• Journal of Electrochemical Science and Technology
• /
• 제9권3호
• /
• pp.195-201
• /
• 2018

To enhance the performance of cathodes at low temperatures, a Cu-coated cathode is prepared, and its electrochemical performance is examined by testing its use in a single cell. At $620^{\circ}C$ and a current density of $150mAcm^{-2}$, a single cell containing the Cu-coated cathode has a significantly higher voltage (0.87 V) during the initial operation than does that with an uncoated cathode (0.79 V). According to EIS analysis, the high voltage of the cell with the Cu-coated cathode is due to the dramatic decrease in the high-frequency resistance related to electrochemical reactions. From XPS analysis, it is confirmed that the Cu is initially in the form of $Cu_2O$ and is converted into CuO after 150 h of operation, without any change in the state of the Ni or Li. Therefore, the high initial cell voltage is confirmed to be due to $Cu_2O$. Because $Cu_2O$ is catalytically active toward $O_2$ adsorption and dissociation, $Cu_2O$ on a NiO cathode enhances cell performance and reduces cathode polarization. However, the cell with the Cu-coated cathode does not maintain its high voltage because $Cu_2O$ is oxidized to CuO, which demonstrates similar catalytic activity toward $O_2$ as NiO.

• 공업화학
• /
• 제20권5호
• /
• pp.553-556
• /
• 2009

본 연구의 목표는 열분해 기술의 문제점을 보완하여 유가자원의 회수와 폐기물 처리의 효율을 높이는데 있다. 우선 경제성을 높이기 위해 기존 열분해온도(보통 $500{\sim}1000^{\circ}C$)보다 낮은 $450^{\circ}C$에서의 저온열분해 반응을 시도하였다. 촉매를 사용하여 반응온도와 반응시간을 단축할 수 있었고, 무 산소 상태를 유지시키는데 유리하도록 간접열을 사용하였다. 결과적으로 유가자원인 구리와 합성연료유의 회수율을 증가시킬 수 있었고, 발생하는 부산물과 배가스의 처리효과가 뛰어남을 알 수 있었다. 배가스는 2단의 중화조를 통과시켜 다이옥신은 거의 발생되지 않았으며, 나머지 대기환경기준의 측정항목 또한 기준치 이하를 보였다. 이번 연구에서는 앞에서 말한 저온 열분해장치(GTPK-001)를 제작하였고, 경제적으로나 친환경적으로 상용화 개발이 가능함을 알 수 있었다.

• 공업화학
• /
• 제27권5호
• /
• pp.483-489
• /
• 2016

본 연구에서 쉽고 빠른 마이크로 조사법을 사용하여 합성한 $Cu_2Se$-그래핀 나노복합체를 광촉매 분해 효과를 연구하였다. 제조된 나노복합체는 XRD, SEM, TEM, 라만분광분석, XPS 및 UV-Vis 흡수분광법을 사용하여 특성화하였다. 그리고 광촉매 분해특성을 가시광선 조사하에 표준염료인 로다민 B의 분해를 통하여 연구하였다. $Cu_2Se$-그래핀 복합체는 상당히 우수한 광촉매 분해 효과를 나타내었고, 이는 180 min 동안 가시광선 조사하에서 약 95%의 분해 효과를 나타내고 있음을 이들 결과로부터 알 수 있었다. 결론적으로 $Cu_2Se$-그래핀 복합체는 염료 오염물질에 대한 적합한 촉매로 사용할 수 있음을 확인하였다.

• Korean Chemical Engineering Research
• /
• 제56권2호
• /
• pp.291-296
• /
• 2018

구리 촉매를 이용하여 실리콘으로부터 기체상태의 methylchlorosilanes을 직접 생성하는 공정이 Rochow에 의해 제시되었고 이 후로 직접 생산 반응에 관하여 많은 연구가 진행되어 오고 있다. 직접 반응 촉매로서의 구리 외에 조촉매들을 첨가함으로서 반응의 활성을 증가시키고, 주 생산물인 DMDC 로의 선택도를 증가시키는 연구도 많이 보고되었다. 하지만 반응 기구에 있어서는 DMDC 의 생성을 설명하는 연구 외에 부산물로 함께 생성되는 여러 종류의 methylchlorosilanes 들의 생성과정을 설명하는 연구는 없는 실정이다. 그래서 본 연구에서는 실리콘 표면에 존재하는 것으로 보여지는 실리콘 활성점인 $=SlCl_2$와 $=Si(CH_3)Cl$의 존재를 제시하고 이 활성점 들에 메틸, 염소 및 수소가 첨가되어 methylchlorosilanes이 생성된다고 간주하였다. Methyl chloride ($CH_3Cl$)의 해리 흡착으로 인한 메틸-실리콘 결합의 생성과 해리 흡착한 후 표면에 존재하여 표면 이동을 하는 것으로 간주되는 Cl와 H을 이용하여 각 silanes 의 생성 경로를 제시하였다. 제시된 각 silanes 들의 생성 경로는 반응 결과 생성된 각 silanes의 종류뿐만 아니라 TPD 과정에서 생성되는 silanes 종류의 생성도 정확하게 설명해 주고 있다.

• 전기화학회지
• /
• 제27권1호
• /
• pp.15-31
• /
• 2024

The antimalarial drug hydroxychloroquine sulphate (HCQ) has taken much attention during the first COVID-19 pandemic phase for the treatment of severe acute respiratory infection (SARI) patients. Hence it is interest to study the electrochemical properties and photocatalytic degradation of the HCQ drug. Copper oxide (CuO) nanoparticles, graphene oxide (GO) and CuO/GO NC (nanocomposite) modified carbon paste electrodes (MCPE) are used for the detection of HCQ in an aqueous medium. Electrochemical behaviour of HCQ (20 μM) was observed using CuO/MCPE, GO/MCPE and CuO/GO NC/MCPE in 0.1 M phosphate buffer at pH 7 with a scan rate of 20 to 120 mV s^-1 by cyclic voltammetry (CV). Differential pulse voltammetry (DPV) of HCQ was performed for 0.6 to 16 μM HCQ. The CuO/GO NC/MCPE showed a reasonably good sensitivity of 0.33 to 0.44 μA μM cm^-2 with LOD of 69 to 92 nM for HCQ. Furthermore, the CuO/GO NC was used as a catalyst for the photodegradation of HCQ by monitoring its UV-Vis absorption spectra. About 98% was degraded in about 34 min under visible light and after 4 cycles it was 87%. The improved photocatalytic activity may be attributed to decrease in bandgap energy and enhanced ability for the electrons to migrate. Thus, CuO/GO NC showed good results for both sensing and degradation applications as well as reproducibility.

• 청정기술
• /
• 제20권4호
• /
• pp.375-382
• /
• 2014

금속산화물이 담지된 허니컴 형상의 플라즈마-촉매 반응기를 이용하여 아이소프로필 알코올(isopropyl alcohol, IPA) 저감 및 부산물 생성 거동에 대해 조사하였다. 허니컴 형상의 다공질 세라믹 지지체(주성분: ${\alpha}-Al_2O_3$)에 금속산화물로 산화철($Fe_2O_3$) 또는 산화구리(CuO)를 담지시킨 후, 이 촉매가 동축 원통형 전극구조 내부에 위치하도록 플라즈마-촉매 반응기를 구성하였다. 플라즈마 반응에 의한 IPA 분해속도가 매우 빨랐기 때문에 IPA 분해효율 자체는 금속산화물 담지 여부 및 금속산화물 종류에 관계없이 유사한 것으로 나타났으나, 부산물 생성거동은 촉매종류에 따라 큰 차이를 보여주었다. 아세톤, 폼알데하이드, 아세트알데하이드, 메테인, 일산화탄소 등의 유해 부산물 농도는 $Fe_2O_3/{\alpha}-Al_2O_3$ < $CuO/{\alpha}-Al_2O_3$ < ${\alpha}-Al_2O_3$ 순으로 높게 나타났다. 유량 $1L\;min^{-1}$, IPA 초기농도 5,000 ppm(산소: 10%), 방전전력 47 W의 조건에서 얻어진 $CO_2$ 선택도는 ${\alpha}-Al_2O_3$, $CuO/{\alpha}-Al_2O_3$, $Fe_2O_3/{\alpha}-Al_2O_3$에 대해 각각 40, 80, 95%로서 $Fe_2O_3/{\alpha}-Al_2O_3$가 플라즈마-촉매를 이용한 IPA의 산화에 가장 효과적인 것으로 나타났다. 플라즈마를 단독으로 사용하여 휘발성유기화합물을 분해할 경우 타르형태의 생성물이 반응기에 퇴적되는 문제점이 있으나, 플라즈마-촉매 공정에서는 이러한 현상이 관찰되지 않았으며 촉매의 활성이 그대로 유지되었다.

• 분석과학
• /
• 제28권3호
• /
• pp.182-186
• /
• 2015

본 연구는 상온에서 과망간산칼륨 (KMnO₄)과 망간아세테이트 (Mn(CH₃COO)₂·4H₂O) 수용액을 반응시켜 초산구리 (Cu(CH₃COO)₂·H₂O) 수용액을 공침한 다공성 CuO/MnO₂ 촉매에 대한 물리화학적 특성에 대해 분석하였다. 합성방법은 KMnO₄과 Mn(CH₃COO)₂·4H₂O의 반응 몰비율을 0.3:1, 0.6:1, 1:1로 반응시켜 초산구리 수용액을 망간아세테이트 투입량 대비 10~75 wt%로 공침시켜 구리이온을 담지시켰다. 제조된 촉매는 TGA/DTA, XRD, SEM 및 BET를 통해 촉매에 대한 물리화학적 특성을 분석하였고, 그 결과 반응 몰비율 변화에 따라 γ-MnO₂, α-MnO₂로 상변이가 이루어 졌으며, 반응 몰비율이 0.6:1 일 때 비표면적이 253 m²/g을 갖는 다공성 CuO/γ-MnO₂ 촉매가 제조되었다.

• 대한화학회지
• /
• 제32권1호
• /
• pp.22-29
• /
• 1988

알카리토류 금속-구리-산화아연계 촉매위에서 메탄올-물혼합물이 이산화탄소와 수소로가는 반응을 150$^{\circ}C$${\sim}\;300^{\circ}C$의 온도범위에서 연구하였다. 일반적으로 구리-아연계 촉매에 알카리토류 금속이 첨가되면 촉매의 활성도는 감소하고 이산화탄소 생성에 대한 선택성은 증가했다. 마그네슘-구리-산화아연 촉매에서는 200$^{\circ}C$부터, 바륨-구리-산화아연계 촉매에서는 250$^{\circ}C$부터 촉매활동을 관찰할 수 있었다. 그리고 250$^{\circ}C$에서 이산화탄소 형성에 대해 가장 높은 선택성을 나타낸 촉매는 바륨-구리-산화아연계 촉매이다. 알카리토류 금속과 산화아연이 반응성에 미치는 효과를 조사하기 위해 이들 촉매에 대해 각각 이산화탄소-승온탈착 실험과 수소-승온환원 실험을 실시하였다. 산화마크네슘, 산화칼슘, 산화바륨의 순서로 이산화탄소와의 상호작용이 증가하였으며, 산화아연은 산화구리의 환원온도를 감소시키는 작용을 했다. 이들 결과들로부터 산화아연은 구리의 산화환원과정에서 수소를 활성화시키는 역할을 하며, 알카리토류 금속은 이산화탄소를 흡착한다고 할 수 있겠다.

• Korean Chemical Engineering Research
• /
• 제49권1호
• /
• pp.21-27
• /
• 2011

메탄올 수증기 개질반응에 대한 적용가능성을 파악하기 위하여 메탄올 합성용 촉매인 ICI-M45와 수성가스 전환반응용 촉매인 MDC-3와 MDC-7을 비교 연구하였다. 또한 수성가스전환 반응에 대한 세 촉매의 비교실험도 수행하였다. 그 결과 MDC-7이 메탄올 수증기 개질반응에서 가장 높은 전화율을 보였으며, $H_2$와 $CO_2$ 생성속도 또한 높게 나타났다. 수성가스 전환반응용 촉매인 MDC-7과 메탄올 합성촉매인 ICI-M45를 이용하여 촉매 충진 방법에 따른 메탄올의 전화율에서의 변화를 살펴본 결과, MDC-7 단독보다 낮은 메탄올의 전화율을 보였다. 수성가스 전환반응에서도 DC- 7, MDC-3, 그리고 ICI-M45의 순으로 반응성이 감소하였다. 상기 두 반응에서 MDC-7이 가장 우수한 이유로는 높은 비표면적과 Cu의 분산도, 그리고 적절한 Cu와 Zn의 비율에 기인함을 확인할 수 있었다.

• 마이크로전자및패키징학회지
• /
• 제30권4호
• /
• pp.91-97
• /
• 2023

전기화학적 이산화탄소 (CO₂) 환원은 CO₂를 고부가가치의 탄소화합물로 전환하는 매우 유망한 방법이다. 본 논문에서는 양극 산화법과 원자층 증착법을 이용하여 전기화학적 CO₂ 환원용 SnO₂/Cu(OH)₂ 나노와이어 (NWs) 전극을 합성하는 손쉬운 방법과 그 특성에 대해 보고한다. 제작된 SnO₂/Cu(OH)₂ NWs (-16 mA/cm²)는 -1.0 V (vs. RHE)에서 Cu(OH)₂ NWs (-6 mA/cm²) 대비 더 우수한 전기화학적 성능을 보였다. CO₂ 환원 성능을 확인해 보았을 때도 일산화탄소(CO), 포름산염 (HCOOH) 생성물에 대해 각각 29.72 %, 58.01 %의 높은 페러데이 효율 (FE)을 보였다. 본 연구는 CO₂ 배출로 인한 기후 변화에 대응하는 경제적이며 지속 가능한 방법을 제공할 뿐만 아니라, 전기화학적 CO₂ 환원용 전극 개발에 크게 기여할 것으로 예상된다.