• Journal of Magnetics
• /
• v.2 no.3
• /
• pp.72-75
• /
• 1997

The temperature dependent saturation magnetization curve of amorphous Fe67 Co18B14Si1, alloy was measured using a SQUID magnetometer and vibrating sample magnetometer from 5 K up to 800 K. Inelastic neutron neutron scattering measurements also have been used to study the long wavelength spin dynamics of this high Tc amorphous ferromagnetic alloy. The magnon dispersion curve exhibit the conventional quadratic relationship E = D (T) q2 + $\Delta$, typical of an iso=obtained from a low temperature magnetization curve, which was consistent with the value obtained from the analysis oif inelastic neutron scattering data after consideration of its temperature dependence.

• Journal of Magnetics
• /
• v.16 no.4
• /
• pp.431-434
• /
• 2011

The reduction of the Nb content in the $(Fe_{0.75}B_{0.20}Si_{0.05})_{96}Nb_4$ bulk metallic glass (BMG) has been studied. The glass-forming ability (GFA) is reduced by decreasing the Nb content, but it can be enhanced by replacing partially Fe by Co. Furthermore, the saturation magnetization of the $(Fe_{0.8}Co_{0.2})_{76}B_{18}Si_3Nb_3$ BMG is 1.35 T, being with 13% larger than that of the base alloy $(Fe_{0.75}B_{0.20}Si_{0.05})_{96}Nb_4$. $(Fe_{0.8}Co_{0.2})_{76}B_{18}Si_3Nb_3$ BMG exhibits slightly larger $B_{800}$ (the magnetic flux density at 800 A/m) and smaller core losses (20%-30%) compared with the commercial Fe-6.5 mass% Si steel.

• KEPCO Journal on Electric Power and Energy
• /
• v.1 no.1
• /
• pp.109-113
• /
• 2015

초임계 이산화탄소 발전 시스템 구축을 위해서는 고온, 고압의 열악한 환경에 노출되는 터빈, 열 교환기, 압축기와 같은 핵심 부품들의 내식성 평가는 반드시 수행되어야 한다. 이를 위해 후보소재 3종 Ferritic-Martensitic Steel (T92), Austenitic Steel (SS316L), Ni-based Alloy (IN738LC)를 선정하여 고온의 유사 초임계 $CO_2$ 발전 환경에서의 내식성 평가를 진행하였다. $600^{\circ}C$, $700^{\circ}C$의 2개의 온도 구간에서 $CO_2$ 분위기를 조성하여 800 시간 동안 노출시킨 뒤, Weight Change, Surface Morphology, Cross Section, Composition을 분석하였다. Cr-rich Protective Layer를 형성하는 Ni-based Alloy와 Fe/Cr-rich oxide를 형성하는 Austenitic Steel은 우수한 부식 저항성을 보인 반면에 Ferritic-Martensitic Steel은 높은 Weight Change와 Fe-rich Non-Protective Oxide가 관찰되어 상대적으로 낮은 부식 저항성을 보였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.241-241
• /
• 2007

We fabricated SmBCO coated conductors(CCs) on IBAD-MgO templates using co-evaporation method. IBAD-MgO templates consist of PLD-LMO/epi-MgO/IBAD-MgO/Ni-alloy and showed good in-plane texture of below FWHM 7 degree. Evaporation rates of Sm, Ba, and Cu were precisely controlled to get the optimum composition ratio after deposition process. To optimize the oxygen partial pressure of reaction region, wide range of the partial pressure was investigated from 1 mTorr to 15 mTorr. By reducing the oxygen partial pressure to 5mTorr, (103)grains in SmBCO layer have been increased. On the other hand, there were only (001)grains in SmBCO layer deposited at 15 mTorr $O_2$. Deposition temperature was also investigated from $600^{\circ}C\;to\;800^{\circ}C$ to make high Ic SmBCO CCs. SmBCO on IBAD MgO template showed that the Ic increased gradually at higher growth temperature to $800^{\circ}C$, which the highest Jc and Ic is $2.6\;MA/cm^2$ and 500 A/cm-w., respectively.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.4
• /
• pp.179-189
• /
• 2006

High velocity oxygen fuel(HVOF) thermal spray coating of WC-Co powder is one of the most promising candidate for the replacement of the traditional hard chrome plating and ceramics coating because of the environmental problem of the very toxic $Cr^{6+}$ known as carcinogen and the brittleness of ceramics coating. WC-Co micron and nano powder were coated by HVOF thermal spraying method for the study of durability improvement of the high speed spindle. Coatings were planned by Taguchi program for the four spray parameters of spray distance, flow rates of hydrogen, oxygen and powder feed rate. Optimal coating process was obtained by the studies of coating properties such as porosity, surface roughness, micro hardness, and micro structure. WC-Co micron and nano powder were coated on the Inconel 718 substrate by the optimal coating process obtained in this study. The wear behaviors were studied by the sliding wear tester at room temperature and at an elevated temperature of $500^{\circ}C$ for the application to high speed spindle. Sliding wear test was carried out for four most promising hard coatings of chrome coating, ceramics coatings such as $A1_2O_3,\;Cr_2O_3$ and HVOF Co-alloy T800 for the comparison of their wear behaviors. HVOF WC-Co coating was better than other coatings showing highest micro hardness of 1400 Hv and comparable friction coefficients with others. HVOF WC-Co coating is a strong candidate for the replacement of the traditional hard chrome plating for the high speed spindle.