• Journal of the Korean Ceramic Society
• /
• v.54 no.3
• /
• pp.243-248
• /
• 2017

Pd-doped $SnO_2$ thick film with a pure tetragonal phase was prepared on patterned Pt electrodes by an ink dropping method. Nanostructured $SnO_2$ powder with a diameter of 10 nm was obtained by a modified hydrazine method. Then the ink solution was fabricated by mixing water, glycerol, bicine and the Pd-doped $SnO_2$ powder. When the Pd doping concentration was increased, the grain size of the Pd-doped $SnO_2$ thick film became smaller. However, an agglomerated and extruded surface morphology was observed for the films with Pd addition over 4 wt%. The orthorhombic phase disappeared even at a low Pd doping concentration and a PdO peak was obtained for a high Pd doping concentration. The crack-free Pd-doped $SnO_2$ thick films were able to successfully fill the $30{\mu}m$ gap of the patterned Pt electrodes by the optimized ink dropping method. The prepared 3 wt% Pd-doped $SnO_2$ thick films showed monoxide gas responses ($R_{air}/R_{CO}$) of 4.0 and 35.6 for 100 and 5000 ppm, respectively.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.535-536
• /
• 2013

본 연구에서는 DC/RF co-sputtering공법을 통해 제작한 In-Mo-O 투명 Mo doping 농도 및 열처리 온도에 따른 전기적, 광학적, 구조적 특성을 분석하고, 최적화된 In-Mo-O 투명전극을 유기태양전지(OPVs)와 유기발광다이오드(OLED)에 적용하여 그 가능성을 평가하였다. Mo doping 농도는 co-sputtering 공정 중 MoO3에 인가되는 radio-frequency (RF) power를 변화시켜 조절되었으며, 투명전극의 광학적 특성 및 전기적 특성 향상을 위해 성막 공정 후 급속 열처리 공정을 온도 별로 진행하였다. In-Mo-O 투명 전극은 Mo 도핑 농도에 영향을 받음을 확인할 수 있었고, 최적화된 Mo doping 파워에서 성막한 In-Mo-O 박막은 급속 열처리 공정 후 면저항 24.57 Ohm/square, 투과도 81.57% (400~1,200 nm wavelength)를 나타내었다. Bulk hetero-junction 기반의 고효율 유기태양전지와 유기발광다이오드 적용하기 위해 본 연구에서 제작된 IMO 투명전극의 구조적 특성, 결정성 및 표면특성은 x-ray diffraction (XRD), atomic force microscopy(AFM), field effect scanning electron microscopy (FE-SEM), High-resolution transmission electron microscopy (HRTEM) 분석을 통해 진행하였다. In-Mo-O 투명 전극상에 제작된 OLEDs와 OPV는 reference ITO 전극에 제작된 OLEDs/OPV와 비교할 때 유사하거나 향상된 특성을 나타내었으며 이는 In-Mo-O 박막이 OLED/OPV용 투명 전극으로 적용이 가능함을 말해준다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.262-263
• /
• 2007

Effect of co-doping on optical and electrical properties of $SnO_2$ based thin films were studied. $SnO_2$ ceramic targets with up to 50mol% $CuSb_2O_6$ were prepared by sintering mixed-oxide compact in the temperature range of $1100^{\circ}C{\sim}1300^{\circ}C$ in air. Thin films were then deposited onto glass substrates by pulsed laser deposition where substrate temperature was maintained in the range of $500{\sim}650^{\circ}C$ with oxygen pressure of 3m~7.5mTorr and energy density of $1Jcm^{-2}$. It was found that with the increase amount of dopant, the electrical properties of thin films tended to improve with the smallest resistivity value obtained at about 8mol% doping, further increase, however, usually impaired the optical transmission in the visible range.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.10a
• /
• pp.33.1-33.1
• /
• 2011

Strontium doped lanthanum manganite (LSM) with perovskite structure for SOFC cathode material shows high electrical conductivity and good chemical stability, whereas the electrical conductivity at intermediate temperature below $800^{\circ}C$ is not sufficient due to low oxygen ion conductivity. The approach to improve electrical conductivity is to make more oxygen vacancies by substituting alkaline earths (such as Ca, Sr and Ba) for La and/or a transition metal (such as Fe, Co and Cu) for Mn. Among various cathode materials, $LaSrMnCuO_3$ has recently been suggested as the potential cathode materials for solid oxide fuel cells (SOFCs). As for the Cu doping at the B-site, it has been reported that the valence change of Mn ions is occurred by substituting Cu ions and it leads to formation of oxygen vacancies. The electrical conductivity is also affected by doping element at the A-site and the co-doping effect between A-site and B-site should be described. In this study, the $La_{1-x}Sr_xMn_{0.8}Cu_{0.2}O_{3{\pm}{\delta}}$ ($0{\leq}x{\leq}0.4$) systems were synthesized by a combined EDTA-citrate complexing process. The crystal structure, morphology, thermal expansion and electrical conductivity with different Sr contents were studied and their co-doping effects were also investigated.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.12 no.10
• /
• pp.4660-4665
• /
• 2011

New precursors as a Li adsorbent, $Li_{1.6}(MnM)_{1.6}O_4$ (M=Cu, Ni, Co, Fe), were synthesized by hydrothermal method and their physicochemical properties were discussed. XRD and HRTEM results revealed that the original spinel structure was stabilized by cobalt-doping while Cu-, Ni- and Fe-doping led to structural changes. Such a structural stabilization by Cobalt-doping was maintained after lithium leaching by acid treatment. Li absorption efficiency from seawater was significantly enhanced by using the Cobalt-doped spinel manganese oxide, $Li_{1.6}[MnCo]_{1.6}O_4$, compared to the commercially available $Li_{1.33}Mn_{1.67}O_4$; the adsorbed amount of Li from 1g-adsorbent was 35 and 16 mg by $Li_{1.6}[MnCo]_{1.6}O_4$, and $Li_{1.33}Mn_{1.67}O_4$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.55 no.6
• /
• pp.576-580
• /
• 2018

In this study, a small amount of CoO was added to commercial Gd-doped $CeO_2$ (GDC) powder. The CoO addition greatly enhanced sinterability at low temperatures, i.e., more than 98% of relative density was achieved at $1,000^{\circ}C$. When GDC/8YSZ (8 mol% yttrium stabilized zirconia) bilayers were sintered, Co-doped GDC showed excellent adhesion to the YSZ electrolyte. Transmission electron microscope (TEM) analysis showed that there were no traces of liquid films at the grain boundaries of GDC, whereas liquid films were observed in the Co-doped GDC sample. Because liquid films facilitate particle rearrangement and migration during sintering, mechanical stresses at the interface of a bilayer, which are developed based on different densification rates between the layers, might be reduced. In spite of $Co^{2+}$ doping in GDC, the electrical conductivity was not significantly changed, relative to GDC.

• Journal of the Korean Ceramic Society
• /
• v.52 no.6
• /
• pp.521-526
• /
• 2015

$Ce_{0.8}Gd_{0.2}O_{1.9}$(GDC20) powder was prepared from a mixture of submicron-sized $CeO_2$ powder and Gd precipitates using ammonium carbonate $((NH_4)_2CO_3)$ as a precipitant. The mixture was calcined at $700^{\circ}C$ for 4 h followed by ball-milling that resulted in the GDC powder with an average particle size of $0.46{\mu}m$. The powder had a very uniform particle size distribution with particle sizes ranging from $0.3{\mu}m$ to $1{\mu}m$. Sintering of undoped GDC samples did not show a relative density of 99.2% until the temperature was increased to $1500^{\circ}C$, whereas GDC samples doped with 5 mol% CoO exhibited a significant densification at lower temperature reaching a relative density of 97.6% at $1100^{\circ}C$ and of 98.8% at $1200^{\circ}C$.

• Carbon letters
• /
• v.10 no.2
• /
• pp.123-130
• /
• 2009

Multi-elements doped $TiO_2$ was prepared as a new photocatalyst in order to decrease the band gap of $TiO_2$ by sol-gel process which can provide the large active sites of $TiO_2$. Multi-elements were doped by using a single precursor, tetraethylammonium tetrafluoroborate (TEATFB). By the benefit of large specific surface area of $TiO_2$ prepared by sol-gel process, catalysts showed initial fast removal of dye. The photoactivity showed that the doped catalysts significantly promote the light reactivity than undoped $TiO_2$. The commendable photoactivity of prepared catalysts is predominantly attributable to the doping of anions which may reduce the band gap.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.34 no.5
• /
• pp.186-192
• /
• 1985

Co2O3 additive effects on the electrical properties in ZnO varistor are investigated. As the Co Cations being substituted and ionized normally to a divalent state for Zn in the lattice site increase, the leakage current in the prebreakdown region decreases and the so-called

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.551.2-551.2
• /
• 2006