• 한국치위생학회지
• /
• 제13권2호
• /
• pp.361-368
• /
• 2013

Objectives : The purpose of this in vitro study was to evaluate the effect of firing cycles on the marginal and internal fit of metal ceramic crown. Methods : Ten same cases of stone models (abutment teeth 11) were manufactured. Ten cobalt-chrome cores were made per each models and the marginal and internal fit was evaluated through a silicone replica technique. The marginal and internal fit of specimens was measured twice. The first measurement was done after manufacturing cobalt-chrome alloy core and the second measurement was done after porcelain firing. T-test of paired sample for statistical analysis was executed with SPSS 12.0K for Windows (${\alpha}$=0.05). Results : Mean(SD) marginal and internal fit were 77.1(23.3) ${\mu}m$ for the cobalt-chrome alloy core group and 84.4(21.9) ${\mu}m$ for the metal-ceramic crown group. They were statistically significant differences between groups for marginal and internal fit (p<.05). Conclusions : All metal ceramic crowns showed marginal and internal fit ranged within the current clinical recommendations.

• 대한치과기공학회지
• /
• 제21권1호
• /
• pp.77-85
• /
• 1999

When producing partial denture using a Chrome-cobalt alloy being used universally, 45 pattern of them to compare casting characters according to 5 burying methods(special ring method, plastic ring method, general metal ring method) and 5 casting directions(straight, upper, lower, left and right directions) were compared and evaluated. The results were as follows : 1. The comparison of casting characters in accordance with burying type shows that the special ring method to install blind air vent using utility wax was the highest rate of 76.9%, followed by 69.1% of the plastic ring to cast without ring and 61.1% of the metal ring method being used universally respectively. Namely the special ring method was best. The significant level was P<0.05 statistically. 2. The comparison of casting character in accordance with casting directions shows that the straight casting was the highest of 77.9%, and followed by right casting of 74.2%, left casting of 66.7%, upper casting of 63.5%, and lower casting of 62.9% respectively, Namely the straight casting was best.

• 대한치과보철학회지
• /
• 제30권2호
• /
• pp.155-166
• /
• 1992

In dentistry, precious metal alloys are, mainly due to economic factors, increasingly displaced by alternatives containing Ni-Cr-Co. There are some reports where hypersensitive reactions to Ni-Cr-Co alloys are presented and discussed. The reactions reported vary from mucosa contact stomatitis to generalized dermatitis without any oral mucosal reaction. The purpose of this study was to investigate the incidence of nickel, chrome, cobalt and copper, and to know whether subjects with positive skin reaction to nickel would also demonstrate adverse intraoral reaction to a non-precious metal nickel. The patch tests were performed in 81 subjects(male 39, female 42) and nickel sulfate 5% aq., potassium bichromate 0.5% at., cobalt chloride 2% aq., & copper sulfate 1% aq., were used for test allergens. And then the intraoral tests were performed in 16 subjects, 8 subjects with positive allergic skin reaction to nickel and 8 subjects with negative allergic skin reaction. A pure metallic nickel plate was attached to the buccal side of the upper second premolar. The results are as follows : 1. The frequency of nickel sensitivity was 9.9% (2 men, 6 women), cobalt was 4.9% (1 man, 3 women), and chrome was 2.5% (2 men) respectively and there was no positive reaction to copper 2. The positive reactions were 8 of 23 (34.8%) with a history of jewelry allergic reactions and 3 of 58 (5.1%) without a history of jewelry allergic reactions. 3. Three of 8 subjects with positive skin reaction. gave reactions to the metal plates.

• 대한치과기공학회지
• /
• 제17권1호
• /
• pp.10-25
• /
• 1995

The purpose of this study is to get the difference of the castability in the production of partial denture between Precious Metal Alloys and Base Metal Alloys accompanied with the frequency of reuse. As materials for an experiment, we selected Baker-444 and Soo-444 and Soo-sung as Precious Metal Alloys, New Crown and Chrome Cobalt as Base Metal Alloys. And we tired to case all of them seven times. The experimental results were as follows : 1) In the probability of segments, Baker-444 showed 100$\pm$0.00%, Soo-sung 97.24$\pm$1.58%, New Crown 95.63$\pm$4.28%, and Chrome Cobalt 91.03$\pm$7.76%. Consequently, Precious Metal Alloys were decidely superior to Base Metal Alloys in the castability. 2) In the view of the acheived result, burn-out temperature and smocking time had greatly affected the castability. 3) After casting, Precious Metal Alloys were much less than Base Metal Alloys in the quantity of consumption. It made much difference from the the compiled stastics(p<0.01)

• Design & Manufacturing
• /
• 제11권3호
• /
• pp.8-12
• /
• 2017

In general, metallic bio-materials is more widely used in solid tissue like bone or tooth than flexible tissue such as skin or muscle. Especially, Cobalt Chrome Molybdenum(Co-Cr-Mo), which is used in tooth surgery, has a great corrosion resistance. Because this bio-material is non-toxic in human body, and has a bio-compatibility that the vital reaction is not occurred with tissue in body. However the chemical reaction is occurred by fatal matter that deteriorate the property of material surface in conventional polishing, and it can affect to fatal disease in human body or decrease the material properties such as hardness, yield strength or bio-compatibility. This surface in poor condition can cause development of corrosion or bacteria. In this study, MR fluid polishing is used to minimize the scratch, pit or surface flaws generated in conventional polishing. Surface roughness is measured according to the polishing condition to obtain fine surface condition.

• 한국분말재료학회지
• /
• 제30권1호
• /
• pp.7-12
• /
• 2023

Metal-additive manufacturing techniques, such as selective laser sintering (SLS), are increasingly utilized for new biomaterials, such as cobalt-chrome (Co-Cr). In this study, Co-Cr gas-atomized powders are used as charge materials for the SLS process. The aim is to understand the consolidation of Co-Cr alloy powder and characterization of samples sintered using SLS under various conditions. The results clearly suggest that besides the matrix phase, the second phase, which is attributed to pores and oxidation particles, is observed in the sintered specimens. The as-built samples exhibit completely different microstructural features compared with the casting or wrought products reported in the literature. The microstructure reveals melt pools, which represent the characteristics of the scanning direction, in particular, or of the SLS conditions, in general. It also exposes extremely fine grain sizes inside the melt pools, resulting in an enhancement in the hardness of the as-built products. Thus, the hardness values of the samples prepared by SLS under all parameter conditions used in this study are evidently higher than those of the casting products.

• 대한치과기공학회지
• /
• 제18권1호
• /
• pp.15-25
• /
• 1996

This study is to measure and compare the hardness and tensile strength of each time after we recast seven times continually only with and metal alloy Chromium-Cobalt alloy used in the production of partial denture frame work. The result of the experiment were as follow; 1) The result of the hardness measurement The result of the first casting was $490.48{\pm}38.38$ and that of the second recasting was $455.18{\pm}35.61$ and form the third recasting. the result were $518.38{\pm}37.68$ and over. The change of the hardness difference between each recasting was as follow; The hardness difference between the first casting and the second recasting was $35.25{\pm}31.93$ and that between the second recasting and the third recasting was $63.20{\pm}54.02$. There was a statistically significant difference(P<0.01) in the above hardness, however, there was little difference on the whole. And after the third recasting, the hardness grew high a little bit. That is why low-melting metals such as Cr, Mn, Cu of alloy ingredient was evaporated or there was an effect of changes in metal crystal structure, I suppose. 2) The result of the tensile strength measurement. There was a statistically significant difference(P<0.01) between the first casting and the second, the fourth recasting, however. there was little difference in general.

• 구강회복응용과학지
• /
• 제27권1호
• /
• pp.73-79
• /
• 2011

연구의 목적은 타이타늄이 함유된 코발트 크롬의 주조성에 타이타늄이 어떠한 영향을 미치는지 평가하기 위함이다. 원재료에는 코발트, 크롬, 몰리브덴, 실리콘, 망간, 탄소, 질소, 티타늄이 사용되었고 이것들을 정량계량하였다. $Biosil^F$ (Degudent, Germany)를 대조군으로 하였고, 실험군에는 티타늄을 1 wt% 에서 4 wt% 까지 각기 다른 함량으로 첨가하여 주조성을 평가하였다. 왁스 패턴은 $30{\times}40$ cm 크기의 직사각형 모양으로, 총 160개의 격자를 함유하고 있다. 원심주조기 (Neutrodyne Easy Ti: Manfredy)를 사용하여 왁스패턴을 주조하였다. 주조성의 평가는 왁스패턴의 4면이 완전한 격자의 수를 육안과 X-ray를 이용하여 검사하였다. 1 wt%에서 3 wt%의 티타늄을 함유한 금속은 대조군과 비슷한 주조성을 나타냈다. 4 wt%의 티타늄을 함유한 금속은 좋지 않은 결과를 보였다. 4 wt% 미만의 티타늄 함유한 실험군의 주조성은 대조군과 비슷하면서도 기계적인 물성은 증가됨을 보였으며 임상에서의 성공적인 사용을 가능케 한다.

• 대한화학회지
• /
• 제23권1호
• /
• pp.52-58
• /
• 1979

금속 디알킬디티오인산염은 윤활유의 산화방지 및 내마모 첨가제로 널리 사용되고 있다. 특히 아연 DDTP가 윤활유 첨가제로서 가장 많이 사용되고 있다. 1차 및 2차 알킬기를 가진 아연, 납, 주석 및 코발트 디알킬디티오인산염을 각각 합성하였다. 합성된 각각의 금속 디알킬디티오인산염에 대하여 윤활유에서의 산화안정성, 열안정성, 금속부식성 및 내마모성을 실험검토하였다. 실험결과, 코발트 DDTP가 크롬합금강에 미치는 내마모성은 다른 화합물에 비하여 극히 우수하였으며 또한 코발트 DDTP는 일정온도 이상에서는 다갈색으로부터 청색으로 변하며 온도의 환원과 더불어 색상도 환원되는 특이한 색상의 온도 감도변화 성질이 있는 것을 알았다. 또한 모든 금속 디알킬디티오인산염은 일정 유효산 농도에 도달되어야만 윤활유의 산화 방지작용을 개시한다는 결과를 얻었다.

• 대한치과기공학회지
• /
• 제33권2호
• /
• pp.121-128
• /
• 2011

Purpose: The purpose of this study is to investigate the level of each metal in non-precious metal alloys dental casting, still used even banned for use and trade by the law, for oral health. Methods: Two kinds of metal alloys were analyzed. One was Ticonium 100 for removable prosthesis and the other was Rexillium V for dental porcelain. Two samples of each metal alloy were made in 0.5g, 1.0g, and 1.5g. Total number of samples were 12. Two kinds of lactic acid Solution, pH7 and pH4.6, were injected into each samples. After injection, each samples had been for 21days ${\pm}$ 1 hour in the water tank of which temperature was $37^{\circ}C$. The level of metal was measured in each sample by inductively couplled plasma-atomic emission spectrometer. Results: In both metal alloys, metals, chrome, nickel, beryllium, and molybdenum, were founded. In Ticonium 1000, the highest level of nickel was 2.531ppm in 1.5g pH4.6 sample while the highest level of nickel was 4.062ppm in 1.5g pH4.6 sample of Rexillium V. In chemical composition of these methal alloys, chrome(14~17%) was much more than beryllium(1.95~1.99%) and molybdenum(5.0~9.0%) but berllium and molybdenum were founded more than chrome in samples. Therefore, chrome showed better anti-corrosion than other metal alloys. In both metal alloys, more metals were founded in higher pH level and more mass. Levels of chrome was significantly different in samples of both metal alloys in each pH level(p<0.05). Levels of nickels was significantly different in samples of both metal alloys in each pH level(p<0.05). Conclusion: For oral health, further studies are needed in nickel-chrome metal alloy and cobalt metal alloy of non-beryllium in addittion to beryllium metal alloy and also long-term studies needed in various period and other non-percious metal alloys for dental casting.