Hot pressing after cold cyclic compaction of Al2O3 powder mixtures containing SiC whiskers or Al2O3 short fibers is studied with emphasis on the effects of cold cyclic compaction. The green density of the mixtures increases as the cycle number increases and the cyclic pressure becomes higher. The higher green density is also obtained by cold cyclic compaction with the lower pressrue than a single stroke cold compaction. To achieve a higher densification during hot pressing, cold cyclic compaction before hot pressing is more efficient compared to the conventional hot pressing process (without cold cyclic compaction). Moreover, a low cyclic pressure did not affect on toughening mechanism by whisker reinforcement.

• Journal of the Korean Ceramic Society
• /
• v.34 no.3
• /
• pp.296-302
• /
• 1997

The effect of cold cyclic compaction on densification of SiC whisker/Al2O3 composite was investigated. Re-lative density of the compact increased as the number of cycle and the compaction pressure increased and the bias pressure decreased. The rate of loading and unloading and the frequency of cold cyclic compaction did not affect much on sliding and rearrangement of the particles. Fracture of SiC whisker was hardly ob-served during cold cyclic compaction and the direction of whisker was randomly oriented throughout the compact regardless of the direction of compaction. Thus, cold cyclic compaction may be an efficient method to densify SiC whisker/Al2O3 composite.

• Journal of the Korean Ceramic Society
• /
• v.30 no.1
• /
• pp.62-68
• /
• 1993

Densification of alumina powder, grain size and fracture toughness of sintered body by hot pressing after cold compaction were investigated and compared to traditional hot pressing process (without cold cyclic compaction). To achieve a higher densification and to reduce the hot pressing time, hot pressing after cold cyclic compaction was more efficient compared to traditional hot pressing. This phenomenon resulted from the increment of packing densityby the acceleration fo rearrangement of powders under cold cyclic compaction. The grain size of sintered body was only dependent on relative density, and densification during hot pressing was governed by thelattice diffusion. Comprisons of grain size, densification mechanism and fracture toughness resulted from hot pressing after/without cold cyclic compaction showed that a low cyclic pressure may not effect on the fragmentation of alumina powders.