• 한국세라믹학회지
• /
• 제25권1호
• /
• pp.15-20
• /
• 1988

In this study, the specimens of cement clinker minerals such as 80C3-S-15C4AF-5C3A added various blending materials were immersed in artificial seawater. In order to ascertain the effect of SO3 and blending materials on seawater resistance of the specimens, the acceleration experiment in the artificial seawater was carried out by repeating of immersion and drying operation periodically. As inner part of the specimen immersed in artificial seawater, Friedel's salt was produced by reaction with Cl ion. In outer part of the specimen, gypsum and ettringite were mainly formed. With the increase of SO3 content in the specimen the formation of ettringite was increased and Frieldel's salt in inner part was decreased. Total pore volume of the specimens was increased according to the amount of Cl ion penetrated and Mg(OH)2 leached in the solution.

• 한국세라믹학회지
• /
• 제27권8호
• /
• pp.1055-1063
• /
• 1990

The early hydration characteristics of the system $C_3S-C_3A-C_4AF$ according to the clinker composition variations, in order to establish the mutual interactionof clinker minerals during the portland cement hydration, have been studied. The early hydration rate of $C_3S$ was greatly effected by the change of $C_3S/C_3A$ ratio. The lower the $C_3S/C_3A$ ratio was, the faster the apex reaching time and the rate of heat liberation of the 2nd exothermic peak originating from the formation of $Ca(OH)_2$ were. The effect of $C_3S/C_3A$ ration on the amounts of $Ca(OH)_2$ formation was decreased, in process of hydration time, but the effect of $C_3S$ content was increased.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 춘계총회,특별강연,심포지움,연구발표회
• /
• pp.114.2-114.2
• /
• 2000

• 한국건설순환자원학회논문집
• /
• 제11권1호
• /
• pp.16-24
• /
• 2023

미연탄을 사용하는 화력발전소에서 발생되는 석탄재는 Si, Al, Fe 성분을 포함하고 있으며, 이들 성분은 시멘트 클링커에 제조에 필요한 주요성분이다. 특히 Al, Fe 성분은 시멘트 클링커의 간극상을 형성하는 성분으로 시멘트 클링커의 소성에 중요한 영향을 미친다. 본 연구에서는 시멘트 클링커의 원료로서 다량의 석탄재를 함량별로 적용하여, 석탄재를 적용한 시멘트 클링커의 소성온도별 광물형성 과정을 확인하고자 하였다. 석탄재를 다량 적용한 시멘트 클링커는 1050~1150 ℃의 소성온도 구간에서 중간상이 생성되는 것을 확인하였고, 이는 석탄재의 함량이 증가할수록 생성량이 증가하였다. 석탄재의 첨가로 생성된 상은 1350 ℃ 이상에서 칼슘실리케아트상과 간극상으로 전환되어 소멸되는 것으로 예상된다. 시멘트 클링커의 일반적인 소성온도인 1450 ℃에서는 다량의 석탄재를 적용한 시멘트 클링커는 순수원료를 사용하여 제조한 기준 시멘트 클링커와 동등수준의 잘 발달된 광물을 형성하였다.

• 토지주택연구
• /
• 제15권1호
• /
• pp.147-156
• /
• 2024

본 연구는 시멘트 클링커 제조에 사용되는 탄산염 광물인 석회석(CaCO₃)을 CO₂가 결합되어 있지 않은 탈탄산 원료를 사용하여 제조 공정 중에 발생하는 CO₂를 저감하고자 하는 연구로 다양한 산업부산물 중 폐콘크리트에 부착되어 있는 시멘트페이스트를 이용하고자 하였다. 일반적으로 시멘트용 석회석은 최소한 CaCO₃의 함유량이 80% 이상(CaO, 44% 이상)의 것을 사용해야만 시멘트 클링커의 품질을 확보할 수 있다. 하지만 폐콘크리트 미분말의 CaO 함량은 평균 20% 정도로 시멘트 클링커 원료로 사용하기 위하여 CaO 함량을 35% 이상으로 조성비를 올려줘야 이용이 가능하다. 따라서 폐콘크리트 미분말의 조성 광물 경도차이를 이용하여 경도가 상대적으로 낮은 CaO 형태의 광물을 선택적으로 분쇄하여 분급 및 체가름을 할 경우 CaO 함량을 35% 이상 상승시킬 수 있다. 이에 본 연구에서는 분쇄 공정을 통해 경도가 상대적으로 낮은 CaO를 함유한 광물들을 선택적으로 분쇄하여 효율적으로 CaO와 SiO₂ 외 기타 성분을 분리하는 최적 조건에 대하여 실험적 및 통계적으로 검토·분석하였다. 시멘트 크링커 원료로서 탈탄산된 35% 이상 CaO를 함유한 폐콘크리트 미분말 제조를 위한 최적 분쇄 조건 실험 결과, 분쇄 시간 5분 이내, 피분쇄물 종류 30mm, 피분쇄물양 1.0 이상이 최적 조건인 것을 알 수 있었지만 단일 입도의 분쇄물이 아닌 혼합입도의 분쇄물에 대한 검토가 필요할 것으로 판단된다.

• 한국재료학회지
• /
• 제21권12호
• /
• pp.679-684
• /
• 2011

One of the trace constituents included in cement clinker, chromium, has become prominent and highly noticed lately as a social issue both inside and outside of this country because it affects the human body negatively. The purpose of the present study was to investigate leaching properties of water-soluble hexavalent chromium by different manufacturing conditions of cement clinker. Raw materials were prepared to add different $SiO_2$, $Al_2O_3$ and $Fe_2O_3$ sources. After the raw materials, such as limestone, sand and clay, iron ore was pulverized and mixed, and the raw meal was burnt at $1450^{\circ}C$ in a furnace with an oxidizing atmosphere. Leaching of soluble hexavalent chromium showed a tendency to decrease with an increasing LSF and IM. However, leaching of soluble hexavalent chromium increased with an increasing S.M. Alkali contents of iron source minerals is closely related to the leaching properties of soluble hexavalent chromium. Green sludge has the highest content of alkali added; leaching of water-soluble hexavalent chromium was mostly high. In order to reduce the water-soluble hexavalent chromium in cement, reducing the alkali content in raw materials is important.

• 한국세라믹학회지
• /
• 제16권3호
• /
• pp.164-168
• /
• 1979

In the previous paper, it was reported that formation of desirable calcium alunimate(CA) in clinker was considerably affected by sulfur-contaminated alumina which was prone to form a disadvantageous mineral, $C_4A_3S$. In this study, however, sulphate-free alumina cement was made from sulfur-free alumina refined from alunite and corresponding materials. The major minerals in the clinker were identified by X-ray diffraction patterns as calcium aluminate (CA), calcium dialuminate $(CA_2)$ and dicalcium alumino silicate $(C_2AS)$. The formation of CA was more effective with decreasing contents of silica to 2 per cent or less and sulfur in the refined alumina. Physical properties of prepared alumina cement such as setting time, stability and compressive strength were measured. The values were similar to those of commercial alumina cements.

• 공업화학
• /
• 제10권5호
• /
• pp.696-700
• /
• 1999

산업부산자원으로부터 유입되는 중금속이 시멘트 클린커 반응에 미치는 영향과 거동에 대하여 연구하였다. 원료물질에 Cu, Cd, Cr, Pb의 중금속 이온을 500 ppm 첨가하고 $1450^{\circ}C$에서 30분간 소성하여 소성성, 중금속의 고정농도 및 분배율에 따른 거동을 관찰하였다. 중금속의 고정농도는 Pb가 5% 이하로 가장 낮았으며 Cr은 약 85%로 가장 높게 나타났다. $1450^{\circ}C$에서 소성한 Cr을 첨가한 클린커는 free CaO의 함량이 3.41%로 소성성이 낮았으며 기타 중금속의 첨가는 클린커의 반응특성에 크게 영향을 미치지 않았다. 다만 중금속의 휘발로 인하여 클린커 조직에 거대 및 미세 기공이 다수 발생되었다. 클린커 원료에 첨가한 중금속중 Cd와 Cr은 주로 alite와 belite에 분배되었으나 Cu는 간극물질에 집중적인 분배율을 나타냈고 Pb는 휘발도가 높아 클린커 조직내에서 검출한계 내로 존재하지 않는 것으로 나타났다.

• 한국건설순환자원학회논문집
• /
• 제9권4호
• /
• pp.553-560
• /
• 2021

본 연구에서는 순수시료를 사용한 시멘트 클링커와 석탄재를 7% 적용한 클링커를 1050~1500℃의 온도로 소성하여 소성온도별 시멘트 광물의 함량 변화와 미세구조의 변화를 검토하였다. 시멘트 클링커의 원료로서 석탄재의 적용은 알루미나 및 규산질의 공급원으로 적용이 가능하였으며, 석탄재를 적용한 시멘트 클링커는 1350℃ 이상의 소성온도에서 순수원료를 적용한 시멘트 클링커와 동등 수준의 광물량을 나타내었고, 미세구조 또한 유사한 상태를 나타내어 시멘트 원료로서 석탄재의 활용이 가능함을 확인하였다. XRD-Reitveld 분석에서 1250℃에서 Belite의 최대량이 생성되어 1350℃에서부터 Belite에서 Alite로의 전환이 나타났다. 1350℃에서부터 간극상과 Alite로 추정되는 광물상이 구분되며, 1400℃에서부터 명확하게 구분되었다. 소성온도가 증가함에 따라 결정상의 형상과 경계가 명확해지며, 결정상의 크기도 증가되는 것이 나타났다.

• 한국건설순환자원학회논문집
• /
• 제8권4호
• /
• pp.514-519
• /
• 2020

본 연구에서는 시멘트 클링커의 원료 중 점토성분의 일부를 석탄재로 대체하여 시멘트 클링커를 각 온도별로 소성하여 시멘트 클링커의 광물상의 변화를 XRD-Rietveld법을 이용하여 정량분석하였다. 시멘트 클링커의 소성온도가 증가할수록 Belite의 양은 감소하고 Alite의 양은 증가하였으며, 유리 CaO의 양도 감소 되었다. Alite와 Belite의 형태는 1450℃ 이상에서부터 형태를 구분 할 수 있었으며. 1500℃ 소성에서는 결정의 크기가 조대하게 성장하여, 과소성이 진행된 것으로 판단된다. 유리 CaO의 경우 소성온도의 상승에 따라 감소하였고, 1450℃ 이상에서 0.5% 이하로 나타나, 1450℃ 이상에서는 충분한 소성이 이루어진 것으로 판단된다. 따라서 시멘트 클링커의 원료 중 알루미나질과 철질 원료의 화학성분 공급원으로서 석탄재의 활용이 가능한 것이 판단되었다.