• 대한기계학회논문집A
• /
• 제22권1호
• /
• pp.44-51
• /
• 1998

In order to develop the evaluation methods of degradation for the Ni-Cr-Mo-V steel, which is in use for turbine rotor in nuclear power plant, the degraded materials were prepared by simulated degradation methods. The result of impact test and fatigue crack growth test shows that the FATT(Fracture Appearance Transition Temperature) and fatigue crack growth rate increased with the increase of degradation. And the result of new electrochemical polarization test method was suggested for the evaluating FATT, fatigue crack growth exponent and coefficient C values based on the results of relationship between corrosion current density(Icorr) & FATT, and the m & C and Icorr.

• 한국해양공학회지
• /
• 제7권1호
• /
• pp.147-155
• /
• 1993

The effect of stress waveforms on corrosin fatigue and the role of dissolution mechanism in 3NilCr steel and 20Ni maraging steel have been investigated in aerated 3% NaCl solution and synthetic seawater under sinusoidal, triangular, square, positive sawtooth, negative sawtooth, and trapezoidal stress waveforms with open circuit at frequency of 1Hz and stress ratio of 0.1. The crack growth rates under square waveform were substantially lower than under sinusoidal and triangular waveforms, but the crack growth rates under sinusoidal waveform were slightly higher under triangular waveform. For a given frequency the growth rates under the positive sawtooth waveform are higher than those under the negative sawtooth waveform. The fatigue crack growth rates of most specimens were in good agreement with the values calculated by the model based on the dissoultion mechanism.

• 한국자동차공학회논문집
• /
• 제16권5호
• /
• pp.1-7
• /
• 2008

A study of new materials that are light-weight, high in strength has become vital to the machinery of auto industries. But then, there are a lot of problems with developing such materials that require expensive tools, and a great deal of time and effort. Therefore, the improvement of fatigue strength and fatigue life are mainly focused on by adopting residual stress. And Influence of corrosive condition for corrosion fatigue crack was investigated, after immersing in 3.5%NaCl, $10%HNO_3$+3.5%HF, $6%FeCl_3$. The immersion period was performed for 365days. The compressive residual stress was imposed on the surface according to each shot velocity based on shot peening, which is the method of improving fatigue life and strength. Fatigue life shows more improvement in the shot peened material than in the un peened material in corrosion conditions. The threshold stress intensity factor range was decreased in corrosion environments over ambient. Compressive residual stress of surface on the Shot-peen processed operate resistance force of fatigue crack propagation. The fatigue crack growth rate of the Shot-peened material was lower than that of the un peened material. Also m, fatigue crack growth exponent and number of cycle of the shot peened material was higher than that of the un peened material. That is concluded from effect of da/dN.

• 대한기계학회논문집A
• /
• 제24권3호
• /
• pp.603-612
• /
• 2000

Corrosion characteristics on the 12Cr alloy steel of turbine blade was electro-chemically investigated in 3.5wt% NaCI and 12.7wt% Na2S04 solution, respectively. Electro-chemical polarization test, Huey test and Oxalic acid etching test were previously conducted to estimate corrosion susceptibility of the material. And, using the horizontal corrosion fatigue tester, corrosion fatigue characteristics of 12Cr alloy steel in distilled water, 3.5wt% NaCI solution, and 12.7wt%(1M) Na2S04 solution were also fracture-mechanically estimated and compared their results. Parameter considered was room temperature, 60'C and 90'C. Corrosion fatigue crack length was measured by DC potential difference method.Obtained results are as follows,1) 12Cr alloy steel showed high corrosion rate in 3.5wt% NaCI solution and Na2S04 solution at high tempratue.2) Intergranular corrosion sensitivity of 12 Cr alloy was smaller than austenitic stainless steel.3) Corrosion fatigue crack growth rate in 3.5wt% NaCI and 12.7wt%(IM) Na2S04 solution is entirely higher than in the distilled water, and also increased with the temperature increase.

• 수산해양기술연구
• /
• 제24권2호
• /
• pp.94-100
• /
• 1988

평면 굽힘부식피로 시험기를 사용하여 선박용 알루미늄합금재의 부식피로파양에 관한 연구를 한 결과 다음과 같은 결론을 얻었다. 1. 비저항이 증가함에 따라서 초기 부식피로균열발생까지의 반복회수는 지연되고, 그 부식감수성은 감소하는 양상을 나타낸다. 2. 비저항이 감소할수록 Paris rule의 실험상수 m 값은 작아지면서 응력강도 계수값에 비해 부식에 의한 영향이 더욱 민감해 진다. 3. 알루미늄 5086 합금의 부식피로균열은 입계균열파양의 양상을 보이고 있다. 4. 응력강도계수값이 증가함에 따라 부식감수성은 감소되어지고 응력강도계수값이 40kg.mm super(-3/2) 이상일 때 부식감수성은 거의 균일하게 된다.

• Corrosion Science and Technology
• /
• 제11권4호
• /
• pp.120-128
• /
• 2012

The fatigue crack growth behaviors of SA508 Gr.3 Cl.2 low alloy steel in high temperature water environment were investigated. Overall, weld metal showed similar crack growth rate as that of base metal. At 0.01 Hz, fatigue crack growth rate (FCGR) was higher than that in air while the difference was smaller at 0.1 Hz. Also, FCGR showed ${\Delta}K$ dependency at 0.1 Hz only, indicating that the environmental effect was much greater at slower loading frequency of 0.01 Hz. FCGR of SA508 Gr.3 Cl.2 low alloy steel was compatible to or smaller than the ASME Sec. XI fatigue reference curves in high temperature water environment.

• 대한기계학회논문집A
• /
• 제24권1호
• /
• pp.156-162
• /
• 2000

Sensitized STS 304 stainless steel crack growth rate(CGR) in high temperature water was investigated under trapezoidal wave loading test using fracture mechanics techniques. The CGR, due to stress corrosion cracking(SCC), were systematically measured as a function of the stress intensity factor and stress. holding time under trapezoidal wave loading. In high temperature water, CGR was enhanced by a synergistic effects in combination with an aggressive environment and mechanical damage. The CGR, $(da/dN)_{env}$ was basically described as a summation of the environmentally assisted crack growth rate $(da/dN)_{SCC}$, $(da/dN)_{CF}$ and fatigue crack growth rate in air $(da/dN)air,. The CGR, $(da/dN)_{env}$, increased linearly with increasing stress holding time. The CGR, $(da/dN)_{SCC}$ decreased linearly with increasing stress holding time. Fracture surface mode varied from trans-granular cracking to inter-granular cracking with increasing stress holding time.

• 한국항공우주학회지
• /
• 제35권1호
• /
• pp.46-51
• /
• 2007

연구는 Al 2024-T3511 재료를 사용하여 피로균열성장 시험을 통한 비부식과 부식에서의 일정진폭 피로균열 전파 테이터(a-N)를 구하여 비부식과 부식에서의 균열진전의 차이를 규명하였다. 또한 비부식과 부식에서의 균열진전 속도 선도(da/dN-${\Delta}K$)를 구하여 Paris의 식을 이용하여 비부식과 부식의 차이를 규명하였다. 그리고 ${\beta}c$(corrosion factor)의 새로운 개념을 도입하여 피로수명을 예측해 본 결과 실험치를 잘 모사할 수 있었다.

• 한국자동차공학회논문집
• /
• 제8권5호
• /
• pp.181-187
• /
• 2000

Fatigue tests under acid fog environment were carried out to investigate the effect of acid fog on the corrosion fatigue strength of SM55C in comparison with distilled water. Main results obtained are as follows. The fatigue strength of SM55C under acid fog environment are remarkably decreased as compared with that of distilled water specimen. The corrosive effect of acid fog on fatigue strength are more serious under low stress amplitude level than under high stress amplitude level, and this leads to continuous reduction of fatigue strength. Under acid fog environment in early stage of crack growth. because the corrosive components dissolve the crack face offensively. the unstable fracture surface appears. But, the stable corrosion precipitation and products layer are formed on the fracture surface in accordance with the time pass.

• 문화기술의 융합
• /
• 제10권1호
• /
• pp.363-368
• /
• 2024

선박, 해양구조물 또는 해상풍력 발전설비 하부구조와 같이 해양환경에서 사용되는 강구조물은 부식이 쉽게 발생한다. 본 연구에서는 실험을 통하여 희생전극으로 많이 사용되는 아연전극의 방식전위와 동등한 -1050mV vs. SCE에서 환경하중에 기인하는 부식피로균열 진전특성에 대하여 고찰하였다. 이를 위하여 본 연구에서는 -1050mV vs. SCE의 음극방식이 해수환경중의 피로균열 진전에 미치는 영향에 대해 합성해수중에서 파랑주기를 고려하여 실험적 고찰을 실시하였다. 음극방식에 의한 방식법은 부식을 차단하지만 과도한 방식은 화학반응에 의하여 수소를 발생시키며, 또한 석회질퇴적물을 발생시킨다. 피로균열진전율은 실험초기에는 해수부식환경하에서의 진전율보다 빠른구간이 나타났다. 그리고 균열길이가 증가하여 응력확대계수 K가 커질수록 균열의 진전율은 해수중의 피로균열진전율보다 느려지는 현상이 나타났다. 그러나 대기중의 균열진전속도보다는 항상 빠른 진전속도를 나타내었다.