• Journal of the Korean Society for Heat Treatment
• /
• v.28 no.5
• /
• pp.239-249
• /
• 2015

Various amount of NbC carbide was intentionally formed in a matrix-type cold-work tool steel by controlled amount of Nb and C addition. And the effect of NbC addition on the mechanical properties was investigated. Four alloys with different Nb and C contents were cast by vacuum induction melting, then hot forging and spheroidizing annealing were conducted. The machinability of the annealed specimens was examined with 3 different cutting tools. And tensile tests at room temperature were conducted. After quenching and tempering, hardness and impact toughness were measured, while wear resistance was evaluated by disk-on-plate type wear test. The increasing amount of NbC addition resulted in degraded machinability with increased strength, whereas the absence of NbC also led to poor machinability due to high toughness. After quenching and tempering, the additional NbC improved wear resistance with increasing hardness, whereas it deteriorated impact toughness. Therefore, it could be found that a moderate addition of NbC was desirable for the balanced combination of mechanical properties.

• Journal of Magnetics
• /
• v.17 no.2
• /
• pp.86-95
• /
• 2012

This study investigated the effects of adding a third alloying element, Ni, to create $Fe_{70-x}Pd_{30}Ni_x$ (x = 2, 4, 6, 8 at.% Ni) ferromagnetic shape memory alloys (FSMAs). The Ni replaced a portion of the Fe. The $Fe_{70-x}Pd_{30}Ni_x$ alloys were homogenized through hot and cold forging to gain a ~38% reduction in thickness, next they were solution-treated (ST) with annealing recrystallization at $1100^{\circ}C$ for 8 h and quenched in ice brine, and then aged at $500^{\circ}C$ for 100 h. Investigation of the microstructures and magnetostriction indicated that the greater Ni amount in the $Fe_{70-x}Pd_{30}Ni_x$ alloys reduced saturation magnetostriction at room temperature (RT). It was also observed that it was more difficult to generate annealed recrystallization. However, with greater Ni addition into the $Fe_{70-x}Pd_{30}Ni_x$ (x = 6, 8 at.% Ni) alloys, the $L1_0+L1_m$ twin phase decomposition into stoichiometric $L1_0+L1_m+{\alpha}_{bct}$ structures was suppressed after the $500^{\circ}C$/100 h aging treatment. The result was that the $Fe_{70-x}Pd_{30}Ni_x$ (x = 6, 8 at.% Ni) alloys maintained a high magnetostriction and magnetostrictive susceptibility (${\Delta}{\lambda}{_\parallel}{^s}/{\Delta}H$) after the alloys were aged at $500^{\circ}C$ for 100 h. This magnetic property of the $Fe_{70-x}Pd_{30}Ni_x$ (x = 6, 8 at.% Ni) alloys make it suitable for application in a high temperature (T > $500^{\circ}C$) and high frequency environments.