• Journal of Ocean Engineering and Technology
• /
• v.22 no.2
• /
• pp.50-57
• /
• 2008

The effect of weld improvement on the corroded fatigue life of welded structures was investigated. Toe grinding, TIG dressing and weld profiling were used as the geometric improvement methods. Fatigue tests under the corroded condition in artificial seawater were carried out to investigate the corrosion fatigue behavior of API 2W Gr.50T steel plate produced by POSCO. The test results in weld improved conditions were compared with those in as-welded condition. The test results were also compared with the design curves in UK DEn Class F. Corroded fatigue life of weld improved specimens was longer than that of as-welded specimen. Especially, the corroded fatigue life exceeded the mean SN curve in air of UK DEn Class F.

• International Journal of Concrete Structures and Materials
• /
• v.11 no.2
• /
• pp.247-259
• /
• 2017

This paper presents a fatigue assessment model that was developed for corroded reinforced concrete (RC) beams strengthened using prestressed carbon fiber-reinforced polymer (CFRP) sheets. The proposed model considers the fatigue properties of the constituent materials as well as the section equilibrium. The model provides a rational approach that can be used to explicitly assess the failure mode, fatigue life, fatigue strength, stiffness, and post-fatigue ultimate capacity of corroded beams strengthened with prestressed CFRP. A parametric analysis demonstrated that the controlling factor for the fatigue behavior of the beams is the fatigue behavior of the corroded steel bars. Strengthening with one layer of non-prestressed CFRP sheets restored the fatigue behavior of beams with rebar at a low corrosion degree to the level of the uncorroded beams, while strengthening with 20- and 30%-prestressed CFRP sheets restored the fatigue behavior of the beams with medium and high corrosion degrees, respectively, to the values of the uncorroded beams. Under cyclic fatigue loading, the factors for the strengthening design of corroded RC beams fall in the order of stiffness, fatigue life, fatigue strength, and ultimate capacity.

• Journal of the Korean Society for Railway
• /
• v.8 no.6 s.31
• /
• pp.525-532
• /
• 2005

Fatigue life of catenary wires in various environments is reduced when stress is concentrated on some points, which are often found in corroded areas by surrounding pollutants. Therefore, the fatigue test were performed in order to investigate the effect of the surface corrosion on the destructive behavior in service environment and accelerated corrosion environment as well as th examine the corrosive property and mechanism of the catenary wires. In the fatigue test of the messenger stranded wire, the corrosion degraded materials showed 35~50% of fatigue life at a same stress amplitude compared to original material. Because the catenary wires have variable load by the interaction of periodic contacts with pantographs the maximum stresses of trolley wire and messenger wire calculated by simulation at the messenger wire during operation was estimated thought the corrosion behavior interpretation of variable stress and fatigue test.

• Journal of the Korea Concrete Institute
• /
• v.22 no.2
• /
• pp.179-186
• /
• 2010

The bond between steel and concrete in reinforced concrete members is essential to resist external load, but the bond mechanism in reinforced concrete beams deteriorated by steel corrosion has not been clearly known yet. Most existing researches have dealt with the bond behavior of corroded steel under monotonic loading, but scarce are researches dealing with bond behavior of corroded steel under repeated loading. This study includes the experimental investigation on the bond behavior with respect to the various degrees of steel corrosion under repeated loading. According to the test results, the bond strength of corroded steel under monotonic loading increases as the rate of steel corrosion increases unless the splitting crack occurs. The slip versus number of load cycles relation was found to be approximately linear in double logarithmic scale, not only in specimens without steel corrosion but also in specimens with steel corrosion. The test results also show that the steel corrosion does not negatively affect the bond strength of corroded steel after repeated loading unless the splitting crack occurs. But the fatigue life decreases sharply after splitting crack occurs. This research will be helpful for the realistic durability design and condition assessment of reinforced concrete structures.