• 한국재료학회지
• /
• 제9권2호
• /
• pp.132-138
• /
• 1999

In order to investigate the toughening characteristic by microcrack formation in ceramic composites, $Al_2$O$_3$/(0~20)vol% YAG composites containing equiaxed second grains were fabricated using$ Al_2$$O_3$ during hot-pressing. AE(acoustic emission) measurements have been coupled with fracture toughness experiments of SENB method, to evaluate the microcrack formation and the improvement in fracture toughness of ceramic composites. Formation of microcrack was detected by Ae. The generation of AE events increased with increasing of load when load was applied at specimen. The AE events are generated mainly around at maximum load. Specially, the detected AE evetns of composites are many as compared with monolithic $Al_2$$O_3$. Fracture toughness of composites was improved than that of monolithic alumina. $Al_2$O$_3$/YAG composites exhibit main toughening effects by microcracking, results from mutual coalesence of microcracks being generated under applied load. However, there are few toughening mechanism like microcracking in monolithic alumina.

• 한국세라믹학회지
• /
• 제35권6호
• /
• pp.551-558
• /
• 1998

Detection of microcrack in {{{{ {Al }_{2 } {O }_{3 } }} ceramics were studided by AE(acoustic emission) technique with 4-point bending test in order to evaluate the fracture process and formation of microcrack. Fully-dense alu-mina ceramics having a different grain size were fabricated by varing the hot-pressing temperature. The grain size of alumina increased with increasing the hot-pressing temperature whereas the bending strength decreasd. The microcracks were observed by SEM and TEM. The generation of AE event increased with increasing the applied load and many AE event was generated at maximum applied load. Alumina with smaller grain size shows the generation of many AE event resulting in an increase of microcrack formation. An intergranular fracture is predominantly observed in fine-grained alumina whereas intragranular fracture occurs predominantly in coarse-grained alumina,. Analysis of micorstructure and AE prove that primary mi-crocracks occur within grain-boundaries of alumina. The larger microcracking were formed by the growth and/or coalesence of primary microcracks. Then the materials become to fracuture by main crack gen-eration at the maximum applied load.

• Journal of Welding and Joining
• /
• 제15권6호
• /
• pp.57-65
• /
• 1997

A study was undertaken to determine the influence of welding variables such as shielding and plasma gases, torch standoff, travel speed and heat input, etc. on the quality of plasma arc welds in Zircaloy-4 sheet, 2mm thick. Effect of shielding gases and their flow rates on the mechanical properties of Zircaloy-4 welds by plasma arc welding were determined in terms of tensile, bardness and bend tests. The microstructure and fracture surface of Zircaloy-4 welds were investigated by optical and scanning electron microscopies. In addition, the causes of porosity and undercut in plasma arc welds of Zircaloy-4 were also investigated. Zircaloy-4 weld bead width and depth by helium shielding gas showed a wider and deeper than those by argon. It was found that Zircaloy-4 welds with shielding gas of helium did dxhibit a little smoother and uniform weld beads than those with shielding gas of argon. It was also found that the optimum gas flow rates for Zircaloy-4 welding were 0.45l/min for plasma gas with Ar and 4.5 - 6 l/min for shielding gas with He. In addition, there was no big difference in the microstructure and fracture surface of the weld metals made by either Ar shielding gas or He shielding gas.

• 대한기계학회논문집
• /
• 제18권6호
• /
• pp.1388-1398
• /
• 1994

The fracture toughness and micro-fracture mechanisms of the porous glass and stainless fiber reinforced glass composite were evaluated by using the acoustice mission(AE) technique, fracture toughness $test(K_{IC})$ and the macroscopic observation of the specimen surface which was being under the loading. At initial portion of the loading, the AE signals with low energy, of which origins were considered as the micro-cracks formated at the crack tip, were emitted. With increasing the applied load, AE signals having higher energies were generated due to the coalesence of micro-cracks and fast fracture. Based on the such relationship between AE emission and loading condition, fracture toughness $K_{IAE}$ could be defined successfully be using the $K_I$ value corresponding to an abrupt change of the accumulated AE signal energies emitted during the fracture toughness test. In spite of its brittleness of glass material, nonlinear deformation behavior before maximum load was observed due to the formation of micro-cracks. Further, the stainless fiber may have attributed to the improvement of fracture toughness and the resistance to crack propagation comparing to noncomposited materials Finally, models of the micro-fracture process combined with the AE sources for the porous glass material and its composite were proposed paying attention to the micro-crack nucleation and its coalescence at the crack tip. Fiber fracture and its Pullout, deformation of fiber itself were also delinated from the model.

• 한국세라믹학회지
• /
• 제36권7호
• /
• pp.734-741
• /
• 1999

Al2O3와 t-ZrO2 분말의 압분체를 공기중 150$0^{\circ}C$ 및 1$600^{\circ}C$에서 2시간 소결하여 제조된 입자복합체의 미세구조와 기계적 성질을 조사하였다. 소수의 미세한 구상의 ZrO2입자는 Al2O3의 입내에 존재하였으나 대분분은 입계에 존재하여 Al2O3의 입계를 고정시키는 것이 가능하였고, 따라서 Al2O3의 입성장을 둔화시켰다. 소결할 동안 입계 ZrO2 입자의 조대회는 응집된 ZrO2 입자내에서의 입계의 소멸과 Al2P3 입계의 이동에 의해서 끌어 당겨진 ZrO2 입자의 합체(coalescence)에 의해서 일어날 수 있었다. ZrO2의 첨가에 의한 Al2O3의 기계적 성질의 변화는 기지상인 Al2O3의 미세구조와 분산된 ZrO2 입자의 크기와 구조에 의존하였다.