• Tribology and Lubricants
• /
• 제17권5호
• /
• pp.399-405
• /
• 2001

In this paper the ball-on-disk type sliding tests with boundary lubricated steels were carried out to verify the relation between surface profiles and wear as well as scuffing. Three kinds of surface roughness and asperity radius were produced on AISI 1045 steels using the different processes of grinding and polishing. Frictional forces and time to scuffing were measured. Also, the shape and amount of wear particles were analyzed to compare with original profiles. From the tests, it was confirmed that the size of wear particles are very related to original surface profile. The time to failures and wear amounts were sensitive to the surface spacing. The large surface spacing shows much longer sliding life and smaller wear amount than the others. Time to scuffing was increased with increasing surface profile spacing. The sire of wear particles was increased and the amount was decreased with increasing surface profile spacing. Wear volume and wear rate K were decreased with increasing surface profile spacing. And after sliding tests, surface cracks of inner parts of the wear track occurred scuffing were observed and compared the differences about each specimen having the different surface profile spacing.

• 제어로봇시스템학회논문지
• /
• 제13권11호
• /
• pp.1060-1066
• /
• 2007

When a high-energy ultrasound propagates through a solid body that contains a crack or a delamination, the two faces of the defect do not ordinarily vibrate in unison, and dissipative phenomena such as friction, rubbing and clapping between the faces will convert some of the vibrational energy to heat. By combining this heating effect with infrared imaging, one can detect a subsurface defect in material efficiently. In this paper a detection of the welding defect of thin SUS 304 plates using the UIR (ultrasonic infrared imaging) technology is described. A low frequency (20kHz) ultrasonic transducer was used to infuse the welded thin SUS 304 plates with a short pulse of sound for 280ms. The ultrasonic source has a maximum power of 2kW. The surface temperature of the area under inspection is imaged by a thermal infrared camera that is coupled to a fast frame grabber in a computer. The hot spots, which are a small area around the defect tip and heated up highly, are observed. From the sequence of the thermosonic images, the location of defective or inhomogeneous regions in the welded thin SUS 304 plates can be detected easily.

• Geomechanics and Engineering
• /
• 제8권3호
• /
• pp.391-414
• /
• 2015

In this paper, stabilities of a plane slide rock slope under different hydraulic distributions were studied based on the nonlinear Barton-Bandis (B-B) failure criterion. The influence of various parameters on the stability of rock slopes was analyzed. Parametric analysis indicated that studying the factor of safety (FS) of planar slide rock slopes using the B-B failure criterion is both simple and effective and that the effects of the basic friction angle of the joint (${\varphi}_b$), the joint roughness coefficient (JRC), and the joint compressive strength (JCS) on the FS of a planar slide rock slope are significant. Qualitatively, the influence of the JCS on the FS of a slope is small, whereas the influences of the ${\varphi}_b$ and the JRC are significant. The FS of the rock slope decreases as the water in a tension crack becomes deeper. This trend is more significant when the flow outlet is blocked, a situation that is particularly prevalent in regions with permafrost or seasonal frozen soil. Finally, the work is extended to study the reliability of the slope against plane failure according to the uncertainty from physical and mechanics parameters.

• 한국분말재료학회지
• /
• 제5권4호
• /
• pp.319-323
• /
• 1998

Powder forging with a back pressure was investigated for production of automobile and compressor parts made of a rapidly solidified Al-Si alloy powder. Disk-shaped green compacts made of a rapidly solidified Al-Si alloy powder were hot forged, and hubs were formed by loading back pressure on their top. The influences of the back pressure and die temperatures on forgeabiliy and properties of parts made of a rapidly solidified Al-Si alloy powder were examined. This method was also applied to the production of a scroll part. The results of these studies are summarized as follows : 1. A back pressure on the hub top is very effective for consolidation and preventing crack formation in the hub. 2. When a back pressure tess than 98 MPa is applied, the forging pressure increases by the same amount of the applied back pressure. With more than 98 MPa, the forging pressure increases further due to an increased friction at the hub side. 3. Die temperatures higher than approximately 670k are needed in order to consolidate well the hub top without cracks.

• 한국주조공학회지
• /
• 제22권4호
• /
• pp.174-183
• /
• 2002

Twin-roll process is a relatively new continuous casting process which can produce high-quality strip products directly, and solidification rate can reach $10^3$ to $10^4$ K/s, leading to fine and uniform microstructures with enhanced mechanical properties. The strip casting condition for producing fine Al-Sn alloy strip was obtained experimentally, and defects appearing on the strip was examined. Crack formation and surface quality of the strip was found to depend mainly on process parameters such as melt temperature, roller gap and rolling speed. Sn structure of network type was observed in Al-20Sn and Al-40Sn alloy strips, and cell spacing of Al-40Sn alloy was smaller than that of Al-20Sn. Banding strength of the heat treated specimens increased with increasing of soaking time and temperature, and bonding strength of Al-20Sn alloy was more superior than that of Al-40Sn alloy. However wear resistance of Al-40Sn alloy contained large amount of soft Sn which possess good anti-friction characteristics was superior than that of Al-20Sn alloy.

• Tribology and Lubricants
• /
• 제26권6호
• /
• pp.336-340
• /
• 2010

Ultrasound thermography detects defects by radiating 20 ~ 30 kHz ultrasound waves to the samples and capturing the heat generated from the defects with the use of an infrared thermographic camera. This technology is being spotlighted as a next-generation NDE for the automobile and aerospace industries because it can test large areas and can detect defects such as cracks and exfoliations in real time. The heating mechanism of the ultrasound vibration has not been accurately determined, but the thermomechanical coupling effect and the surface or internal friction are estimated to be the main causes. When this heat is captured by an infrared thermographic camera, the defects inside or on the surface of objects can be quickly detected. Although this technology can construct a testing device relatively simply and can detect defects within a short time, there are no reliable data about the factors related to its detection ability. In this study, the ultrasound thermography technique was used to manufacture gasoline and diesel engine piston specimens, and nondestructive reliability tests to verify the applicability and validity of the ultrasound thermography technique.

• Tribology and Lubricants
• /
• 제30권4호
• /
• pp.199-204
• /
• 2014

Various heat-treated and surface coating methods are used to mitigate abrasion in sliding machine parts. The most cost effective of these methods involves hard coatings such as diamond-like carbon (DLC). DLC has various advantages, including a high level of hardness, low coefficient of friction, and low wear rate. In practice, a supporting layer is generally inserted between the DLC layer and the steel substrate to improve the load carrying capacity. In this study, an indentation and sliding contact problem involving a small, hard, spherical particle and a DLC-coated steel surface is modeled and analyzed using a nonlinear finite element code, MARC, to investigate the influence of the supporting layer thickness on the coating characteristics and the related coating failure mechanisms. The results show that the amount of plastic deformation and the maximum principal stress decrease with an increase in the supporting layer thickness. However, the probability of the high tensile stress within the coating layer causing a crack is greatly increased. Therefore, in the case of DLC coating with a supporting layer, fatigue wear can be another important cause of coating layer failure, together with the generally well-known abrasive wear.

• Steel and Composite Structures
• /
• 제28권6호
• /
• pp.767-778
• /
• 2018

The purpose of this study is to investigate how a fully restrained bolted beam splice affects the connection behavior as a column-tree connection in steel special moment frames under cyclic loading when located within the plastic hinge zone. The impacts of this attachment in protected zone are observed by using nonlinear finite element analyses. This type of splice connection is designed as slip-critical connection and thereby, the possible effects of slippage of the bolts due to a possible loss of pretension in the bolts are also investigated. The 3D models with solid elements that have been developed includes three types of connections which are the connection having fully restrained beam splice located in the plastic hinge location, the connection having fully restrained beam splice located out of the plastic hinge and the connection without beam splice. All connection models satisfied the requirement for the special moment frame connections providing sufficient flexural resistance, determined at column face stated in AISC 341-16. In the connection model having fully restrained beam splice located in the plastic hinge, due to the pretension loss in the bolts, the friction force on the contact surfaces is exceeded, resulting in a relative slip. The reduction in the energy dissipation capacity of the connection is observed to be insignificant. The possibility of the crack occurrence around the bolt holes closest to the column face is found to be higher for the splice connection within the protected zone.

• Tribology and Lubricants
• /
• 제15권1호
• /
• pp.39-45
• /
• 1999

The wear behavior of $Al_2$O$_3$-40%TiO$_2$deposited on casted aluminum alloy (ASTM A356) by APS (Air Plasma Spray) against SiC ball has been investigated in this work. Wear tests were carried out at room temperature. The friction coefficient of $Al_2$O$_3$-40%TiO$_2$coating is lower than that of pure $Al_2$O$_3$coating(APS). $Al_2$O$_3$-40%TiO$_2$coating indicated the existence of the optimal coating thickness. It is found that voids and pores of coating surface resulted in the generation of cracks, and the cohesive of splats and the porosity of surface play a role in wear characteristics. It is suggested that the mismatch of thermal expansion of substrate and coating play an important role in wear performance. Tension and compression under thermo-mechanical stress may be occurred by the mismatch between thermal expansion of substrate and coating. The crack propagation above interface is observed in SEM.

• 소성∙가공
• /
• 제15권8호
• /
• pp.550-555
• /
• 2006

In this study, effects of forming angle and friction coefficient on a initiation of the Mannesmann hole defect were analyzed by using a response surface method. The maximum effective plastic strain at center point of specimen is utilized for the prediction of the starting point of crack occurrence, which is suggested by the comparison of integrals of four different ductile fracture models between the histories of the effective plastic strain at center point. It was revealed that the principal stress at the center is the dominant element to the increase of the effective plastic strain. It was also verified by the simulation results from the comparison of experiment and simulation. It is provided that the forming angle of 25 degrees and the spreading angle of 1 degree can be a proper design condition without an occurrence of internal hole defect and an excessive slip.