• Journal of the Korean Society for Railway
• /
• v.3 no.2
• /
• pp.77-83
• /
• 2000

This study proposes the integrity evaluation of the bogie frame using ultrasonic fractography analysis. Analysis objectives in this study are to investigate fracture planes of damaged zone by the A-scan method. The surface condition of fracture planes shows degree of degradation by the stress concentration. The detection of the natural defects in the bogie frame is performed using the characteristics of echodynamic pattern in ultrasonic signal. Results of ultrasonic testing agree fairly well with those of actual fracture plane. In quantitative fractography analysis, microstructures of actual fracture plane turned out to be intergranular and transgranular fracture. Proposed ultrasonic fractography analysis in this study can be used for the integrity evaluation of the bogie frame.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.10
• /
• pp.1626-1635
• /
• 1997

It is important to ensure the reliability of the first localized reactor vessel steel. To satisfy with this purpose, a study on the impact/hardness, low cycle fatigue(LCF), crack growth rate(da/dN) and fracture toughness( ) of base material(BM) and weld metal(WM) were performed under room temperature air and corrosion conditions. A summary of the results is as folows : (1) Charpy impact absorbed energy of BM was the highest value, heat affected zoon(HAZ) and the lowest, WM. The hardness of BM was similar to HAZ. (2) Coefficients of Manson equation using the monotonic tensile test data were obtained for the present material. (3) The effects of stress ratio and ambient (120.deg. C and NaCl) condition on da/dN were investigated, da/dN with NaCl condition expressed the highest value. (4) The results of Charpy V-notch impact test had good correlation with $K_{IC}$ characteristics and the lowest curve of $K_{IC}$ for BM was derived, more researches about WM and HAZ are required hereafter.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.11 no.5
• /
• pp.140-146
• /
• 2003

Metal matrix composites had generated a lot of interest in recent time because of their high specific strength and stiffness in specific properties. It was also highlighted as the material of frontier industry because strength, heat-resistance, corrosion-resistance and wear-resistance were superiored. In this study, the strength properties of $Al_{18}B_{4}O_{33}$/AC4CH composites were represented mixing the binder of $SiO_2$. It was also fabricated by squeeze casting. $Al_{18}B_{4}O_{33}$/AC4CH was fabricated at the melt temperature of $760^{\circ}C$, the perform temperature of $700^{\circ}C$ and mold temperature of $200^{\circ}C$ under the pressure of 83.4MPa. Consequently, fatigue life was observed roughly in the order of AC4CH> nobiner> $SiO_2$, independently on crack propagation direction and stress ratio.

• Journal of the Korean Society of Safety
• /
• v.33 no.6
• /
• pp.1-7
• /
• 2018

The Continuous Ship Unloader (CSU) is an equipment that unloads freight from the ship docked in the port to the land. And the design target life time is designed to be 30 to 50 years, and it is classified as a semi-permanent large facility. However, cracks may occur due to structural defects, abnormal loads, and corrosion, and fatigue failure may occur before the design life is reached. In this study, we predicted the remaining life time of the main component of the CSU considering crack. And also proposed inspection cycle for maintenance of CSU based on the results of the remaining life time prediction. For this purpose, the structure, operational stresses of the CSU were analyzed and main members were selected. And tensile tests and fatigue crack propagation tests were performed with SM490YA and SM570TMC, which are used as main materials for CSU.

• Proceedings of the KSME Conference
• /
• 2003.11a
• /
• pp.1388-1393
• /
• 2003

In this study, analytic stress-displacement solutions are obtained by using a shear lag modeling constructed for the spliced joint area with a splicing gap filled with adhesive material of elastic modulus $E_{a}$ in the fiber metal laminate (FML) which is known to have excellent fatigue, corrosion and fire-flame resistant characteristics while with relatively low densities compared to the conventional aluminum alloys for lightweight structures.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.14 no.2
• /
• pp.75-82
• /
• 2005

Recently the needs of high reliable substances of high strength and high ductility are gradually increased with the development of aerospace industry. The characteristics of maraging steel has high ductililty, formability, corrosion resistant and high temperature strength and is easy to fabricate, weld and treat with heat, and maintain an invariable size even after heat treatment. e steels are furnished in the solution annealed condition and they achieve full properties through martensitic precipitation aging a relatively simple, low temperature heat treatment. As is true of the heat treating procedures, aging is a time/temperature dependent reaction. Therefore, the objective of this stud)'was consideration of fatigue characteristics according as Nb(niobium) content and time/temperature of heat treatment change. Also the stress analysis, fatigue lift, and stress intensity factor were compared with experiment results and FEA(finite element analysis) result. The maximum ftresses of)( Y, and Z axis direction showed about $2.12\times$10$^{2}$MPa, $4.40\times$10$^{2}$MPa and $1.32\times$10$^{2}$MPa respectively. The fatigue lives showed about $7\%$ lower FEA result than experiment result showing almost invariable error every analyzed cycle. Stress intensity factor of the FEA result was lower about $3.5~ 10\%$ than that of the experiment result showing that the longer fatigue crack ten添 the hi인or error. It considered that the cause for the difference was the modeled crack tip having always the same shape and condition regardless of the crack growth.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.6
• /
• pp.1351-1360
• /
• 1993

The fatigue behavior of GFRP composites is affected by environmental parameters. Therefore, we have to study on effect of sea water on fatigue behavior of GFRP composites as to maintain the safety and confidence in design of ocean structure of GFRP. In this paper, we investigated the fatigue properties of chopped strand glass mat/polyester composite in synthetic sea water. (pH 8.2) In case of the glass fiber (CSM type) reinforced polyester composite materials, the fatigue crack in the both dry and wet specimens tested in air or synthetic sea water occurred at the initial of cycle. Thereafter, it was divided with two regions that one decreased with the crack extension and the other increased with the crack extension. The transition point occurred during the crack propagation shifted to high ${\Delta}K$ value as load increase but its point is not changed regardless of immersion or test environment under a constant load. The synthetic sea water degrades the bond strength between fiber and matrix, thereby the tendency of rapid deceleration and acceleration of the crack growth was appeared.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.23 no.2
• /
• pp.156-164
• /
• 2003

STS316L had been used as the structural material for energy environmental facilities, because austenite stainless steels like 316L have superior mechanical properties of which toughness, ductility, corrosion resistant and etc. However, those welded structures are receiving severe damage due to increasing of the aged degradation. Most studies until now have been carried out against fatigue behaviors of weldments, and were not well studied on nondestructive evaluation methods. In this study, the fatigue crack propagation behavior of STS316L weldment usually used for vessels of the nuclear power plant was investigated. Also, the degradation characteristics of 316L stainless steel weldments were evaluated by the ultrasonic parameter such as ultrasonic velocity, attenuation factor and time-frequency analysis. The results of this study can be used as a basic data for the prediction of the fatigue crack life of weldments structures without disjointing or stopping service of structures in service.

• Journal of the Korean Ceramic Society
• /
• v.41 no.1
• /
• pp.69-75
• /
• 2004

The degree of the indentation damage and strength degradation for 3Y-TZP ceramics and (Y,Nb)-TZP/$Al_2O_3$ dental implant composites was investigated under the Hertzian cyclic fatigue. Fatigue tests were conducted at contact loads of 500 to 3000 N and up to $10^6$ cycles in exact in vitro environments. At 500 N, no strength degradation and crack generation was observed up to $5{\times}10^5$ contact cycles. Fatigue properties of 3Y-TZP ceramics was superior to (Y,Nb)-TZP/ㅍ composites due to stress relief caused by the phase transformation from tettagonal to monoclinic phase. As contact load increased, the drastic reduction in strength was found when the damage transition from ring to radial crack occurred. The extent of strength degradation was more pronounced in vitro environments probably due to chemical corrosion of artificial saliva through cracks introduced during large numbers of contacts.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.333-336
• /
• 2008

CFRP tendons have been attempted in concrete structures as a substitute for steel tendons considering their many advantages such as the corrosion-resistance, light weight etc. However, the elastic behavior up to failure is likely to result in ductility problems. To overcome such problems, prestress concrete beams with partially bonded tendons have been developed and suggested. In this new system, the un-bonded part near the mid-span contributes to the improvement of ductility. And the bonded parts at both ends play a role as a safe anchorage. According to the previous research on the static behavior, the suggested method has demonstrated enough ductility and strength. However it is essential to verify the long-term safety for repetitive fatigue loads under service states. For this purpose, flexural fatigue loading tests were carried out in this research. This paper includes an experimental investigation on the static load-carrying capacities of the beams with or without fatigue tests. The results showed that the beams prestressed with partially bonded CFRP tendons possessed good fatigue capacity under the constant cyclic loads.