• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.7
• /
• pp.504-509
• /
• 2018

The purpose of this study was to manufacture a high-performance titanium yellow pigment. Anatase type $TiO_2$ was the skeleton of the pigment and $Sb_2O_3$ is used as the color assistant for the coloring agent, $Cr_2O_3$. Mixed raw materials for the pigment were $TiO_2$(98%), $Sb_2O_3$(99.5%), and $Cr_2O_3$(99.5%). The raw materials were mixed by a dry process and crystallized by calcination at $1,000{\sim}1,200^{\circ}C$. The crystalline material was pulverized in a Jar Mill under $1{\mu}m$ by a wet process and dried for 12 hours at $100^{\circ}C$. The pigment was finally made by a fine grinding process. To determine the best temperature for calcination, 4 temperature sections ($1000^{\circ}C$, $1100^{\circ}C$, $1150^{\circ}C$, and $1200^{\circ}C$) were set up. The X-ray diffraction peak of the rutile crystalline structure was highest at $1,150^{\circ}C$. The yellow ceramic pigment, which has the rutile structure, was applied for coating materials. The synthesized pigments underwent a discoloration tests on the acid resistance, alkaline resistance, weather resistance and heat resistance. In addition, a detection test on harmful heavy metals ($Cr^{+6}$) was done. The resulting values (${\Delta}E$) of the weather resistance test (2000hr), acid resistance test, alkaline resistance test, and heat resistance test were 0.74, 0.16, 0.07 and 0.29. The resulting value for heavy metals testing was 34ppm.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.35 no.1
• /
• pp.1-7
• /
• 2002

To study the increased resistance in fish against Vibrio vulnificus known as an important agent of vibrio septicemia in human, we analyzed specific and nonspecific immune response in flounder after administration of V. vulnificus bacterins by oral route. It contained the comparison of antibody concentrations in the sera of flounder after oral administration by two different protocols with uncoated heat killed bacterin of V vulnificus (UHKB, 20 mg/kg body weight), i.e., 4 weeks continuously (group 4W) and taking 2 weeks resting period between the 1st and last week of administration (group 1-2-1W). Even though, 1-2-1W group showed significantly increased level of specific antibody in serum, it did not reach to that of 4W group. Certainly, flounder vaccinated twice a week for four weeks (20 mg/kg b.w.) showed increased concentration of specific antibody against V. vulnificus at week 2 after last administration by oral route and maintained throughout the experimental period. It also was confirmed by the increased numbers of specific antibody secreting cells (SASC) in the leukocytes isolated from the splenocytes of the flounder of 4W group at week 1 after last administration until the end of experimental period. However, enteric, acid-resistant film coated heat killed bacterin (ECHB) did not show both greater immune reaction for antibody production and faster elimination of a challenge dose of V. vulnificus compared with those of the UHKB. These results suggested that UHKB administered by oral route was very effective method to prevent the contamination of V vulnificus in flounder, and did not show the increased antigenicity by coating the surface with acid-resistant film.

• Korean Journal of Dental Materials
• /
• v.44 no.3
• /
• pp.263-272
• /
• 2017

In this study, antibacterial chlorhexidine (CHX)-containing hydroxyapatite (HAp) was coated on titanium and investigated its characteristics. Ti-mSBF-CHX group was prepared by soaking titanium disks in the modified simulated body fluid (mSBF) mixed with CHX. Ti-mSBF group was coated using mSBF without CHX. Ti-mSBF-adCHX group was prepared by soaking Ti-mSBF specimen in CHX-containing solution. The crystallines clusters composed with nano-shaped crystallites were coated on the surface of the Ti-mSBF specimen. The ribbon-shaped crystallites were observed with the crystalline clusters on the Ti-mSBF-CHX specimen. The content of CHX chemical compositions was high in ribbon-shaped crystallites. HAp crystalline structure was dominant for all prepared specimens, and ${\beta}-TCP$ (tricalcium phosphate) and OCP (octacalcium phosphate) crystalline structures were observed in the Ti-mSBF-CHX specimen. FT-IR spectra showed the strong peaks of CHX in Ti-mSBF-adCHX and Ti-mSBF-CHX groups. However, after immersing in a phosphate buffered saline (PBS), CHX was rapidly released in Ti-mSBF-adCHX group, while it was slowly released in Ti-mSBF-CHX. We expect that the coating method of Ti-mSBF-CHX group could be used for protecting inflammation of titanium implant by incorporating antibacterial agent CHX into HAp layer.