• 콘크리트학회논문집
• /
• 제17권5호
• /
• pp.829-834
• /
• 2005

A series of reinforced G109 type specimens was fabricated and pended with a 15 weight percent NaCl solution. Mix design variables included 1) two cement alkalinities (equivalent alkalinities of 0.32 and 1.08), 2) w/c 0.50 and 3) two rebar surface conditions (as-received and wire-brushed). Potential and macro-cell current between top and bottom bars were monitored to determine corrosion initiation time. Once corrosion was initiated, the specimen was ultimately autopsied to perform visual inspection, and the procedure included determination of the number and size of air voids along the top half of the upper steel surface. This size determination was based upon a diameter measurement assuming the air voids to be half spheres or ellipse. The followings were reached based upon the visual inspection of G109 specimens that were autopsied to date. First, voids at the steel-concrete interface facilitated passive film breakdown and onset of localized corrosion. Based upon this, the initiation mechanism probably involved a concentration cell with contiguous concrete coated and bare steel serving as cathodes and anodes, respectively. Second, the corrosion tended to initiate at relatively large voids. Third, specimens with wire-brushed steel had a lower number of voids at the interface for both cement alkalinities, suggesting that air voids preferentially formed on the rough as-received surface compared to the smooth wire brushed one.

• Computers and Concrete
• /
• 제9권2호
• /
• pp.153-169
• /
• 2012

The contribution of steel fibers on the 28-day compressive strength of high-performance steel fiber reinforced concrete was investigated, is presented. An extensive experimentation was carried out over water-cementitious materials (w/cm) ratios ranging from 0.25 to 0.40, with silica fume-cementitious materials ratios from 0.05 to 0.15, and fiber volume fractions ($V_f$= 0.0, 0.5, 1.0 and 1.5%) with the aspect ratios of 80 and 53. Based on the test results of 44 concrete mixes, mathematical model was developed using statistical methods to quantify the effect of fiber content on compressive strength of HPSFRC in terms of fiber reinforcing index. The expression, being developed with strength ratios and not with absolute values of strengths, is independent of specimen parameters and is applicable to wide range of w/cm ratios, and used in the mix design of steel fiber reinforced concrete. The estimated strengths are within ${\pm}3.2%$ of the actual values. The model was tested for the strength results of 14 mixes having fiber aspect ratio of 53. On examining the validity of the proposed model, there exists a good correlation between the predicted values and the experimental values of different researchers. Equation is also proposed for the size effect of the concrete specimens.

• 한국농공학회지
• /
• 제41권2호
• /
• pp.104-110
• /
• 1999

This study was performed to evaluate the properties of permeable polymer concrete with fly ash and CaCO3. The following conclusions are drawn. The static modulusof elasticity is in the range of 1.19 $\times$105 ~1.49$\times$105 kgf/$\textrm{cm}^2$, which is approximately 53 ~56% of that of the normal cement concrete. The oission's number of permeable polymer concrete is in the range of 3.95 ~6.53, which is less than that of the normal cement concrete. The dynamic modulus of elasticity is in the range of 1.29$\times$105 ~1.59$\times$105 kgf/$\textrm{cm}^2$, which is approximately less compared to that of the normal cement of the static modulus . Fly ash 50% and CaCO3 50% filled permeable polymer concrete has showed higher dynamic modulus. The water permeability is in therange of 3.971 ~4.393$\ell$ /$\textrm{cm}^2$/h, and it is largely dependent upon the mix design. These concrete can be used to the structures which need water permeability.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1999년도 봄 학술발표회 논문집(I)
• /
• pp.293-298
• /
• 1999

The crack of concrete induced by the heat of hydration is a serious problem, particularly in concrete structures such as underground box structure, mat-slab of nuclear reactor buildings, dams or large footings, foundations of high rise buildings, etc.. As a result of the temperature rise and restriction condition of foundation, the thermal stress which may induce the cracks can occur. Therefore the various techniques of the thermal stress control in massive concrete have been widely used. One of them is prediction of the thermal stress, besides low-heat cement which mitigates the temperature rise, pre-cooling which lowers the initial temperature of fresh concrete with ice flake, pipe cooling which cools the temperature of concrete with flowing water, design change which considers steel bar reinforcement, operation control and so on. The objective of this paper is largely two folded. Firstly we introduce the cracks control technique by employing low-heat cement mix and thermal stress analysis. Secondly it show the application condition of the cracks control technique like the subway structure in Seoul.

• Advances in concrete construction
• /
• 제6권1호
• /
• pp.29-45
• /
• 2018

This paper investigates the effect of inclusion of glass fibers on mechanical and fracture properties of binary blend geopolymer concrete produced by using fly ash and ground granulated blast furnace slag. To study the effect of glass fibers, the mix design parameters like binder content, alkaline solution/binder ratio, sodium hydroxide concentration and aggregate grading were kept constant. Four different volume fractions (0.1%, 0.2%, 0.3% and 0.4%) and two different lengths (6 mm, 13 mm) of glass fibers were considered in the present study. Three different notch-depth ratios (0.1, 0.2, and 0.3) were considered for determining the fracture properties. The test results indicated that the addition of glass fibers improved the flexural strength, split tensile strength, fracture energy, critical stress intensity factor and critical crack mouth opening displacement of geopolymer concrete. 13 mm fibers are found to be more effective than 6 mm fibers and the optimum dosage of glass fibers was found to be 0.3% (by volume of concrete). The study shows the enormous potential of glass fiber reinforced geopolymer concrete in structural applications.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2002년도 학술논문발표회
• /
• pp.7-12
• /
• 2002

The purpose of this study is to design and to apply the self-compaction concrete mixture to field, having not only high strength but also compensation for shrinkage without thermal crack under 4 sides outer restraint of the member. In the experimental mix, replacement ratio of limestone Powder, CSA expansive additives, and unit water were selected as parameters, using portland blast-furnace slag cement. And, bleeding test, expansibility test, hydration heat analysis were performed. As a results, when Cement is replaced with 35% limestone Powder, 6% CSA expansive additives at unit water 175kg/$m^3$, demanded performances of fresh and hardened self-compaction concrete are accomplished in the field application.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 춘계 학술발표회 제16권1호
• /
• pp.584-587
• /
• 2004

This research investigates the rheological behavior and the confined water ratio of the cement paste and binder condition in order to predict mix design proportion of the high flowing concrete. The purpose of this study is to determine the optimum replacement ratio of binders including fly ash, and lime stone powder by the cement weight. For this purpose, belite cement, blast furnace slag cement and ordinary portland cement are selected. As test results, the confined water ratio shows the following range ; OPC>blast furnace slag cement>belite cement. Therefore, belite cement is proved very excellent cementitious materials in a view point of the flowability. The optimum replacement ratio of lime stone powder is shown over $30\%$ in case of belite cement and about $10\%$ in case of slag cement type. Also, the optimum replacement ratio of fly ash is shown $30\%$ by the cement weight considering the confined water ratio and deformable coefficient of the paste condition.

• 콘크리트학회지
• /
• 제1권1호
• /
• pp.75-86
• /
• 1989

본 본문에서는 실리카 흄을 사용한 고강도 콘크리트의 제조와 역학적 특성 및 최적 배합에 대한 실험적 연구를 수행하였다. 본 본문에서는 주요 실험변수를 물-시멘트비와 혼화재인 실리카 흄의 혼입량으로 정하였으며, 압축강도 및 휨강도와 합렬인장강도 특성을 분석하였다. 실리카흄의 혼입으로 강도가 증가함을 발견하였으나 어느 범위이상의 과도한 혼입은 오히려 강도를 저해하는 것으로 나타났다. 물-시멘트비 0.28에서는 실리카 흄 혼입량이 5%일 때 최대의 강도가 나타났고, 물-시멘트비 0.40에서는 15%, 물-시멘트비 0.55에서는 20%혼입에서 가장 큰 강도가 나타났다. 또한 본 연구에서는 압축강도와 물-시멘트비 및 실리카 흄량 사이의 관계를 도출하여 그 관게식을 제시하였으며, 이 식으로부터 소요강도를 위한 본 배합변수를 유추할 수 있다. 본 연구결과 물-시멘트비 효과와 실리카 흄의 효과가 상쇄되는 구간이 존재하며, 따라서 이들 효과를 함께 고려한 최적배합을 도출하여 제시하고 있다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1996년도 봄 학술발표회 논문집
• /
• pp.107-111
• /
• 1996

The testing specimens were made from the standard mix proportion according to those of domestic PC factories to establish a basic data for the Accelerated Curing Effect. The experimental tests were conducted according to the conditions of each sub-curing periods. By comparing the results of compression tests on de-molded and 28-day water-curing specimens, we find that the most effective curing condition to obtain more than the required design strength after 28 days of water curing may be as follwings; the presteaming period does not affect seriously and less than $30^{\circ}C$/hr-the rate of temperature rise and less than $82^{\circ}C$ - maximum temperature are necessary. It seems that post-curing procedure is very important factor to increase the effect of accelerated curing.

• 콘크리트학회지
• /
• 제9권6호
• /
• pp.195-206
• /
• 1997

산업폐기물인 폐주물사를 재활용하여 에너지절감과 환경오염방지효과를 얻을 수 있다. 반요인실험법을 사용하여 폐주물사를 잔골재에 일정비율 치환한 콘크리트의 적정배합설계제시를 위한 예비실험에서 물-시멘트비, 폐주물사의 잔골재치환율, 잔골재율, 슬럼프와 같은 주요변수와 변수사이의 2차상호작용을 파악하였다. 예비실험결과 폐주물사의 잔골재치환율 70%까지 실시하였을 때 폐주물사를 혼입한 콘크리트의 강도 발현에 가장 중요한 변수는 물-시멘트비로 분석되었고 폐주물사의 잔골재치환율은 거의 영향이 없는 것으로 분석되어 폐주물사를 콘크리트의 잔골재로 대체할 수 있음을 알 수 있었다. 각 변수의 2차상호작용에서는 폐주물사의 잔골재치환율과 잔골재율의 상관관계가 콘크리트의 강도발현에 가장 큰 영향을 미치는 것으로 나타났다. 목표압축강도에 대한 적정배합조건을 폐주물사의 잔골재 치환율에 따라 물-시멘트비, 잔골재율에 대해 제시하였다.