• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.217-220
• /
• 1999

We investigated the effects of doping elements on the Bi-Sr-Ca-Cu-0 ceramics. The doping elements can be classified into groups depending on their supeconducting characteristics in the Bi -Sr-Ca-Cu -O structure. The first group of doping elements(Co, Fe, Ni and Zn) substitute into the copper site and can reduce the critical temperatures of the 2223 and 2212 phases. The second group of doping elements(Y and La) substitute into the Ca site and cause the disappearance of the 2223 phase and increase the critical temperatures in the 2212 phase.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.04a
• /
• pp.74.2-74.2
• /
• 2000

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.134-137
• /
• 2004

새로운 리튬 2차전지용 양극활물질인 Li[NiMnCo]O2를 간단히 합성할 수 있는 방법과 Si의 doping에 의해 그 특성을 향상하였다. 원하는 당량비의 Li, Ni, Co, Mn의 nitrate를 고순도의 에탄올에 용해하고 여기에 Si의 원료물질로서 poly(methyl phenyl siloxane)을 원하는 양(전체 전이금속 이온의 $2{\sim}10\;mol%$)만큼 첨가한 후 약 30분 정도 교반하였다. 이 용액을 약 $70{\sim}80^{\circ}C$ 정도의 온도에서 고점도의 진흙 상태가 될 정도로 가열하고 $450{\sim}500^{\circ}C$의 온도에서 약 5시간 정도 열처리 하여 유기물이 없는 상태의 전구체를 제조하였다. 이 전구체를 분말형태로 분쇄하고 $600{\sim}650^{\circ}C$ 정도의 온도에서 3시간, $900{\sim}950^{\circ}C$ 정도의 온도에서 5시간 연속적으로 열처리 하여 최종 활물질을 제조하였다. 이렇게 제조된 활물질은 175mAh/g 정도의 높은 비용량을 나타내었으며 4.5V 충전 조건에도 우수한 수명특성을 나타내었다. Si이 doping되지 않은 활물질에 비해 Si이 doping된 물질은 율특성, 수명특성에서 보다 우수한 특성을 나타내었는데 이것은 층상구조 활물질의 격자상수 증가와 impedance 증가 억제에 기인한 것으로 분석되었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.198-203
• /
• 2000

This paper investigated the effects of doping elements on the Bi-Sr-Ca-Cu-O ceramics. The doping elements can be classified into four groups depending on their superconducting characteristics in the Bi-Sr-Ca-Cu-O structure. The first group of doping elements(Co, Fe, Ni and Zn) substitute into the copper site and can reduce the critical temperatures of the 2223 and 2212 phases. The second group of doping elements(Y and La) substitute into the Ca site and cause the disappearance of the 2223 phase and increase the critical temperatures in the 2212 phase. The third group of doping elements(P and K) have a tendency to decompose the superconducting phase and reduce the optimal sintering temperature. The fourth group of doping elements(B, Si, Sn and Ba) almost unaffected the superconductivity of the 2223 and 2212 phase.

• Journal of Sensor Science and Technology
• /
• v.28 no.5
• /
• pp.271-276
• /
• 2019

Pure and 0.5, 1, 2, 5, and 10 at% of Mo-doped $Co_3O_4$ yolk-shell spheres were synthesized by ultrasonic spray pyrolysis of droplets containing Co nitrate, ammonium molybdate, and sucrose and their gas sensing characteristics to 5 ppm trimethylamine (TMA), ethanol, p-xylene, toluene, ammonia, carbon monoxide, and benzene were measured at $225-325^{\circ}C$. The sensor using pure $Co_3O_4$ yolk-shell spheres showed the highest response to p-xylene and very low response to TMA at $250^{\circ}C$, while the doping of Mo into $Co_3O_4$ tended to increase the overall responses of gas sensors. In particular, the sensor using 5 at% Mo-doped $Co_3O_4$ yolk-shell spheres exhibited the high response to TMA with low cross-responses to other interfering gases. The high response and selectivity of Mo-doped $Co_3O_4$ yolk-shell spheres to TMA are attributed to the electronic sensitization by higher valent Mo doping and acid-base interaction between TMA and Mo components.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.6
• /
• pp.1993-1997
• /
• 2012

Mg-doped ZnO one-dimensional (1D) nanostrutures were synthesized by using a thermal evaporation technique. The morphology, crystal structure, and sensing properties of the Mg-doped ZnO nanostructures functionalized with Pt to CO gas at $100^{\circ}C$ were examined. The diameters of the 1D nanostructures ranged from 80 to 120 nm and that the lengths were up to a few tens of micrometers. The gas sensors fabricated from multiple networked Mg-doped ZnO nanowires functionalized with Pt showed enhanced electrical response to CO gas. The responses of the nanowires were improved by approximately 70, 69, 111, and 81 times at CO concentrations of 10, 25, 50, and 100 ppm, respectively. Both the response and recovery times of the nanowire sensor for CO gas sensing were not nearly changed by Pt functionalization. It also appeared that the Mg doping concentration did not influence the sensing properties of ZnO nanowires as strongly as Pt-functionalization. In addition, the mechanism for the enhancement in the CO gas sensing properties of Mg-doped ZnO nanowires by Pt functionalization is discussed.

• Carbon letters
• /
• v.9 no.2
• /
• pp.131-136
• /
• 2008

In order to investigate the effect of doping C, N, B and F elements on $TiO_2$ for reducing the band gap, the heat treatment of $TiO_2$ was carried out with tetraethylammonium tetrafluoroborate. Through XRD and XPS analysis, the C, N, B and F doped anatase $TiO_2$ was confirmed. According to the increase of temperature during treatment, the particle size was increased due to aggregation of $TiO_2$ with elements (B, C, N and F). To investigate the capacity of photocatalyst for degradation of dye under solar light, the degradation of acridine orange and methylene blue was conducted. The degradation of dyes was carried out successfully under solar light indicating the effect of doping elements (B, C, N and F) on $TiO_2$ for reducing the band gap effectively.

• Journal of the Korean Ceramic Society
• /
• v.45 no.3
• /
• pp.167-171
• /
• 2008

Zirconium-doped $Li_{1.1}Co_{1-x}Zr_xO_2(0{\leq}x{\leq}0.05)$ powders as cathode materials for lithium ion batteries were synthesized using an ultrasonic spray pyrolysis method. Cyclic voltammetry and cyclic stability tests were performed, and the changes of microstructure were observed. The solubility limit of zirconium into $Li_{1.1}CoO_2$ was less than 5 mol%, and monoclinic $Li_2ZrO_3$ phase was formed above the limit. The Zr-doping suppressed the grain growth and increased the lattice parameters of the hexagonal $LiCoO_2$ phase. The Zr-dopiong of 1mol% resulted in the best cyclic performance in the range of $3.0{\sim}4.3V$ at 1C rate (140 mA/g); the initial discharge capacity decreased from 158 mAh/g to 60 mAh/g in the undoped powder, while from 154 mAh/g to 135 mAh/g in the Zr-doped powder of 1 mol% after 30 cycles. The excellent cycle stability of Zr-doped powder was due to the low polarization during chargedischarge processes which resulted from the delayed collapse of the crystal structure of the active materials with Zr-doping.

• Journal of Magnetics
• /
• v.1 no.1
• /
• pp.51-54
• /
• 1996

The effects of additional P-doping on the magnetic properties, thermal stability and cation distribution of Co-doped ${\gamma}-{Fe_2} {O_3}$have been investigated by means of magnetic annealing and measurements with vibration sample magnetometer and torque magnetometer. It is found that the P-doping promotes the coercivity and its magnetic-thermal stability, which may be attributed to increase of the cubic magneto-crystalline anisotropy constant, $K_1$ and the activation energy, E, for cation rearrangement, respectively. The cation distribution of P and Co-substituted iron oxide was calculated from the variation of the saturation magnetization with P-doping on the basis of the Neel model. It was found that the most of P ions in the iron oxides occupied the B-site of spinel lattice.

• Journal of the Korean Ceramic Society
• /
• v.54 no.3
• /
• pp.243-248
• /
• 2017

Pd-doped $SnO_2$ thick film with a pure tetragonal phase was prepared on patterned Pt electrodes by an ink dropping method. Nanostructured $SnO_2$ powder with a diameter of 10 nm was obtained by a modified hydrazine method. Then the ink solution was fabricated by mixing water, glycerol, bicine and the Pd-doped $SnO_2$ powder. When the Pd doping concentration was increased, the grain size of the Pd-doped $SnO_2$ thick film became smaller. However, an agglomerated and extruded surface morphology was observed for the films with Pd addition over 4 wt%. The orthorhombic phase disappeared even at a low Pd doping concentration and a PdO peak was obtained for a high Pd doping concentration. The crack-free Pd-doped $SnO_2$ thick films were able to successfully fill the $30{\mu}m$ gap of the patterned Pt electrodes by the optimized ink dropping method. The prepared 3 wt% Pd-doped $SnO_2$ thick films showed monoxide gas responses ($R_{air}/R_{CO}$) of 4.0 and 35.6 for 100 and 5000 ppm, respectively.