• Corrosion Science and Technology
• /
• v.2 no.1
• /
• pp.41-46
• /
• 2003

Flow-Accelerated Corrosion behavior concerning both activation and mass transfer process of SA106 Gr.C steel was studied using rotating cylinder electrode in room temperature alkaline solution by DC and AC electrochemical techniques. Passive film was tanned from pH 9.8 by step oxidation of ferrous product into hydroxyl compound. Corrosion potential shifted slightly upward with rotating velocity through the diffusion of cathodic species. Corrosion current density increased with rotating velocity in pH 6.98, while it soon saturated from 1000 rpm at above pH 9.8. On the other hand the limiting current increased with rotating speed regardless of pH values. It seems that activation process, which represents formation of passive film on the bare metal surface, controls the entire corrosion kinetics

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.151.1-151.1
• /
• 2017

This work studied the corrosion behavior of AZ31 Mg alloy galvanically coupled with Cu during immersion in 0.1 and 0.5 M NaCl solutions by in-situ observation and galvanic corrosion current measurement using a zero resistance ammeter. The corrosion behavior of AZ31 Mg alloy was also studied by salt spray test. The average galvanic corrosion density during 2 h immersion in 0.1 NaCl solution was found to decrease as an exponential function with increasing the surface area ratios between AZ31:Cu or with increasing the distance between AZ31 and Cu. The corrosion of electrodeposited Cu on AZ31 Mg alloy was concentrated at the area next to Cu (about 5 mm for immersion test and 2 mm for salt spray test) and pitting corrosion was accelerated at the area beyond the severely corroded area by the galvanic coupling effect.

• Journal of Welding and Joining
• /
• v.17 no.3
• /
• pp.66-70
• /
• 1999

In order to investigate the quantitative behavior of galvanic corrosion in weld joints between stainless std이 and carbon steel, electrochemical polarization experiments were performed at pH4, pH7 and pH10 with boric acid concentration 4000ppm, and water temperature were selected as $35^{\circ}$C and $60^{\circ}$C. As the results, the galvanic corrosion phenomena of carbon steel weld material at $60^{\circ}$C was revealed $2{1\over2}$ times higher corrosion rate than that at $35^{\circ}$C condition. The corrosion rate of stainless steel was almost inedependent of the variation of pH. The significant corrosion rates of carbon steel and the weld joint of carbon-carbon steel were observed at pH 4.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1043-1044
• /
• 2006

Compositional dependence of corrosion behavior of rapidly solidified Mg-rich Mg-Zn-Y alloys in NaCl aqueous solution has been investigated. Mg-Zn-Y ternary alloys containing small amounts of Zn exhibited low corrosion rate, although the $Mg_{98}Y_2$ (at. %) binary alloy showed severe corrosion with violet evolution of hydrogen. The alloy with highest corrosion-resistance was $Mg_{97.25}Zn_{0.75_Y_2$, its corrosion rate was about 1 mm year-1 in 0.17 M (1.0 wt. %) NaCl solution. $Mg_{97.25}Zn_{0.75}Y_2$ alloy exhibited passive region in anodic polarization curves when immersed in NaCl solution. Rapidly solidification and small amount of Zn addition may bring about an increase in electrochemical homogeneity of Mg-Zn-Y alloys, resulting in enhancement of corrosion resistance.

• Corrosion Science and Technology
• /
• v.7 no.6
• /
• pp.344-349
• /
• 2008

Epoxy coatings were prepared to give a different corrosion protection by reacting it with two different kinds of curing agent, and then effects of the curing agents on the structure, surface hydrophobic tendency, water transport behavior and hence corrosion protection of epoxy coatings were examined using hygrothermal cyclic test, and impedance analysis. In the results of EIS, the corrosion protection of epoxy coating cured by polyamide shows better than epoxy coating cured by polyamide epoxy adduct. It was well agreed with its water transport behavior and hydrophobic tendency.

• Nuclear Engineering and Technology
• /
• v.32 no.6
• /
• pp.595-604
• /
• 2000

Flow-Accelerated Corrosion Behavior of SA106 Gr.C steel in room temperature alkaline solution simulating the CANDU primary water condition was studied using Rotating Cylinder Electrode. Systems of RCE were set up and electrochemical parameters were applied at various rotating speeds. Corrosion current density decreased up to pH 10.4 then it increased rapidly at higher pH. This is due to the increasing tendency of cathodic and anodic exchange half-cell current. Corrosion potential shifted slightly upward with rotating velocity. Passive film was formed from pH 9.8 by the mechanism of step oxidation and the subsequent precipitation of ferrous species into hydroxyl compound. Above pH 10.4, the film formation process was active and the film became stable. Corrosion current density showed increment in pH 6.98 with the rotating velocity, while it soon saturated from 1000 rpm above pH 9.8. This seems that activation process which represents formation of passive film on the bare metal surface controls the entire corrosion process

• Korean Journal of Metals and Materials
• /
• v.49 no.10
• /
• pp.780-789
• /
• 2011

The effects of alloyed carbon on the pitting corrosion, the general corrosion, and the passivity behavior of Fe18Cr10Mn0.4NxC (x=0~0.38 wt%) alloys were investigated by various electrochemical methods and XPS analysis. The alloyed carbon increased the general corrosion resistance of the FeCrMnN matrix. Carbon enhanced the corrosion potential, reduced the metal dissolution rate, and accelerated the hydrogen evolution reaction rate in various acidic solutions. In addition, carbon promoted the pitting corrosion resistance of the matrix in a chloride solution. The alloyed carbon in the matrix increased the chromium content in the passive film, and thus the passive film became more protective.

• Nuclear Engineering and Technology
• /
• v.54 no.3
• /
• pp.984-990
• /
• 2022

Corrosion release behavior of Alloy 690 in high-temperature water was investigated under the conditions of injected Zn concentrations of 0 ppb, 10 ppb and 50 ppb. A protective oxide film composed of Zn(Fe_xCr_1-x)₂O₄ and Cr₂O₃ was formed with Zn injection, resulting in a better corrosion resistance. In comparison with the Zn-free condition, the corrosion release rate under the Zn-injection conditions was smaller. The corrosion release inhibiting factors were 1.7 and 1.9 under the conditions of 10 ppb and 50 ppb Zn-injection respectively. A foreseen application of the corrosion and corrosion release rates has been proposed and discussed.

• Advances in materials Research
• /
• v.13 no.3
• /
• pp.183-194
• /
• 2024

D3 tools steel and 440C stainless steel (SS) are normally being employed for application such as knife blade and cutting tools. These steels are iron alloys which have high carbon and high chromium content. In this study, lab work focused on the microstructural and corrosion behavior of D3 tools steel and 440C SS after went through heat treatment processes. Heat treatments for both steels were started with normalizing at 1020 ℃, continue with hardening at 1000 ℃followed by oil quenching. Cryogenic treatment was carried out in liquid nitrogen for 24 hours. The addition of cryogenic heat treatment is believed to increase the hardness and corrosion resistance for steels. Both samples were then tempered at two different tempering temperatures, 160 ℃ and 426 ℃. For corrosion test, the samples were immersed in NaCl solution for 30 days to study the corrosion behavior of D3 tool steel and 440C SS after heat treatment. The mechanical properties of these steels have been investigated using Rockwell hardness machine before heat treatment, after heat treatment (before corrosion) and after corrosion test. Microstructure observation of samples was carried out by scanning electron microscopy. The corrosion rate of these steels was calculated after the corrosion test completed. From the results, the highest hardness is observed for D3 tool steel which tempered at 160 ℃(54.1 HRC). In terms of microstructural analysis, primary carbide and pearlite in the as-received samples transform to tempered martensite and cementite after heat treatment process. From this research, for corrosion test, heat treated 440C SS sample tempered with 426 ℃possessed the excellent corrosion resistance with corrosion rate 0.2808 mm/year.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05a
• /
• pp.274-277
• /
• 2006

There are many structures attacked by chloride ions near a marine environment. And they are attacked by a salt of de-icing chemicals. So, the embedded reinforcement is corroded. In the same time, these are under a fatigue loading by a traffic loading in bridges. In previous studies, there are many researches that deal with a bond behavior under a monotonic loading according to the rate of a steel corrosion. But there are most cases that the steel corrosion and the repeated loading are acted on structures simultaneously. So, in this study, it is investigated a fatigue-bond behavior of RC structures under a steel corrosion and a fatigue loading. Main variables of the test are a corrosion of steel reinforcement and a level of stress.