• Journal of Ocean Engineering and Technology
• /
• v.23 no.4
• /
• pp.58-63
• /
• 2009

Two kinds of welding methods are used for austenitic 304 stainless steel: laser welding and TIG welding. The difference in the corrosion characteristics of the welded zone between these two welding methods was investigated using electrochemical methods, such as corrosion potential measurements, polarization curves, cyclic voltammograms, etc. The Vickers hardnesses of all the welded zones (WM: Weld Metal, HAZ: Heat Affected Zone, BM: Base Metal) showed relatively higher values in the case of laser welding than for TIG welding. Furthermore, the corrosion current densities of all the welding zones showed lower values compared to TIG welding. In particular, the corrosion current density of the HAZ with TIG welding had the highest value of all the welding zones, which suggests that chromium depletion due to the formation of chromium carbide appears in the HAZ, which is in the range of the sensitization temperature. Thus, it can easily be corroded with a more active anode. Consequently, we found that the corrosion resistance of all of the welding zones for austenitic 304 stainless steel could apparently be improved by using Laser welding.

• Journal of Advanced Marine Engineering and Technology
• /
• v.33 no.8
• /
• pp.1162-1169
• /
• 2009

Two kinds of welding methods were carried out for 22APU stainless steel, one is a Laser welding and the other is the TIG welding. In this case, difference of corrosion characteristics of welded zone with two welding methods mentioned above was investigated with electrochemical methods such as measurement of corrosion potential, polarization curves and cyclic voltammogram etc.. Vickers hardness of all welded zone (WM:Weld Metal, HAZ:Heat Affected Zone, BM:Base Metal)in the case of Laser welding showed a relatively higher value than those of TIG welding. Futhermore their corrosion current density in all welding zone were also observed with a lower value compared to TIG welding. In particular corrosion current density of BM regardless of welding method indicated the lowest value than those of other welding zone. Intergranular corrosion was not observed at the corroded surface of all welding zone in the case of Laser welding, however it was observed at WM and HAZ with TIG welding, which is suggested that chromiun depletion due to forming of chromium carbide appears to WM and HAZ which is in the range of sensitization temperature. Therefore their zone can easily be corroded with more active anode. Consequently we can see that corrosion resistance of all welding zone of 22APU stainless steel can apparently be improved by using of Laser welding.