bi-2223 HTS tape is capable of being fabricated in longer than 100 m length by industrial processes. In this study, we fabricated 100 m 19 filamentary Bi-2223 ($Bi_{1.8}Pb_{0.4}Sr_2Ca_2O_{10+x}$) HTS tape by PIT (Power in Tube) process. Critical current(IC) of this long length tape was measured 18.5 A at 77K, self field. Critical current of 100 m length tape was mainly resulted from the increase of inhomogeneity in oxide from the increase of inhomogeneity in oxide layer. Engineering critical current (Je=Ic/total tape cross-section area) that is important factor for practical applications and fabrication cost was measured 2.2 kA/cm2.

• Progress in Superconductivity
• /
• v.1 no.2
• /
• pp.95-98
• /
• 2000

We have studied critical currents of $YBa_2Cu_3O_7$ step-edge junctions with different step orientations with respect to the major axes of $SrTiO_3$ (100) substrates. The junctions were prepared by pulsed laser deposition and argon ion milling with photoresist mask. We investigated current-voltage characteristics and critical current of the junctions as a function of the angle. The junction critical current showed an angle dependent modulation with maxima near 0 or 90 degree and minima near 45 and 135 degrees. The experimental results were analyzed based on the microstructure of the junction along the step and the d-wave symmetry of $YBa_2Cu_3O_7$ superconductor.

• Proceedings of the KIEE Conference
• /
• 1997.07a
• /
• pp.260-263
• /
• 1997

In this paper, we describe the mechanical strain effects on the critical current density of HTS (BSCCO) pancake-type-magnet. Firstly the strain of pancake coil is calculated in terms of coil length, which is also a function of angle, and then the critical current density degradation due to strain is calculated along the coil. We assumed that the critical current density degradation pattern is same with that of $Nb_{3}Sn$. We also modelled the effects of magnetic field on the critical curent degradation, and the results are compared with those with null magnetic field.

• Progress in Superconductivity and Cryogenics
• /
• v.11 no.2
• /
• pp.11-14
• /
• 2009

We estimated the critical current distribution of the long length CCs using hall probe method, and checked the reliability by comparing with the four-probe dc transport method. The deviation ratio of $I_{c-T}$ (a measured critical current by four probe dc transport method) and $I_{c-H}$ (calculated critical current by formula (3).) was nearly smaller than 12%. The Hall probe method appeared powerful to evaluate the critical current of CCs in a reel to reel system.

• Progress in Superconductivity
• /
• v.3 no.1
• /
• pp.130-133
• /
• 2001

A multifilamentary Bi-2223 HTS tape for superconducting power applications was studied through the fabrication of 250-meter long tapes by the PIT(powder in tube) process. To fabricate continuous long wire, a drawing machine, a two-drum bull block and a rolled tape winding machine were developed. Especially, 250-meter long tapes were heat treated in the shape of pancake coil to reduce the heat affect zone and to achieve the high critical current. Engineering critical current density was improved through both the enhancements of critical current density by control of thermal process and the increase of filling factor by using thin Ag alloy sheath tubes less than 1.5 mm in thickness. We have made successfully 250-meter long 37 filamentary tapes with high filling factor up to 31 % employing the modified drawing and rolling technique. The critical current of 250-meter long tapes with pancake coil type was measured by transport method at self-field up to 250 gauss of center field. The measured values, based on the transport critical current at self-field, $I_{c}$ -B characteristics and magnetic field analysis, are 34 A of I$_{c}$ and 4.0 $kA/\textrm{cm}^2$ of $J_{e}$ at 250 m, 77 K, and 0 T. We also have achieved the 56 A of I$_{c}$ and 7.0 $0 kA/\textrm{cm}^2$ of$ J_{e}$ in short tapes at 77K, self-field, and 1$mutextrm{V}$/cm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.05a
• /
• pp.252-255
• /
• 1996

Superconducting current lead is one of the promising applications of the oxide high-Tc superconductors, because they have the advantage of decreasing heat conduction to low temperature region, comparing with a conventional cooper alloy lead. High critical current density is a key factor for the applications such as current lead. (Bi,Pb)$_2$Sr$_2$Ca$_2$Cu$_3$O$\_$x/ high Tc superconductor haute been investigated in terms of critical current density. Bi-2223 superconducting current lead made by CIP and solid state sintering process. Bi-2223 current lead that heat treated at 836$^{\circ}C$ for 240 h in 1/13 P$\_$O$_2$/ had over 150 A/$\textrm{cm}^2$ of critical current density at 77K. We knew that the superconducting properties of tube type current leads were better than rods type of them. And we investigated the relation of Bi-2223 formation and heat treatment condition by XRD and SEM analysis.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.1
• /
• pp.69-73
• /
• 2001

In this study, we fabricated Bi-2223/Ag high temperature superconducting tapes using PIT(Powder-In-Tube) process to apply the superconducting magnet, cable and etc. It is inevitable to deform the superconducting taps with axial strain for application. Therefore, for the characterization of the strain sensitivity of the superconducting properties, the degradation of Bi-2223/Ag tapes due to axial strain were investigated by measuring the critical current as a function of applied tension strain and external magnetic field. The critical current of Bi-2223/Ag tapes were decreased slightly up to 0.3∼0.4% applied strain but, drastically decreased more than these strains. Superconducting filament cores consisted of brittle ceramic fibers were broken easily by the large strain and current path were decreased simultaneously.

• Progress in Superconductivity
• /
• v.11 no.2
• /
• pp.158-161
• /
• 2010

We measured the critical current of a Cooper pair transistor consisting of two Josephson junctions and a gate electrode. The Cooper pair transistors were fabricated by using electron-beam lithography and double-angle evaporation technique. The Gate voltage dependence of critical current was measured by observing voltage jumps at various gate voltages while sweeping bias current. The observed oscillation was 2e-periodic, which shows the Cooper pair transistor had low level of quasiparticle poisoning.

• Progress in Superconductivity
• /
• v.3 no.1
• /
• pp.65-69
• /
• 2001

We measured the transport properties of$ YBa_2$$Cu_3$$O_{x}$ ramp-edge junction fabricated with interface-engineered barrier. The current-voltage characteristics show a typical resistively-shunted junction like behavior Voltage noise measurement revealed that the main source of the 1/f noise is the critical current and resistance fluctuations. The analysis of the noise data showed that the critical current fluctuations increase with temperature, whereas the resistance fluctuations are almost constant, and both fluctuations are almost correlated. The smaller magnitude of the critical current and resistance fluctuations seems to result from the columnar-deflects.s.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.810-813
• /
• 2000

In this study, we fabricated Bi-2223/Ag high temperature superconducting tapes using PIT (Powder-In-Tube) process to apply the superconducting magnet, cable and etc. It's inevitable to deform the superconducting tapes with axial strain for application. Therefore, for the characterization of the strain sensitivity of the superconducting properties, the degradation of Bi-2223/Ag tapes due to axial strain were investigated by measuring the critical current as a function of applied tension strain and external magnetic field. The critical current of Bi-2223/Ag tapes were decreased slightly up to 0.3∼0.4% applied strain but, drastically decreased more than these strains. Superconducting filament cores consisted of brittle ceramic fibers were broken easily by the large strain and current path were decreased simultaneously.