• Journal of Korean Society of Steel Construction
• /
• v.9 no.4 s.33
• /
• pp.515-521
• /
• 1997

The effects of heat treatment and fiber orientation on tensile strength and fatigue behavior were studied in a continuously reinforced. magnesium-based composite Following an earlier TEM investigation, specimens were thermally aged to modified the interfacial zone between the alumina fibers and the magnesium alloy matrix. From the tensile experimental results, the ultimate tensile strength of the aged specimens were lower than that of the as-fabricated due to weak fiber-matrix interfacial strength with chemical reaction during the thermal processing. The fatigue crack growth experiments were conducted with specimens having the fiber orientation normal to the crack growth direction (longitudinal) and also specimens with the fibers oriented parallel to the crack growth direction(transverse). A comparison of the fatigue crack growth behavior indicates that aged longitudinal specimens are more resistant to fatigue crack growth the as-fabricated longitudinal specimens. Conversely, as-fabricated transverse specimens are more resistant to fatigue crack growth than aged transverse specimens.

• Geomechanics and Engineering
• /
• v.14 no.2
• /
• pp.195-202
• /
• 2018

Many laboratory experiments on crack propagation under uniaxial loading and biaxial loading have been conducted in the past using transparent materials such as resin, polymethyl methacrylate (PMMA), etc. However, propagation behaviors of three-dimensional (3D) cracks in rock or rock-like materials under tri-axial loading are often considerably different. In this study, a series of true tri-axial loading tests on the rock-like material with two semi-ellipse pre-existing cracks were performed in laboratory to investigate the acoustic emission (AE) characteristics and propagation characteristics of 3D crack groups influenced by intermediate principal stress. Compared with previous experiments under uniaxial loading and biaxial loading, the tests under true tri-axial loading showed that shear cracks, anti-wing cracks and secondary cracks were the main failure mechanisms, and the initiation and propagation of tensile cracks were limited. Shear cracks propagated in the direction parallel to pre-existing crack plane. With the increase of intermediate principal stress, the critical stress of crack initiation increased gradually, and secondary shear cracks may no longer coalesce in the rock bridge. Crack aperture decreased with the increase of intermediate principal stress, and the failure is dominated by shear fracturing. There are two stages of fracture development: stable propagation stage and unstable failure stage. The AE events occurred in a zone parallel to pre-existing crack plane, and the AE zone increased gradually with the increase of intermediate principal stress, eventually forming obvious shear rupture planes. This shows that shear cracks initiated and propagated in the pre-existing crack direction, forming a shear rupture plane inside the specimens. The paths of fracturing inside the specimens were observed using the Computerized Tomography (CT) scanning and reconstruction.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.4
• /
• pp.118-124
• /
• 2017

In this study, a numerical simulation was performed using commercial code Fluent(v.17.1). The underground Combined Cycle Power Plant (CCPP) was simplified to analyze the methane gas leakage with the crack size and position. In addition, extensive numerical simulations were carried out for different crack sizes from 10 mm to 20 mm. The crack position is the gas leakage, which is assumed to be near the pipe elbow and the gas turbine. A total of 4 cases were compared and analyzed. To analyze the gas leakage, the concept of the Lower Flammable Limit (LFL) was applied. The leakage distance was defined in the longitudinal direction, and the transverse direction was estimated and quantitatively analyzed. As a result, the leakage distance in the longitudinal direction varies by 52.3 % depending on the crack size at the same crack position. Moreover, the maximum difference was 34.8 % according to the crack position when the crack sizes are identical. As jet flow impacts on the obstacle and changes its direction, the recirculation flows are formed. These results are expected to provide useful data to optimize the location and number of gas detections in confined spaces, such as underground CCPP.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.2
• /
• pp.143-156
• /
• 2015

The stress and displacement fields at the crack tip were studied during the unsteady propagation of a mode III crack in a direction that was different from the property graduation direction in functionally graded materials (FGMs). The property graduation in FGMs was assumed based on the linearly varying shear modulus under a constant density and the exponentially varying shear modulus and density. To obtain the solution of the harmonic function, the general partial differential equation of the dynamic equilibrium equation was transformed into a Laplace equation. Based on the Laplace equation, the stress and displacement fields, which depended on the time rates of change in the crack tip speed and stress intensity factor, were obtained through an asymptotic analysis. Using the stress and displacement fields, the effects of the angled property variation on the stresses, displacements, and stress intensity factors are discussed.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.137-142
• /
• 2003

In this study, the propagation behavior of fatigue crack effected hole defects was investigated under mixed-mode I+II loading. To create mixed-mode stress field at crack tip, the compact tension shear (CTS) specimen and loading device were used in this tests. The propagation experiments of fatigue crack were performed by changing of the loading application angle(${\phi}$) and the distance(L) estimated from pre-crack tip to hole center located side by side by side with a pre-crack. As L changes, the variation for propagation aspect of fatigue crack, fatigue life and crack propagation rate were examined under mixed-mode loading. Under mixed-mode loading, the propagation rate of fatigue crack increased while the propagation direction changed dramatically because of the interference of hole defects.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.21 no.2
• /
• pp.276-282
• /
• 2012

This study looked for Mode status of each for fatigue crack growth behavior about the repeat load of mode I and the static load of mode II. The experiment was performed in the state of the repetition frequency of the sine wave 10Hz, the stress ratio 0.1, maximum load 300kg.f, a static load 0, 100, 200, 300kg.f, As the experimental results, in mode of static load, while the load value increases, the crack growth rate is slower as the energy of a crack mixing grows. Mode I and the power mode II get an influence each other in the direction of crack propagation path, but as they eventually get closer to the breaking point of the crack growth, it is dominated by the mode I.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1993.10a
• /
• pp.644-649
• /
• 1993

Practical structures are subject not only to tension but also to shear and torsional loading. In this study, the mode 1 and 2 stress intensity factors of specimens were calculated by using elastic finite element mothod. The stress fields at the crack tip subjected to mixed-mode loading were also studied by usingf eleatic finite element method and were compared with theoretical results. The three-point-bending, four-point-bending, and mixed-mode-loading experiment were carried out. And, crack propagation rate da/dN and crack growth direction were examined. Also, the elastic finite element method was applied to calculate the stress intensity factors of branch crack tip and we relate the stress intenity factor range of branch crack tip(the result of FEM) to crack propagation rate(the experimental result). The .DELTA. -da/dN relation corelated with that of mode 1.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.8
• /
• pp.1875-1882
• /
• 1993

Variable thickness plates are commonly used as structural members in the majority of industrial sectors. Previous fracture mechanics researches on variable thickness plates were limited to mode I loading cases. In practice, however, cracks are usually located inclined to the loading direction. In this respect, combined mode(mode I/II) stress intensity factors $K_{I}$ and $K_{II}$ at the crack tip for a variable thickness plate were obtained by 3-dimensional finite element analysis. Variable thickness plates containing a slant edge crack were chosen. The parameters used in this study were dimensionless crack $length{\lambda}$, slant $angle{\alpha}$, thickness $ratio{\beta}$ and width ratio{\omega}$. Stress intensity factors were calculated by crack opening displacement(COD) and crack sliding displacement(CSD)method proposed by Ingraffea and Manu.

• Journal of the Korean Society of Safety
• /
• v.14 no.2
• /
• pp.3-10
• /
• 1999

Fatigue crack growth rates in commercial plate of high strength Al 7075-T651 were investigated for the T-L direction in air, water and sea water. In this paper the effect of cyclic load wave-form(trapezoid and triangle) on fatigue crack growth rates in air, water and sea water environments were investigated using standard LEFM testing procedures. It was founded that the fatigue crack growth behaviors were not affected by cyclic load wave-forms. In region II (stable crack growth region), the fatigue crack growth behaviors were insensitive to cyclic load wave-forms and were sensitive to environment i.e. fatigue crack growth behaviors were higher in sea water than in air for all cyclic load wave-form. The result of fractographical morphology in air, water and sea water by SEM showed obvious dimple rupture and typical striation in air, but transgranular fracture surface in water and sea water. The values m are not affected by corrosion environments but C are different values.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.113-118
• /
• 2003

Stress and displacement fields for a propagating crack in a functionally gradient material (FGM) which has exponentially varying elastic and physical properties along the direction of the crack propagation, are derived. The equations of motion in nonhomogeneous material are developed using displacement potentials. The solutions to the displacement fields and the stress fields for a crack propagating at constant speed along the gradient are obtained through an asymptotic analysis. The influences of nonhomogeneity on the higher order terms of the stress fields are explicitly brought out. Using these stress components, isochromatic fringes around the stationary crack are generated at crack for different nonhomogeneity and the effects of nohonhomgeneity on these fringes are discussed.