• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.6
• /
• pp.4237-4244
• /
• 2015

This study examined the efflorescence characteristics of a concrete sidewalk block manufactured using recycled stone powder sludge and photocatalytic generated by surface polishing during the sidewalk block manufacturing process. The study evaluated the characteristics of the sidewalk block in terms of its quality, based on the amount of stone powder sludge used, efflorescence, and further based on the mixing ratio and number of applications of the photocatalytic. The experimental results indicated that heavy metals such as lead, hexavalent chrome, cadmium, and mercury were not present in the concrete sidewalk block, thereby confirming the effectiveness of the recycled stone powder sludge. The optimum mixing ratio of used in the concrete sidewalk block (for satisfying KS standard values such as water absorption ratio and flexural strength) was found to be 20%. The concrete sidewalk block incorporating the stone powder sludge and photocatalytic exhibited a water absorption ratio of 5.4% and flexural strength of 5.2 MPa, thereby satisfying the quality standards. Additionally, when the photocatalytic was used, efflorescence did not occur even at the low temperature of $-5^{\circ}C$, and the by the sidewalk block was found to be 70% under normal conditions and 68% when subjected to an accelerated weathering test.

• Cement Symposium
• /
• no.32
• /
• pp.217-221
• /
• 2005

The utilization of calcined clay, in the form of meta kaolin, as a pozzolanic for mortar and concrete has received considerable attention in recent years. so, the influence of waste concrete sludge and meta kaolin on cement concrete strength has been stud

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.765-768
• /
• 2005

This study is investigated the strength properties of ALC(Autocalved Lightweight Concrete) using SPS(Stone Powder Sludge), to develop recycling technique of SPS. At a given replacement percent of SPS and addition percent of foam, the results show that its the strength properties are equal or higher than the quartz used in a raw material of ALC, and it is also found that the addition percent of the foam and the strength properties have a certain relation of linear.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1995.10a
• /
• pp.75-79
• /
• 1995

The results of an experimental study on the manufacture and the mechanical properties of fiber reinforced calcium silicates-cement composites utilizing by products (fly ash or cement sludge) for construction materials are presented in this paper. As the test results show, compressive, tensile, and flexural strength, fracture toughness of fiber reinforced calcium silicates-cement composites were improved by increasing the fly ash and fiber contents, but were decreased by increasing cement sludge contents. Somehat, especially increasing fiber contents the fracture toughness of the composites were remarkably increased. Also, the mechanical properties of the composites reinforcing alkali-resistance GF were higher than those of the composites reinforcing Samoa Pulp.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.157-160
• /
• 2005

The purpose of this study is to efficiently treat the sewage sludge discharged from sewage treatment plants and evaluate the feasibility of the manufacture of lightweight aggregates(LWA) using a large quantity of sewage sludge and inorganic waste binder ;f1y-ash, waste-stone, tailing, phosphogypsum. Then they were burned in different soak temperatures from 1190$^{circ}C$ to 1290$^{circ}C$ with fixed soak time and heating rate at 5 minutes and 20$^{circ}C$/min respectively in order to produce lightweight aggregate (LWA). Experiment were generated to evaluate the quality of LWA as well as the relationship between burning condition and product's quality.

• Journal of the Korea Concrete Institute
• /
• v.29 no.4
• /
• pp.399-406
• /
• 2017

CaO-based by-product, which consist of CaO, $SO_3$, $Al_2O_3$ and so on, has being used to raw materials of CaO compound. When It was applied to recycling water of remicon, concrete performance can be enhanced because hydration reaction of powder material is accelerated. In this study, activated-sludge, which was putted desulfurization gypsum of CaO-based in recycling water, was manufactured to verify effect of them, and then they was investigated by characteristics of cement matrix and mortar. As a results, they indicated reduction of setting time and high soundness in cement matrix, and acceleration of hydration reaction can be verified by XRD analysis. Also, it can be maintained good workability if water content by usage of desulfurization gypsum, which used for production of activated-sludge, was adjusted. In addition, it can be verified strength development by activated-sludge although cement content by usage of desulfurization gypsum was reduced.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.4
• /
• pp.477-482
• /
• 2016

This study investigates the expressions characteristics of compression strength depending on the condition of fresh concrete and cured concrete by producing Non-cement mortar and concrete only with solidified sludge in the dehydrated cake form, recycled concrete and premixed materials(BS, FA) in order to actively use remicon recycling water as resources, rather than as construction waste material. After treating wastewater of pH 12.5 or more with alkali activator and after promoting BS hydration reaction, the amount of BS inflow was found to be increased and compression strength was increased accordingly: these results coincide with the analysis results of TG-DTA and SEM.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.1
• /
• pp.92-99
• /
• 2021

CaO-based by-products composed of CaO, SO3, Al2O3, etc. are generally used as raw materials for CaO compounds. When applied to the recovered water of ready-mixed concrete, the hydration reaction of the powder material is accelerated and concrete performance can be improved. In this study, activated sludge was prepared to apply to the recovered water of ready-mixed concrete by mixing CaO-based hot-rolled slag(C12A7) in the recycling water of ready-m ixed concrete. Cem ent paste setting time and mortar compressive strength performance tests confirmed the effect on the hydration reaction. Therefore, the possibility of concrete application using activated sludge was confirmed.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.4
• /
• pp.395-403
• /
• 2020

CaO-based by-product, which consist of CaO, SO3, Al2O3 and so on, has being used to raw materials of CaO compound. When It was applied to recycling water of remicon, concrete performance can be enhanced because hydration reaction of powder material is accelerated. In this study, activated-sludge, which was putted desulfurization gypsum of CaO-based in recycling water, was manufactured to verify effect of them, and then they was investigated by characteristics of redy-mixde concrete. As a result of concrete tests, it was confirmed that there is no problem of strength or drying shrinkage while ensuring workability. Therefore, the possibility of specific application using activated sludge was confirmed.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.4
• /
• pp.275-282
• /
• 2018

This study examines the ways to address environmental issues by utilizing activated loess to reduce the amount of cements that emit a large amount of carbon dioxide during the process of manufacturing, and by reusing the polysilicon sludge produced as a result of manufacturing polysilicon, one of the components for solar power generation panels. The findings of the experiment showed that the optimal replacement ratio of the polysilicon sludge is 20%, 35% for W/B, and 20% for the ratio of the fine aggregate addition. As it is deemed that utilizing the polysilicon sludge for reinforced concrete may lead to rebar corrosion due to the $CI^-$ contained in the sludge, it can be considered to use for unreinforced concrete or bricks.