• Journal of the Korean Ceramic Society
• /
• v.33 no.2
• /
• pp.149-154
• /
• 1996

ZnO and Al-doped ZnO thin films were prepared by sol-gel dip-coating method and electrical and optical properties of films were investigated. Using the zinc acetate dihydrate and acetylaceton(AcAc) as a chelating agent stable ZnO sol was synthesized with HCl catalyst. Adding aluminium chloride to the ZnO sol Al-doped ZnO sol could be also synthesized. As Al contents increase the crystallinity of ZnO thin film was retarded by increased compressive stress in the film resulted from the difference of ionic radius between Zn2+ and Al3+ The thickness of ZnO and Al-doped ZnO thin film was in the range of 2100~2350$\AA$. The resistivity of ZnO thin films was measured by Van der Pauw method. ZnO and Al-doped ZnO thin films with annealing temperature and Al content had the resistivity of 0.78~1.65$\Omega$cm and ZnO and Al-doped ZnO thin film post-annealed at 40$0^{\circ}C$ in vacuum(5$\times$10-5 torr) showed the resistivity of 2.28$\times$10-2$\Omega$cm. And the trans-mittance of ZnO and Al-doped ZnO thin film is in the range of 91-97% in visible range.

• Journal of Adhesion and Interface
• /
• v.6 no.3
• /
• pp.19-25
• /
• 2005

Synthetic rubber based pressure-sensitive adhesives (PSAs) usually containing SIS or SBS block copolymer, tackifier, plasticizer, and other additives are now widely used on various applications. As these PSAs are physically crosslinked and can be applied without the use of solvent, they are thermally processable and environmentally friendly. However these PSAs cannot be used in high temperature applications and in applications where solvent and chemical resistance properties are required. We developed the PSA adding UV curable system, such as thiol-ene system, to increase adhesion properties at elevated temperature. The adhesion properties such as probe tack, peel strength, shear adhesion failure temperature (SAFT) were evaluated. The probe tack test was conducted with varying probe materials and coating thickness of PSAs. Using the contact angle, the surface property of the cured PSAs was also observed.

• Korean Journal of Materials Research
• /
• v.22 no.11
• /
• pp.626-630
• /
• 2012

The properties of SOFC unit cells manufactured using the decalcomania method were investigated. SOFC unit cell manufacturing using the decalcomania method is a very simple process. In order to minimize the ohmic loss of flattened tube type anode supports of solid oxide fuel cells(SOFC), the cells were fabricated by producing an anode function layer, YSZ electrolyte, LSM electrode, etc., on the supports and laminating them. The influence of these materials on the power output characteristics was studied when laminating the components and laminating the anode function layer between the anode and the electrolyte to improve the output characteristics. Regarding the performance of the SOFC unit cell, the output was 246 $mW/cm^2$ at a temperature of $800^{\circ}C$ in the case of not laminating the anode function layer; however, this value was improved by a factor of two to 574 $mW/cm^2$ due to the decrease of the ohmic resistance and polarization resistance of the cell in the case of laminating the anode function layer. The outputs appeared to be as high as 574 and 246 $mW/cm^2$ at a temperature of $800^{\circ}C$ in the case of using decalcomania paper when laminating the electrolyte layer using the in dip-coating method; however, the reason for this is that interfacial adhesion was improved due to the dense structure, which leads to a thin thickness of the electrolyte layer.

• 한국태양에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.34-39
• /
• 2011

Screen printing method is a common way to fabricate the crystalline silicon solar cell with low-cost and high-efficiency. The screen printing metallization use silver paste and aluminum paste for front and rear contact, respectively. Especially the rear contact between aluminum and silicon is important to form the back surface filed (Al-BSF) after firing process. BSF plays an important role to reduces the surface recombination due to $p^+$ doping of back surface. However, Al electrode on back surface leads to bow occurring by differences in coefficient of thermal expansion of the aluminum and silicon. In this paper, we studied the properties of mono crystalline silicon solar cell for rear electrode with aluminum and aluminum-boron in order to characterize bow and BSF of each paste. The 156*156 $m^2$ p-type silicon wafers with $200{\mu}m$ thickness and 0.5-3 ${\Omega}\;cm$ resistivity were used after texturing, diffusion, and antireflection coating. The characteristics of solar cells was obtained by measuring vernier callipers, scanning electron microscope and light current-voltage. Solar cells with aluminum paste on the back surface were achieved with $V_{OC}$ = 0.618V, JSC = 35.49$mA/cm^2$, FF(Fill factor) = 78%, Efficiency = 17.13%.

• 한국태양에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.245-248
• /
• 2011

Many researches have been carried out to improve light absorption in the crystalline silicon solar cell fabrication. The rear reflection is applied to increase the path length of light, resulting in the light absorption enhancement and thus the efficiency improvement mainly due to increase in short circuit current. In this paper, we manufactured the silicon solar cell using the mono crystalline silicon wafers with $156{\times}156mm^2$, 0.5~3.0 ${\Omega}{\cdot}cm$ of resistivity and p-type. After saw damage removal, the dielectric film ($SiN_x$)on the back surface was deposited, followed by surface texturing in the KOH solution. It resulted in single-side texturing wafer. Then the dielectric film was removed in the HF solution. The silicon wafers were doped with phosphorus by $POCl_3$ with the sheet resistance 50 ${\Omega}/{\Box}$ and then the silicon nitride was deposited on the front surface by the PECVD with 80nm thickness. The electrodes were formed by screen-printing with Ag and Al paste for front and back surface, respectively. The reflectance and transmittance for the single-sided and double-sided textured wafers were compared. The double-sided textured wafer showed higher reflectance and lower transmittance at the long wavelength region, compared to single-sided. The completed crystalline silicon solar cells with different back surface texture showed the conversion efficiency of 17.4% for the single sided and 17.3% for the double sided. The efficiency improvement with single-sided textured solar cell resulted from reflectance increase on back surface and light absorption enhancement.

• Journal of the Semiconductor & Display Technology
• /
• v.13 no.3
• /
• pp.27-33
• /
• 2014

To develop high efficiency crystalline solar cells, the $SiN_x$ film for surface passivation and anti-reflection coating is very important and it is generally deposited by PECVD. In this paper, the $SiN_x$ film deposited by Hot-Wire chemical vapor deposition(HWCVD) that has no plasma damage was studied. First, to optimize the $SiN_x$ film deposition process, $SiH_4$ gas rate and substrate temperature were varied and then refractive index and thickness were measured. When $SiH_4$ gas rate was 22sccm and substrate temperature was $100^{\circ}C$, refractive index was 1.94 and higher than that of other process conditions. Second, the lifetime was measured by varying the annealing temperature and time. The annealing process was made from 5 to 30 minutes at $300{\sim}500^{\circ}C$. When the annealing temperature was $100^{\circ}C$ and time was 10minute, the lifetime was the highest. The lifetime of annealed samples was also measured after the firing process at $975^{\circ}C$. Although the lifetime of all samples was decreased by firing process, the lifetime of annealed samples before the firing process was higher than that of fired samples only. Finally, the characteristics of solar cells with HWCVD $SiN_x$ film were measured.

• Korean Journal of Materials Research
• /
• v.9 no.11
• /
• pp.1055-1061
• /
• 1999

Indium Tin Oxide (ITO) films were fabricated by vacuum deposition technique and their microwave shielding properties were investigated for the application to the transparent shield material. The vacuum coating was conducted in a RF co-sputtering machine. The film composition and structure associated with the sputtering conditions (argon and oxygen pressure. substrate temperature. RF input power) were investigated for the attainment of high electrical conductivity and good transparency. The electrical conductivity of IT0 films fabricated under the optimum deposition conditions (substrate temperature : $300^{\circ}C$. Ar flow rate : 20 sccm, Oxygen flow rate : 10 sccm, In/Sn input power : 50/30 W) showed 5.6$\times10^4$mho/m. The optical transparency is also considerably good. The microwave shielding properties including the dominant shielding mechanism are investigated from the electrical conductivity, thickness and skin depth of the ITO films. The total shielding effectiveness is then estimated to be 26 dB, which provides a suggestion that the IT0 films can be effectively used as the transparent shield material.

• The Journal of Advanced Prosthodontics
• /
• v.1 no.2
• /
• pp.68-74
• /
• 2009

STATEMENT OF PROBLEM. When veneering composite resin-metal restoration is prepared, the fact that bond strength between Ti and composite resin is relatively weak should be considered. PURPOSE. The purpose of this study is to evaluate the shear bond strength between the veneering composite resin and commercial pure (CP) Ti / Ti-6Al-4V alloy according to the method of surface treatment. MATERIAL AND METHODS. The disks were cast by two types of metal. Their surfaces were treated by sandblasting, metal conditioner, TiN coating and silicoating respectively. After surface treatment, the disks were veneered by composite resin (Tescera$^{TM}$, Bisco, USA) which is 5 mm in diameter and 3 mm in thickness. The specimens were stored in water at $25^{\circ}C$ for 24 hours, and then evaluated for their shear bond strength by universal testing machine (STM-$5^{(R)}$, United Calibration, USA). These values were statistically analyzed. RESULTS. 1. All methods of surface treatment were used in this study satisfied the requirements of ISO 10477 which is the standard of polymer-based crown and bridge materials. 2. The metal conditioner treated group showed the highest value in shear bond strength of CP Ti, silicoated group, TiN coated group, sandblasted group, in following order. 3. The silicoated group showed the highest value in shear bond strength of Ti-6Al-4V alloy, metal conditioner treated group, sandblasted group, TiN coated group, in following order. CONCLUSION. Within the limitations of this study, all methods of surface treatment used in this study are clinically available.

• Journal of the Korean Ceramic Society
• /
• v.48 no.3
• /
• pp.236-240
• /
• 2011

In order to deposit a homogeneous and uniform ${\beta}$-SiC films by chemical vapor deposition, we demonstrated the phase stability of ${\beta}$-SiC over graphite and silicon via computational thermodynamic calculation considering pressure, temperature and gas composition as variables. The ${\beta}$-SiC predominant region over other solid phases like carbon and silicon was changed gradually and consistently with temperature and pressure. Practically these maps provide necessary conditions for homogeneous ${\beta}$-SiC deposition of single phase. With the thermodynamic analyses, the CVD apparatus for uniform coating was modeled and simulated with computational fluid dynamics to obtain temperature and flow distribution in the CVD chamber. It gave an inspiration for the uniform temperature distribution and low local flow velocity over the deposition chamber. These calculation and model simulation could provide milestones for improving the thickness uniformity and phase homogeneity.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.9
• /
• pp.1035-1040
• /
• 2011

This research was performed on a microfilter made of a hybrid material (ceramic + metal) that was coated with ceramics on the metal-filter surface by using the thermal spray method. The ceramic powders used were $Al_2O_3+40TiO_2$ powder with a particle size of $20{\mu}m$ and $Al_2O_3$ (98%+)powder with a particle size of $45{\mu}m$. The metal filters were filter-grade $20{\mu}m$, $30{\mu}m$, and $50{\mu}m$ sintered metal powder filters (SIKA-R 20 IS, 30 IS, 50 IS; Sinter Metals Filters) and filter-grade $75{\mu}m$ sintered mesh filter with five layers. Ceramic-coated filters that were coated using the thermal spray method had a great influence on powder material, particle size, and coating thickness. However, these filters showed a fine performance when used as micro-filters.