• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.1
• /
• pp.124-132
• /
• 1997

This paper describes an experimental and numerical study on growing ductile crack-tip behaviors. The hybrid experimental and numerical method by means of a computer image processign technique, was applied to the analysis of both base metal and weld metal CT specimens. In the weld metal specimen, the initial crack-tip was placed in front of fusion line, and the crack orientation was perpendicular to it. Finite element analysis of crack growth behaviors in both base and weld matal specimens made of A533B Class 1 steel were also performed to examine the effects of weldment on near crack-tip fields. a series of experimental studies on crack-tip behaviors have clearly shown the qualitative effects of material properties, especially a hardening exponent. The experimental and numerical results have also shown that weldment does not affect displacement and strain fields near a crack-tip while a stress field is influenced by the difference between yield stresses of both base and weld metals.

• Journal of Ocean Engineering and Technology
• /
• v.9 no.2
• /
• pp.89-97
• /
• 1995

The investigate the effect of fiber orientation on the interlaminar fracture toughness of carbon fiber reinforced plastics three prepregs which are domestic products are used in this paper. Those are used for the unidirectional composites, but only one is used for the cross-ply laminate composites which is molded $[0/90]_{6s},\;[0/45]_{6s},\;and\;[0/45/90]_{4s}$. The specimens used for the mode I and mode II Tests are DCB and ENF samples are examined by scanning electron microscope(SEM). The value of $G_{IC}$ is almost same when modified three calculating methods are applied. The highest value of $G_{IC}$at crack initiation is obtained at the $[0/90]_{6s}$ interlaminar and the lowest one is at the $[0/45/90]_{4s}$ interlaminar. The highest value of $G_{IIC}$ at crack initiation, however, is obtained at the $[0/90]_{6s}$ interlaminar and the lowest one is at the $[0/45]_{6s}$. The photographs of SEM show a difference behaviour between mode I and mode II fracture surface.

• Computers and Concrete
• /
• v.16 no.5
• /
• pp.759-774
• /
• 2015

This study simulates the flexural behavior of ultra-high-performance fiber-reinforced concrete (UHPFRC) beams reinforced with steel and glass fiber-reinforced polymer (GFRP) rebars. For this, micromechanics-based modeling was first carried out on the basis of single fiber pullout models considering inclination angle. Two different tension-softening curves (TSCs) with the assumptions of 2-dimensional (2-D) and 3-dimensional (3-D) random fiber orientations were obtained from the micromechanics-based modeling, and linear elastic compressive and tensile models before the occurrence of cracks were obtained from the mechanical tests and rule of mixture. Finite element analysis incorporating smeared crack model was used due to the multiple cracking behaviors of structural UHPFRC beams, and the characteristic length of two times the element width (or two times the average crack spacing at the peak load) was suggested as a result of parametric study. Analytical results showed that the assumption of 2-D random fiber orientation is appropriate to a non-reinforced UHPFRC beam, whereas the assumption of 3-D random fiber orientation is suitable for UHPFRC beams reinforced with steel and GFRP rebars due to disorder of fiber alignment from the internal reinforcements. The micromechanics-based finite element analysis also well predicted the serviceability deflections of UHPFRC beams with GFRP rebars and hybrid reinforcements.

• Geotechnical Engineering
• /
• v.13 no.1
• /
• pp.159-168
• /
• 1997

In order to investigate the effect of parameters such as orientation and surface roughness of a reinforcing material as well as the water content of the clay matrix on the stress-strain and failure behavior of reinforced clay, uniaxial compression tests were performed on clay samples reinforced with a steel inclusion Test results showed that the increase or decrease in strength of reinforced clay samples was found to depend on the orientation of a steel inclusion as well as water content of clay samples. The possible weakening mechanism induced by reinforcement in clay samples was related to the development of cracks along the tips of interface between steel inclusion and clay matrix. A theoretical interpretation of failure behavior of reinforced clay was made by using fracture mechanics theory, and the experimental results were compared with the theoretical predictions. The predicted crack propagation direction obtained from fracture criteria for a material containing a closed crack with friction agreed reasonably well with the measured values obtained from tests.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.10
• /
• pp.1229-1235
• /
• 2011

Fatigue tests were conducted on the aluminum alloy, A7075-T6 to determine the most reliable fretting fatigue damage parameter. Specimens with grooves were used, so that either fretting fatigue crack at the pad/specimen interface or plain fatigue crack at the groove could be nucleated, depending on the pad pressure. Both the crack nucleation location and initial crack orientation were examined using optical microscopy, and the results were used to assess the reliability of the various fretting fatigue damage parameters that have been most commonly used in the literature. Finite element analysis was employed to obtain the stress and strain data of the specimen, which were needed to estimate the parameter values and the orientation of the critical plane. It was revealed that both the Fatemi.Socie and McDiarmid parameters, which assume shear-mode fatigue cracking, are the most reliable.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.531-532
• /
• 2009

This paper presents crack spacing which quantitatively considers the fiber distribution and prediction of uniaxial tensile behavior of ECC on the basis of crack spacing and fiber distribution. The predictions exhibit similar tensile stess-strain curves to the test results within 10% error.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.26 no.2
• /
• pp.204-212
• /
• 1990

The SMC composite, now being considered in certain structural applications, is anticipated to experience repeated loading during service. Thus, understanding of the fatigue behavior is essential in proper use of the composite material. In this paper, using the SMC composite composed of E-glass chopped strand and unsaturated polyester resin three point bending fatigue tests are carried out to investigate the fatigue crack propagating behavior under various cyclic stresses and fatigue damage of various microcrack forms. The following results are obtained from this study; 1) Most of the total fatigue life of the SMC composite is consumed at the initial extension or the growth of the macroscopic crack. 2) A Paris' type power-law relationship between the crack propagation rate and stress intensity factor range is obtained, and the value of material constant m is much higher (m=9~11)than that of other metals. 3) In case of high cyclic stress the fatigue damage show high microcrack density and short crack length, but in case of low cyclic stress does it vice versa. 4) Fatigue damage is characterized by microcrack density, crack length and distribution of crack orientation.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.11
• /
• pp.2219-2227
• /
• 2002

In a nuclear power plant, reactor pressure vessel (RPV) is the primary pressure boundary component that must be protected against failure. The neutron irradiation on RPV in the beltline region, however, tends to cause localized damage accumulation, leading to crack initiation and propagation which raises RPV integrity issues. The objective of this paper is to estimate the integrity of RPV under hot leg leaking accident by applying the finite element analysis. In this paper, a parametric study was performed for various crack configurations based on 3-dimensional finite element models. The crack configuration, the crack orientation, the crack aspect ratio and the clad thickness were considered in the parametric study. The effect of these parameters on the maximum allowable nil-ductility transition reference temperature ($(RT_{NDT})$) was investigated on the basis of finite element analyses.

• Journal of the Korean Society of Safety
• /
• v.28 no.6
• /
• pp.57-63
• /
• 2013

This paper discusses 2D models of beams for simulating the fracture of brittle materials. A simulation of an experiment on a concrete beam subjected to bending, in which two overlapping cracks occur, is used to study the effect of individual beam characteristics and different arrangements of the beams in the overall network mesh. It was found that any regular orientation of the beams influences the resulting crack patterns. Methods to implement a wide range of poisson's ratios are also developed, the use of the mesh to study arbitrary micro-structures is outlined. The crack pattern that are obtained with mesh are in good agreement with the experimental results. Also, numerical simulations of the tests were performed by means of a model, and non-integer dimensions were measured on the predicted mesh damage patterns.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.2
• /
• pp.283-290
• /
• 2002

In this paper, we consider the dynamic electromechanical behavior of an eccentric Yoffe permeable crack in a piezoelectric ceramic strip sandwiched between two elastic orthotropic materials under the combined anti-plane mechanical shear and in-plane electrical loadings. Fourier transforms are used to reduce the problem to the solution of two pairs of dual integral equations, which are then expressed to a Fredholm integral equation of the second kind. The initial crack propagation orientation for PZT-5H piezoceramics is predicted by maximum energy release rate criterion.