• Structural Engineering and Mechanics
• /
• v.15 no.3
• /
• pp.367-378
• /
• 2003

The magnitude of the plastic zone around the crack tip of DENT (Double Edge Notched Tension) specimen and the crack growth length under cyclic loading were measured by ESPI (Electronic Speckle Pattern Interferometry) system. The measured magnitude of plastic zone was compared with the proposed by Irwin and calculated by a nonlinear static method of MSC/NASTRAN. The measured crack growth length by ESPI system was also compared with the obtained data by the image analysis system. From the study, it is confirmed that the plastic zone and crack growth length can be measured accurately with the high-tech equipment (ESPI System).

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.12
• /
• pp.2091-2099
• /
• 2001

Fatigue crack growth behavior of inclined cracked Al 6061-T6 thick aluminum plate(6mm) repaired with the bonded composite patch was studied. A 0°inclined crack bonded reinforced composite patch and 15°, 30°, 45°, 60°inclined crack plates were tested. The effect of patch and inclined angle were studied and compared to each other. Also we investigated to the crack propagation direction and debonding behavior during the fatigue crack growth test. In this paper. a study was con(ducted to get an fatigue life, fatigue crack growth ratio and crack growth direction. Finally, the effectiveness of composite patch on inclined cracked plate was investigated. The results demonstrated thats there was a definite variation in fatigue life and fatigue crack growth behavior depending on the inclined crack angle.

• Journal of the Korean Society for Precision Engineering
• /
• v.21 no.4
• /
• pp.161-169
• /
• 2004

In this study, we investigated fatigue crack growth behavior of laser welded sheet metal due to a single overload. Fatigue specimens were made using butt joint of cold rolled sheet metal that was welded by $CO_2$ laser. The fatigue crack propagation tests were performed in such a way that fatigue loading was parallel to the weld line while crack propagation was perpendicular to the weld line. Single overload was applied when fatigue crack tip was arrived near the weld line. The distances between the crack tip and the weld line at which a single overload was applied were 6, 4 and 2mm. The effect of specimen thickness and overload ratio on the fatigue behavior was determined. The plastic zone size of crack tip due to the single overload was determined from the finite element analysis. For investigating fatigue crack growth behavior, we used different thickness specimen 0.9mm and 2.0mm, and variable overload ratio applied fatigue crack propagation test. Also we used finite element analysis for investigating the plastic zone size of crack tip when single overload applied

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.643-647
• /
• 2003

Power plant Piping operating at elevated temperature often fails prematurely by the growth of microcracks under creep conditions. Therefore, the life assessment of high temperature components that contain cracks is an important technological problem. The mechanisms of crack growth in simple metals and alloys have been investigated using both mechanical and microstructural approaches. In this study, life prediction accounting for creep, crack growth and thermal stress is analyzed.

• Journal of the Korean Society for Precision Engineering
• /
• v.17 no.5
• /
• pp.168-172
• /
• 2000

The stiffened panel is representative of a large portion of aircraft construction and therefore has much practical importance. In this paper, the influence of various shape parameters on the stress intensity factors and the fatigue crack growth in the panels with bonded composite stiffeners are studied experimentally. Results are presented as crack growth rates for various values of crack lengths, stiffness ratios, and stiffening Materials.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.1349-1353
• /
• 2003

Previous researches for fiber reinforced composite material(FRCM) have been evaluated the fatigue delamination behavior using the traditional fracture mechanics parameters. Therefore. previous researches for FRCM have not generally been firmed yet. Because delamination growth behavior in FRCM should be consider relationship between delamination area, A$\sub$D/ and crack length, a instead of traditional fracture mechanics parameters. Especially, in case of delamination behavior for FRCM without crack should be considering equivalent crack, i.e., pseudo crack, a$\sub$p/, using the fracture behavior of FRCM with crack. The major purpose of this study was to evaluate the delamination for FRCM without crack. The details of the studies are as follow : 1) Relationship between crack growth rate, da/dN and stress intensity factor, ΔK in FRCM containing a saw-cut and circular hole with crack. 2) Propose of PSEUDO CRACK MODEL for the delamination in FRCM without crack. 3) Analysis of crack propagation energy, E$\sub$crack/ using a total energy, E$\sub$total/ and delamination growth energy, E$\sub$del/.

• Journal of Advanced Marine Engineering and Technology
• /
• v.22 no.4
• /
• pp.490-497
• /
• 1998

An elast-biscoplastic finite element analysis is performed to investigate detailed growth behavior of creep cracks and the numerical results are compared with experimental results. The results of mesh translation method are compared with those of node release method. Load line displancement curve obtained from the crack growth analysis by mesh translation shows the improved results than that obtained from the crack growth by node release method when the secondary creep rate is only used as creep material property. The results of accounting for primary creep rate and instantaneous plasticity shows a good agreement with the experimental result.

• Journal of the Korean Society for Precision Engineering
• /
• v.17 no.10
• /
• pp.49-55
• /
• 2000

This study describes the fatigue characteristics for Al2024 alloy, which is aircraft structure material. For this work, the plane-strain fracture toughness test, the plane-stress fracture toughness test and the crack growth rates test were conducted under the standard testing method. Test equipment is a computer-controlled closed-loop fatigue testing machine. The data of each test result is very important to aircraft structure reliability estimation, life prediction, design analysis, endurance analysis and damage tolerance analysis. In addition, the fatigue crack growth threshold($\DeltaKth$) value decreased as the stress ratio increased. Also, $\DeltaKth$ decreased as the thickness increased in LT, TL directions.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.11 no.4
• /
• pp.82-89
• /
• 2012

In order to clarify the effect of overload on crack growth behaviors, fatigue tests for overload were carried out for round plain specimens of SM45C steel. In the experiment, typical semi-elliptical crack shape was found and further crack growth behaviors were tested. Using three types of single overload fatigue tests, Crack growth retardation phenomenon were examined. The growth rate of surface crack(da/dN) during retardation period was analyzed in terms of ${\Delta}K$ and ${\Delta}K_{eff}$. On the growth rate of surface crack analyzed by ${\Delta}K$, the dependence of overload stress levels appears. However, on the growth rate by ${\Delta}K_{eff}$ obtained by Willenborg analysis, there is a liner relationship between da/dN and ${\Delta}K_{eff}$ with narrow scatter band.

• Proceedings of the KSME Conference
• /
• 2000.04a
• /
• pp.182-187
• /
• 2000

The application of fracture mechanics have traditionally concentrated on cracks leaded by tensile stresses, and growing under an opening or mode I mechanism. However, many cases of failures occur from growth of cracks subjected to mixed mode loading. Several criteria have been proposed regarding the crack growth direction under mixed mode loadings. This paper is aimed at prediction of fatigue crack growth behaviour under mixed mode(I+II) in two dimensional branched type precrack. In this paper, the maximum tangential stress(MTS) criterion was used to predict crack growth direction. Not only experiment but also finite element analysis(FEA) was carried out. The theoretical predictions were compared with experimental results in this paper