• 한국지구물리탐사학회:학술대회논문집
• /
• 2009.10a
• /
• pp.155-159
• /
• 2009

Crack-controlled method which utilizes the dynamic energy such as explosives and propellent gases have been applied to the development of mineral resource and oil and civil engineering. It is necessary to consider the fracture processes associated with the material properties and external forces to control crack propagation using borehole pressure. To investigate the influence of the applied borehole pressure waveform on the crack propagation in rock masses having different material properties, a no-free surface model was used, consisting of a borehole in rock with a continuous boundary. Loading rates ranging from 1 to 100MPa/${\mu}s$ with different rock mass properties was employed to investigate the loading rate dependency of fracture patterns in the rock mass.

• Journal of the Korea Concrete Institute
• /
• v.23 no.1
• /
• pp.109-120
• /
• 2011

This paper presents an experimental study results on the crack control of flexure-dominant reinforced concrete beams repaired with strain-hardening cement composite (SHCC). Five RC beams were fabricated and tested until failure. One unrepaired RC beam was a control specimen (CBN) and remaining four speciemens were repaired with SHCC materials. The test parameters included two types of SHCC matrix ductility and two types of repair method (patching and layering). Test results demonstrated that RC beams repaired with SHCC showed no concrete crushing or spalling until final failure, but numerous hair cracks were observed. The control specimen CBN failed due to crushing. It is important to note that SHCC matrix can improve crack-damage mitigation and flexural behavior of RC beams such as flexural strength, post peak ductility, and energy dissipation capacity. In the perspective of crack width, crack widths in RC beams repaired with SHCC had far smaller crack width than the control specimen CBN under the same deflection. Especially, the specimens repaired with SHCC of PVA0.75%+PE0.75% showed a high durability and ductility. The crack width indicates the residual capacity of the beam since SHCC matrix can delay residual capacity degradation of the RC beams.