• Journal of Welding and Joining
• /
• v.11 no.4
• /
• pp.91-102
• /
• 1993

The plasma sprayed $Cr_3C_2$-NiCr coatings are widely used as wear-resistant and corrosion-resistant materials. The mechanical and wear properties of the plasma sprayed $Cr_3C_2$-NiCr coating on steel plate were examined in this study. The pore in the coatings could be classified into two types, the one is the intrinsic pore originated from the spraying powder, the other is the extrinsic pore formed during spraying. During the tensile adhesion test, the fracture occured at the interface of top coating and bond coating. It is though that the compressive residual stress increases with the increase of the top coating thickness. From the wear test, it was found that the wear rate increased with the increase of the sliding velocity regardless of the temperature. It is thought that the fracture toughness reduces with the increase of the sliding velocity at $30^{\circ}C$ and that the adhesion amount increases with the increase of the sliding velocity at $400^{\circ}C$ It is concluded that the wear mechanism at $30^{\circ}C$ is the fracture and pull-out of the carbide particles due to the fatigue on sliding surface, while the wear mechanism at $400^{\circ}C$ is the adhesion of the smeared layer formed during wear process.

• Aerospace Engineering and Technology
• /
• v.8 no.1
• /
• pp.138-143
• /
• 2009

Thermal barrier efficiency and endurance of coatings in liquid rocket engine combustor were evaluated for air plasma spray coating and electro/electroless plating. The result of firing tests has revealed occasional occurrence of local delamination of $ZrO_2$, NiCrAlY coating obtained by the method of air plasma spray in the region of supersonic flow and it necessitated a new coating method as a substitution. It was found that Ni-Cr coating by means of electro/electroless plating can substitute $ZrO_2$, NiCrAlY coatings of air plasma spray in terms of thermal barrier efficiency and endurance.

• Tribology and Lubricants
• /
• v.34 no.6
• /
• pp.217-225
• /
• 2018

In this study, we spray a Ni-Cr composite powder onto AISI 4340 steel using the high velocity oxygen fuel method. We subsequently subject the Ni-Cr coating (as-sprayed) to ultrasonic nanocrystal surface modification (UNSM) process to improve the tribological performance. This study aims at increasing the wear resistance and durability of the Ni-Cr coating by altering the surface integrity and microstructure via the UNSM process. The UNSM process reduces the surface roughness of the as-sprayed coating by about 64%, which is explained by observing the elimination of high peaks and valleys and filling up micro-pores. Furthermore, a change in the microstructure of the coating due to continuous high-frequency strikes to the surface by a tip can lead to an increase in hardness from about 48 to 60 HRC. Furthermore, we investigate the characterization of the friction and wear behavior of Ni-Cr coating by a ball-on-disc tribometer in the dry conditions. We determine that after the UNSM process, there is a significant reduction in the friction coefficient of the as-sprayed coating from approximately 1.1 to 0.75. This is owing to the increased hardness and smoothed surface roughness. In addition, we investigate the surface morphology and wear track of the coatings before and after the UNSM process using a scanning electron microscope, energy dispersive spectrometer, and three-dimensional laser scanning microscope. We observe that the wear track of the Ni-Cr coating after the UNSM process is lower than that of the as-sprayed one. Thus, we confirm that the UNSM process has a significant influence on the improvement of the tribological performance of the Ni-Cr composite coating.

• Journal of dental hygiene science
• /
• v.9 no.4
• /
• pp.405-412
• /
• 2009

The purpose of this study investigated the effect of Au coating on adhesion between porcelain matrix and metal substructure interface. Titanium, Ni-Cr alloy and Co-Cr alloy are well known as proper metal for the dental restorations. The success of a porcelain fused to metal (PFM) restoration depends upon the quality of the porcelain-metal bond. However, adhesion between dental alloys and porcelain is related to diffusion of oxygen during ceramic firing. The excessive oxidized layers make hard adhesion between dental alloy and ceramic. Ni-Cr and Co-Cr specimens were divided into test and a control group and Titanium specimens were divided into three test groups and a control group. Each group had 20 specimens. The adhesion characteristics of porcelain and metal with Au coating layer and without Au coating layer were observed with scanning electron microscopy(SEM). The adhesion was evaluated by a biaxial flexure test and volume fraction of adherent porcelain was determined by SEM/EDS analysis. Result of this study suggest that Au coating layer is effective barrier to diffuse oxide layer completely protect non-precious alloys from oxidation during the porcelain firing. The SEM photomicrographs of cross-section specimens showed a smooth interface between Au coating layer and metals and porcelain which suggested proper chemical bonding, and no gap, porosity were observed. The mode of failure was mainly adhesive for Ti tested specimens, but mixed failures with adhesive and cohesive were observed in Ni-Cr and Co-Cr specimens. The adhesion between non-precious metals and porcelain would not be improved by Au coating agent. However, It is suggested that the continuous study is required further investigation and development.

• Journal of Welding and Joining
• /
• v.15 no.1
• /
• pp.125-134
• /
• 1997

This study was conducted by L9 orthogonal array to obtain optimum spray parameters for This study was conducted by L9 orthogonal array to obtain optimum spray parameters for $Cr_3C_2 - 7wt%$(80wt%Ni-20wt%Cr) coating powder. The factors were hydrogen flow rate, oxygen flow rate, gun-to-work distance, powder feed rate. And evaluation methods for the coating were surface roughness, oxygen concentration, micro-hardness, pore size and distribution, low angle ($30^{\circ}$) erosion rate, and microstructure of coating. The optimum HVOF spray conditions were proved as follows : hydroen flow rate ; 681 SLPM, oxygen flow rate ; 215 SLPM $H^2/O^2 ratio= 3.16), gun-to-work distance ; 22cm, powder feed rate; 25g/min. The hardness (Hv300) was 1147 and the erosion rate ($30^{\circ}$degree) was $3.16\times10^{-4}$g/g. It is believed that the optimized spray conditions can be improved the wear-resistance and anti-erosion characteristics of the coating.

• Korean Journal of Materials Research
• /
• v.8 no.8
• /
• pp.757-765
• /
• 1998

This study was performed to investigate the influence of fuel/oxygen ratio (F/O= 3.2, 3.0, 2.8) on the oxidation behavior of two kinds of (20wt%NiCr claded $\textrm{Cr}_{3}\textrm{C}_{2}$, and 7wt%NiCr mixed $\textrm{Cr}_{3}\textrm{C}_{2}$) composite powder with different manufacturing method. The results show that the oxidation behavior between the 20wt% NiCr claded $\textrm{Cr}_{3}\textrm{C}_{2}$ and 7wt% NiCr mixed $\textrm{Cr}_{3}\textrm{C}_{2}$ coating was widely different. The surface morphology of the coating composed of 7wt% NiCr mixed $\textrm{Cr}_{3}\textrm{C}_{2}$ was changed to porous with F/O ratio by the aggressive evolution of gas phases($\textrm{CO}_2$, CO and $\textrm{CrO}_3$) and the oxide cluster composed of Ni and Cr were grown after oxidation at $1000^{\circ}C$ for 50 hours. But the surface morphology of the coating composed of 20wt% NiCr claded $\textrm{Cr}_{3}\textrm{C}_{2}$ was not changed to porous after oxidation at $1000^{\circ}C$ for 50 hours. Therefore, the reason for high oxidation rate is due to activation of $\textrm{Cr}_{3}\textrm{C}_{2}$ to oxidation by entrapped oxygen gases within coating layer, and to closely relate with the decomposition of $\textrm{Cr}_{3}\textrm{C}_{2}$ to $\textrm{Cr}_{7}\textrm{C}_{3}$ phase. Accordingly, On the evidence of these results, the study about the oxidation behavoir of the HVOF sprayed $\textrm{Cr}_{3}\textrm{C}_{2}$ coating depending on hydrogen flow rate must be done.

• Journal of Powder Materials
• /
• v.27 no.3
• /
• pp.210-218
• /
• 2020

A T-800 (Co-Mo-Cr) coating material is fabricated using Co-Mo-Cr powder feedstock and laser cladding. The microstructure and melted Al erosion properties of the laser-cladded T-800 coating material are investigated. The Al erosion properties of the HVOF-sprayed MoB-CoCr and bulk T-800 material are also examined and compared with the laser-cladded T-800 coating material. Co and lave phases (Co₂MoCr and Co₃Mo₂Si) are detected in both the laser-cladded T-800 coating and the bulk T-800 materials. However, the sizes of the lave phases are measured as 7.9 ㎛ and 60.6 ㎛ for the laser-cladded and bulk T-800 materials, respectively. After the Al erosion tests, the erosion layer thicknesses of the three materials are measured as 91.50 ㎛ (HVOF MoB-CoCr coating), 204.83 ㎛ (laser cladded T-800), and 226.33 ㎛ (bulk T-800). In the HVOF MoB-CoCr coating material, coarse cracks and delamination of the coating layer are observed. On the other hand, no cracks or local delamination of the coating layer are detected in the laser T-800 material even after the Al erosion test. Based on the above results, the authors discuss the appropriate material and process that could replace conventional bulk T-800 materials used as molten Al pots.

• Journal of Mechanical Science and Technology
• /
• v.16 no.7
• /
• pp.911-918
• /
• 2002

The tribological performance of A1$_2$O$_3$/NiCr coating deposited on steel (SH45C) was investigated under lubrication. The parameters of sliding wear consist of normal load and coating thickness. Test result showed that there was no evidence of an improved bonding strength in the coating. However, the wear resistance of the A1$_2$O$_3$/NiCr coaling was significantly greater than that of the Al$_2$O$_3$ coating. It was eviclent that the residual stress for the A1$_2$O$_3$coating was higher than that of the A1$_2$O$_3$/NiCr coating from the Scratch test failure of coating. The bond coating played an important role in decreasing the residual stress. Also, it was found that the residual stress had d notable influence on the wear mechanism.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2000.04a
• /
• pp.164-169
• /
• 2000

The remote measurement system(RMS) as a new experimental method is limited in its application to crack measurements at elevated temperatures because of the oxide layer on the specimen surface. Since TiAlN and Cr coating layers have a high resistance to oxidation and wear, this paper proposed a TiAlN and Cr coating technique for specimens to facilitate the measurement of crack growth behavior using RMS. To investigate the effects of the coating layer, tension and fatigue tests were carried out at room temperature and at 538$^{\circ}C$, using specimens of 1Cr-1Mo-0.25V steel. From the experimental results, it was found that the mechanical properties of the TiAlN and Cr coated specimens were similar to those of the substrate. Accordingly, the TiAlN and Cr coated layer had hardly any influence on the fatigue crack propagation.

• Journal of Ocean Engineering and Technology
• /
• v.16 no.2
• /
• pp.60-66
• /
• 2002

The remote measurement system(RMS) as a new experimental method is limited in its application to crack measurement at elevated temperatures because of the oxide layer on the specimen surface. Since TiAIN and Cr coating layers have a high resistance to oxidation and wear, this paper proposed a TiAIN and Cr coating technique for specimens to facilitate the measurement of crack growth behavior using RMS. To investigate the effects of the coating layer, tension and fatigue tests were carried out at room temperature and at $538^{\circ}C$. The test material was 1Cr-1Mo-0.25V steel which is widely used as a turbine rotor material. From the experimental results, it was found that the mechanical properties of the TiAIN and Cr coated specimens were similar to those of the substrate. Accordingly, the TiAIN and Cr coated layer had hardly any influence on the fatigue crack propagation.