• 한국세라믹학회지
• /
• 제37권5호
• /
• pp.425-431
• /
• 2000

Cobalt ferrite thin films on Corming glass substrate were fabricated by a sol-gel method. Cobalt ferrite thin films with the grain size of 20-35 nm and thickness of 50nm were obtained. Rapid thermal annealing (RTA) and Annealing processes were adopted for comparison of characteristics of the films. Coercivity values were changed with thermal condition and magnetization values were increased as a function of soaking time. With prolonged soaking time, however, it was decreased because of the diffusion of cations from the glass substrate. The RTA process in preparation of cobalt ferrite thin film was the effective way to prevent and to form a single spinel phase in reduced soaking time. The film heated at 600$^{\circ}C$ for 30 minutes by RTA had coercivity of 2,600 Oe, saturation magnetization 460 emu/㎤, and Mr$.$$\delta$ of 1.43 memu/$\textrm{cm}^2$.

• 한국세라믹학회지
• /
• 제43권11호
• /
• pp.703-709
• /
• 2006

We report on the synthesis of highly uniform, single phase zinc and cobalt thin films prepared by the Liquid Phase Deposition (LPD) method. X-Ray diffraction, TGA and EDX measurements support the assumption that the as deposited films are constituted by a mixture of crystallized FeOOH and amorphous M(OH)$_2$ (M=Co, Zn) which is converted upon heat treatment in air at 600?C into the corresponding zinc ferrites. The films with adjustable chemical compositions are identified with a crystal structure as spinel-type and present a spherical or rod-like microstructure, depending on the both the nature and concentration of the divalent transition metal ions. Zinc ferrite thin films present a superparamagnetic behavior above blocking temperatures which decrease with increasing the Zn content and are ferromagnetic at 5 K with coercivities ranging between 797.8 and 948.5 Oe, whereas the cobalt ferrite films are ferromagnetic at room temperature with magnetic characteristics strongly dependent on the chemical composition.

• 한국자기학회지
• /
• 제16권2호
• /
• pp.140-143
• /
• 2006

단결정 상태의 $CoFe_2O_4$ 박막을 rf magnetron sputtering 증착법을 이용하여 (100) MgO 기판 위에 성장시켰다. X선 회절기, Rutherford back-scattering 분석기와 고감도 주사전자현미경을 이용하여 측정한 결과 증착된 박막이 기판과 잘 정렬되어 성장한 것을 확인할 수 있었다. $600^{\circ}C$의 기판 온도에서 성장한 페라이트 박막은 약 200nm크기의 사각형 형태로 규칙적으로 분포되어 있음이 관찰되었다. 그러나 $700^{\circ}C$의 기판 온도에서 성장한 박막은 불규칙한 모양으로 이루어져 있었으며 30nm에서 150nm에 이르는 다양한 입자 크기를 보이고 있었다. 섭동자화기를 이용한 자기이력곡선 측정 결과 성장한 박막의 자화용이축이 기판과 수직하게 배열하는 것을 알 수 있었다. 또한 MgO 기판과 성장 박막과의 격자상수 차이로 인하여 기판과 수직한 방향의 보자력은 매우 큰 값을 나타내었다. 즉 평행한 방향의 보자력은 283 Oe이고 수직한 방향의 보자력은 6800 Oe였다. $700^{\circ}C$의 기판 온도에 서 성장한 페라이트 박막은 $600^{\circ}C$의 기판 온도에서 성장한 박막의 보자력 및 포화자화 값과 유사한 값을 보였으나 각형비는 급격하게 감소하였다.