• Korean Journal of Materials Research
• /
• v.4 no.8
• /
• pp.952-957
• /
• 1994

Fe/Co and FeN/CoN multilayer films were prepared by using RF and DC magnetron sputter^ ing technique with Ar or a mixture of Ar and $N_{2}$ gas. Annealing treatment was carried out in a vacuum at temperatures between $100^{\circ}C$ and $500^{\circ}C$ for lhour. Saturation magnetization (MS) and coercivity (Hc) of Fe/Co mutilayer films were investigated as a function of Fe layer thickness and annealing temperature. Permeability ($\mu$) was also examined. Saturation magnetization of 1.8T and coercivity of 1.80e were obtained for the as-deposited Fe/Co($70 \AA /15 \AA$) multilayer film. The Coercivity(Hc) did not change from 1.8 Oe till the annealing temperature $250^{\circ}C$ and then increased rapidly at higher annealing temperatures above $300^{\circ}C$. Coercivity(Hc) measured for the as-deposited FeN/CoN multilayer film was 5 Oe. It decreased gradually with annealing up to $250^{\circ}C$, and then increased rapidly at higher tempera tures.

• Journal of the Korean Magnetics Society
• /
• v.18 no.3
• /
• pp.85-88
• /
• 2008

We calculated the electronic structures of substituted cobalt nitrides, that is $FeCo_3N$ and $NiCo_3Ni$, by using the all electron fullpotential linearized augmented plane-wave (FLAPW) energy band method, and investigated the influence on the magnetic properties of $Co_4N$ due to the substitution of Co atom located at corner sites by iron and nickel atoms. We found that the magnetic moments of CoII atoms located at the face-center positions in these compounds are almost same to that of $Co_4N$. The magnetic moments of Fe and Ni atoms in $FeCo_3N$ and $NiCo_3Ni$ are 3.086 and $0.795\;{\mu}_B$, and they have the localized nature of magnetism.

• Journal of the Korean Magnetics Society
• /
• v.15 no.4
• /
• pp.241-245
• /
• 2005

CoFeNi alloys are some of the most studied soft magnetic materials because of their applications as write-head core materials in HDD and MEMS. Ternary CoFeNi films with high saturation magnetic flux density, Bs and low coercivity, He were successfully grown by electrodeposition. The optimal composition was $Co_{30}\;Fe_{34}\;Ni_{36}(at\%)$, and Bs and Hc were 1.9 T and 0.16 A/m, respectively. The XRD and TEM results show that the low Hc of the CoFeNi films was due to very fine crystal particles and mixed fcc and bcc phases.

• Journal of the Korean Magnetics Society
• /
• v.17 no.3
• /
• pp.120-123
• /
• 2007

The typical double-barrier magnetic tunnel junction (DMTJ) structure examined in this paper consists of a Ta 45/Ru 9.5/IrMn 10/CoFe7/$AlO_x$/free layer/AlO/CoFe 7/IrMn 10/Ru 60 (nm). The free layer consists of an $Ni_{16}Fe_{62}Si_8B_{14}$ 7 nm, $Co_{90}Fe_{10}$ (fcc) 7 nm, or CoFe $t_1$/NiFeSiB $t_2$/CoFe $t_1$ layer in which the thicknesses $t_1$ and $t_2$ are varied. The DMTJ with an NiFeSiB-free layer had a tunneling magnetoresistance (TMR) of 28%, an area-resistance product (RA) of $86\;k{\Omega}{\mu}m^2$, a coercivity ($H_c$) of 11 Oe, and an interlayer coupling field ($H_i$) of 20 Oe. To improve the TMR ratio and RA, a DMTJ comprising an amorphous NiFeSiB layer that could partially substitute for the CoFe free layer was investigated. This hybrid DMTJ had a TMR of 30%, an RA of $68\;k{\Omega}{\mu}m^2$, and a of 11 Oe, but an increased of 37 Oe. We confirmed by atomic force microscopy and transmission electron microscopy that increased as the thickness of NiFeSiB decreased. When the amorphous NiFeSiB layer was thick, it was effective in retarding the columnar growth which usually induces a wavy interface. However, if the NiFeSiB layer was thin, the roughness was increased and became large because of the magnetostatic $N{\acute{e}}el$ coupling.

• Journal of Powder Materials
• /
• v.10 no.5
• /
• pp.333-336
• /
• 2003

The purpose of this study is the fabrication of nano-sized Fe-Co alloy powders with soft magnetic properties by the slurry mixing and hydrogen reduction (SMHR) process. $FeCl_2$0 and $CoCl_2$ powders with 99.9% purities were used for synthesizing nanostructured Fe-Co alloy powder. Nano-sized Fe-Co alloy powders were successfully fabricated using SMHR, which was performed at 50$0^{\circ}C$ for 1 h in H$_2$ atmosphere. The fabricated Fe-Co alloy powders showed $\alpha$' phase (ordered body centered cubic) with the average particle size of 45 nm. The SMHR powder exhibited low coercivity force of 32.5 Oe and saturation magnetization of 214 emu/g.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.4 no.1
• /
• pp.57-62
• /
• 1994

$YbFeCoO_4$ single crystal was grown by floating zone method. The atmospheric condition of the growth was controlled in air and the growth rate was 1~2 mm/hr. After melting the feed rod of the composition of $YbFeCoO_4$, $YbFeCoO_4$ was decomposed to $YbFeCoO_4$ and CoO phase in the initial state of the growth. The liquid composition, however, changed to the direction of the eutectic point along the liquidus line and then stopped at the point in which $YbFeCoO_4$ single crystal could be grown. The growth direction of the crystal was preferred orientation [110], perpendicular to the c-axis in the hexagonal system due to using the polycrystalline seed.

• Journal of the Korean Magnetics Society
• /
• v.9 no.2
• /
• pp.104-110
• /
• 1999

The effect of the composition and the heat treatment on the magnetic and magnetoresistance properties in AgCo alloy films and Fe/AgCo/Fe trilayers prepared by the co-evaporation method were studied. As the alloy film thickness decreases, especially below 50 nm thick, the magnetoresistance decreases and the saturation field increases significantly. The change of the Co content, heat treatment, and deposition of the Fe under/over-layer were effective to prevent the reduction of the and the increasing of the saturation field. For 40 at.%Co sandwiches, the minimum saturation field was obtained in the 20 nm alloy film with 30nm Fe under-over layer annealed at 300 $^{\circ}C$ for 10 min. Its saturation field and the MR ratio were 1.01 kOe 5.16% respectively.

• Journal of the Korean Magnetics Society
• /
• v.11 no.5
• /
• pp.211-216
• /
• 2001

Top synthetic spin valves wi th structure Ta/NiFe/CoFe/Cu/CoFe(Pl)/Ru/CoFe(P2)/FeMn/Ta on Si (100) substrate with SiO$_2$ of 1500 were prepared by dc magnetron sputtering system. We have changed only the thickness of the free layer and the thickness difference (Pl-P2) in the two ferromagnetic layers separated by Ru, and investigated the effect of magnetic film thickness on the GMR properties and the interlayer coupling field in a spin valve with a synthetic antiferromagnet. As thickness difference of pinned layer was decreased from +25 to -25 , MR ratio was decreased gradually. However, there was a dip zone indicating a big change of MR ratio around Pl = P2, which can be due to the large canting of pinned layers. The modified Neel model was suggested for the top synthetic spin valve to explain the interlayer coupling field according to the thickness change of ferromagnetic layers. The interlayer coupling field was decreased due to the magnetostatic coupling (orange peel coupling) as suggested by model. However, the interlayer coupling field was not explained at the dip zone by the modified Neel model. The deviation of modified Neel model at the dip zone could be due to the largely canting of the pinned layers as well, which depends on different thickness in synthetic antiferromagnetic structure.

• Journal of the Korean Magnetics Society
• /
• v.10 no.5
• /
• pp.203-209
• /
• 2000

Top synthetic spin valves with structure Ta/NiFe/CoFe/Cu/CoFe(P 1)/Ru/CoFe(P2)/FeMn/Ta on Si (100) substrate with natural oxide were prepared by dc magnetron sputtering system. We have changed only the thickness in free layers and the thickness difference (Pl-P2) in two ferromagnetic layers separated by Ru, and investigated the effect of magnetic film thickness on interlayer coupling field in spin valve with synthetic antiferromagnet. According to the decrease of free layer thickness, interlayer coupling field was increased due to the magnetostatic coupling(orange peel coupling). In case of t$\_$P1/>t$\^$P2/, interlayer coupling field agreed well with the modified Neel model suggested in conventional spin valve structures by Kools et al. However, in case of t$\_$P1/>t$\^$P2/, it was found that the interlayer coupling field was not explained by the Modified Neel Model and was confirmed the necessity of further remodeling. The dependence of Cu thickness on the interlayer coupling field was investigated and 10 Oe of interlayer coupling field was obtained when the Cu thickness is 32 $\AA$.

• Proceedings of the Korean Magnestics Society Conference
• /
• 1991.05a
• /
• pp.43-44
• /
• 1991