In this study, CT specimens were prepared from spring steel(SPS5) processed shot peening. The fatigue crack growth tests were carried out in the environment of the room temperature md low temperature at $25^{\circ}C$, $-30^{\circ}C$, $-50^{\circ}C$, $-70^{\circ}C$ $-100^{\circ}C$ and $-150^{\circ}C$ in the range of stress ratio of 0.05 by means of opening mode displacement. The threshold stress intensity factor range ΔKth in the early stage of fatigue crack growth (Region I) and stress intensity factor range $\Delta$K in the stable of fatigue crack growth (Region II) were decreased in proportion to descend temperature. It was shown that the fatigue resistance characteristics and fracture strength at low temperature are considerable higher than those of mom temperature in the early stage and stable of fatigue crack growth region.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2000.10a
• /
• pp.147-153
• /
• 2000

The fatigue crack propagation behavior of the SA516/70 steel which is used for pressure vessels was examined experimentally at room temperature, $150^{\circ}C$, $250^{\circ}C$ and $370^{\circ}C$ with stress ratio of R=0.1 and 0.3. The fatigue crack propagation rate da/dN related with the stress intensity factor range $\Omega\textrm{K}$ was influenced by the stress ratio within the stable growth of fatigue crack(Region II) with an increase in $\Omega\textrm{K}$. The resistance to the fatigue crack growth at high temperature is higher in comparison with that at room temperature, and the resistance attributed to the extent of plasticity-induced by compressive residual stress according to the cyclic loads. Fractographic examinations reveal that the differences of the fatigue crack growth characteristics between room and high temperatures are mainly explained by the crack closure and oxide-induced by high temperature.

• Journal of Ocean Engineering and Technology
• /
• v.15 no.2
• /
• pp.105-110
• /
• 2001

The fatigue crack propagation behavior of the SA516/70 steel which is used for pressure vessels was examined experimentally at room temperature, 150$^{\circ}C $, 250$^{\circ}C $ and 370$^{\circ}C $ with stress ratio of R=0.1 and 0.3. The fatigue crack propagation rate da/dN related with the stress intensity factor range $\Delta K$ was influenced by the stress ratio within the stable growth of fatigue crack(Region II) with an increase in $\Delta K$. The resistance to the fatigue crack growth at high temperature is higher in comparison with that at room temperature, and the resistance attributed to the extent of plasticity-induced by compressive residual stress according to the cyclic loads. Fractographic examinations reveal that the differences of the fatigue crack growth characteristics between room and high temperature are mainly explained by the crack closure and oxide-induced by high temperature.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.8
• /
• pp.1163-1172
• /
• 2001

The two dimensional problem of a layered tribological system(TiN/Steel) containing a vertical surface breaking crack and subject to rolling contact is considered in this study. Using finite elements and stress extrapolation method, a series of preliminary models are developed. Preliminary results indicate that the extrapolation technique is valid to determine Modes I and II stress intensity factors for cracks. In the case of TiN/Steel medium, KI and KII were determined for variations in crack length, layer thickness, and load location. The results show that KII reaches maximum values when the contact is adjacent to the crack where Mode I stresses are compressive. KII values decrease with decreased crack length and significantly decrease for reduced layer thickness.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.11 no.1
• /
• pp.143-150
• /
• 2003

Experimental research has been carried out to investigate the characteristics of the fatigue crack initiation and propagation behavior of Tailor Welded Blank(TB) sheet used for vehicle body. We used three types of specimens which were machined of the same base metal: one is 1.4mm thick, another is 1.6mm thick, and the third(TB specimen) is laser-welded of two specimens(1.4mm and 1.6mm thick ones). The results of tensile and hardness test indicate that the yield strength of the TB specimen is the highest, and the hardness around welding bead is higher than that of base metal. Fatigue strength and fatigue limit of the TB specimen are much superior to those of the base metal up to $10^6$ cycles. The fatigue crack propagation of the heat-affected zone of the TB specimen is slower than that of the base metal. Welding bead has the fastest crack Propagation in the low stress intensity factor range$(\DeltaK)$ region, but the slowest in the high $\DeltaK$ region. The fatigue propagation characteristic of the TB specimen is relatively stable in comparison with that of the base metal in the high ${\Delta}K$ region around over $28MPa\sqrt{m}$.

• Proceedings of the KSME Conference
• /
• 2003.11a
• /
• pp.1222-1227
• /
• 2003

Pitting wear is a dominant form of polyethylene surface damage in total knee replacements, and may originate from surface cracks that propagate under repeated tribological contact. In this study, stress intensity factors, $K_{I}$ and $K_{II}$, were calculated for a surface crack in a polyethylene - CoCr - bone system under the rolling and/or sliding contact pressures. Crack length and load location were considered in determination of probable crack propagation mechanisms and fracture modes. Positive $K_{I}$ values were obtained for shorter cracks in rolling contact and for all crack lengths when the sliding load was apart from the crack. $K_{II}$, was the greatest when the load was directly adjacent to the crack $(g/a={\pm}1)$. Sliding friction caused a substantial increase of both $K_{I}^{max}$ and $K_{II}^{max}$. The effective Mode I stress intensity factors, $K_{eff}$, were the greatest at $g/a={\pm}1$, showing the significance of high shear stresses generated by loads adjacent to surface cracks. Such behavior of $K_{eff}$ suggests mechanisms for surface pitting by which surface cracks may propagate along their original plane under repeated rolling or sliding contact.

• Journal of the Korean Society of Safety
• /
• v.23 no.4
• /
• pp.25-29
• /
• 2008

Recently, new functionally graded material(FGM) that has a spatial variation in composition and properties is developed because of its good quality. This material yields the demands for resistance to corrosion and high temperature in turbine blade, wear resistance as in gears and high strength machine parts. Especially coating treatment in FGM surface brings forth a mechanical weak at the interface due to discontinuous stress resulting from a steep material change. It often, leads cracks or spallation in a coating area around an interface. The behavior of propagation cracks in FGMs was here investigated. The interface stresses were reduced because of graded material properties. Also graded material parameter with exponential equation was founded to influence the stress intensity factor. And the resistance curve with FGM coating was slightly increased.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2002.04a
• /
• pp.53-58
• /
• 2002

This paper aims to synthesize the research on fatigue mechanisms of high strength aluminum alloys which are widely used in motorcars or airplanes to prevent accidents. To measure the data of crack opening ratio, the same materials and methods are used for evaluating the fatigue crack propagation rate as an effective stress intensity factor. But, many researchers have brought different results. An exact crack opening ratio was, therefore, proposed for getting a more accurate fatigue crack propagation rate.

• Journal of Ocean Engineering and Technology
• /
• v.9 no.1
• /
• pp.83-91
• /
• 1995

Surface defects in structural members are apt to be origins of fatigue cracks growth, which may cause serious failure of whole structures. Most structure has a part where stress concentrates such as welded joints, corner parts, etc. And then, analysis on crack growth and penetration from these defects, therefore, is one of the most important subjects for the reliability of LBB design. The present paper has performed an experimental and analysis on the fatigue crack propagation by variety in crack length of surface cracked plate with stress concentration part. The crack growth behavior can be explained quantitatively by using Newman-Raju equation and the stress partitioning method proposed by ASME B&P Code Sec. XI. The stress concentration factor $K_t$ has affected on the crack growth. The crack growth after penetration depends upon the initial front side crack length.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.7
• /
• pp.1217-1222
• /
• 2002

The dynamic photoelasticity with the aid of Cranz-Shardin type high speed camera system is utilized to record the dynamically propagating behavior of the interface crack. This paper investigates the effects of the hole (existed along the path of the crack propagation) shape on the dynamic interface crack propagation behavior by comparing the experimental isochromatic fringes to the theoretical stress fields.