• Korean Journal of Materials Research
• /
• v.12 no.11
• /
• pp.845-849
• /
• 2002

Alloys of $Fe_3$Al, $Fe_3$Al-6Cr, $Fe_3$Al-4Cr-1Mo, $Ni_3$Al, and $Ni_3$Al-2.8Cr were oxidized at $1000^{\circ}C$ in air, and the oxide scales formed were studied using XRD. SEM, EPMA, and TEM. The oxide scales that formed on $Fe_3$Al-based alloys consisted primarily of $\alpha$-$Al_2$$O_3$ containing a small amount of dissolved Fe and Cr ions, whereas those that formed on $Ni_3$Al-based alloys consisted primarily of $\alpha$-$Al_2$$O_3$, together with a small amount of $NiAl_2$$O_4$, NiO and dissolved Cr ions. For the entire alloys tested, nonadherent oxide scales formed, and voids were inevitably existed at the scale-matrix interface.

• Korean Journal of Materials Research
• /
• v.17 no.6
• /
• pp.308-312
• /
• 2007

Chromium oxide thin films have been deposited on silicon substrates using a tabletop 9kJ mathertyped plasma focus (PF) device. Before deposition, pinch behavior with gas pressure was observed. Strength of pinches was increased with increasing working pressure. Deposition was performed at room temperature as a function of working pressure between 50 and 1000 mTorr. Composition and surface morphology of the films were analyzed by Auger Electron Spectroscopy and Scanning Electron Microscope, respectively. Growth rates of the films were decreased with pressure. The oxide films were polycrystalline containing some impurities, Cu, Fe, C and revealed finer grain structure at lower pressure.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.3
• /
• pp.815-820
• /
• 2011

Three kinds of organometallic compounds (chromium acetylacetonate, magnesium acetate and vanadyl acetylacetonate) were used as transition metal precursor, titanium n-butoxide and multi-walled carbon nanotube as titanium and carbon precursor to prepare metal oxide-CNT/$TiO^2$ composites. The surface properties and morphology of metal oxide-CNT/$TiO^2$ composites were by Brauer-Emett-Teller (BET) surface area measurement, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and energy dispersive X-ray (EDX) analysis. The photocatalytic activity of prepared metal oxide-CNT/$TiO^2$ composites was determined by the degradation effect of methylene blue in an aqueous solution under irradiation of visible light.

• Proceedings of the Korean Nuclear Society Conference
• /
• 2005.10a
• /
• pp.346-347
• /
• 2005

• Transactions of Materials Processing
• /
• v.8 no.3
• /
• pp.319-319
• /
• 1999

From isothermal and cyclic oxidation tests on thermomechanically treated Ti-5%Al, Ti47%Al-4%Cr, and Ti-48%Al-2%Cr-2%Nb alloys at 800, 900, 1000℃ in air, it was found that Ti-48%Al-2%Cr-2%Nb and Ti-47%Al-4%Cr had the best and the worst oxidation resistance, respectively. The oxide scales consisted primarily of TiO₂and Al₂O₃, with and without a small amount of dissolved Cr and 7b ions, depending on the alloy composition. These ions were slightly enriched inside the inner oxide layer, and strongly enriched around the scale-matrix interface. The outer TiO₂-rich layer was formed by the outward diffusion of Ti ions, while the inner (TiO₂+A1₂O₃,) mixed layer was formed by the inward transport of oxygen. The outward movement of Al ions farmed the intermediate Al₂O₃-rich Iayer, above talc prepared alloys.

• Transactions of Materials Processing
• /
• v.8 no.3
• /
• pp.327-327
• /
• 1999

The oxidation behavior of 60%Cu-40%Zn brass haying small amounts of Zr, Cr, Mg, Al, and Si was studied between 873 and 1043 K in air. The alloying element of Mg was harmful, while other alloying elements were beneficial to oxidation resistance. Particularly, the simultaneous addition of Al and Si decreased the oxidation rate drastically. During oxidation, Zr formed ZrO₂, Cr formed CuCr₂O₄, Mg formed MgO, Al formed A1₂CuO₄, and Si formed amorphous SiO₂. These oxides were incorporated in the oxide scale composed predominantly of ZnO. The oxide scales formed on all the tested alloyswere prone to cracking, wrinkling, and spallation.

• Applied Chemistry for Engineering
• /
• v.10 no.1
• /
• pp.85-92
• /
• 1999

The complete catalytic oxidation of vinyl chloride was investigated over chromium oxide supported ${\gamma}$-alumina using a fixed bed micro-reactor at temperature between 240 and $300^{\circ}C$ and concentration between 600 and 3500 ppm. The oxidation of vinyl chloride was nonlinear in the concentration of vinyl chloride and zeroth order in the concentration of oxygen. The addition of HCl and $H_2O$ as products to the feed stream didn't influence the conversion of vinyl chloride. Several kinetic rate model were tested to describe the data over the range of condition investigated, and developed a model which provide the best correlation of experimental data. The resulting model of kinetic rate was derived by assuming that the reacting occurred via adsorption and subsequent decomposition of the vinyl chloride onto the oxygen covered chromium oxide surface, with the reaction being inhibited by the adsorption of vinyl chloride. The percent standard deviation between the predicted and experimental was about 5.2%, and the activation energy was 18.9 kcal/mol.

• Journal of Power System Engineering
• /
• v.13 no.3
• /
• pp.33-39
• /
• 2009

The aim of this study is to analyze the welds characteristics of the 205 stainless steel pipe for application of street pole material. The welds corrosion behavior of STS 205 pipe in 0.1 N sulphuric acid solution and 5% NaCl solution at room temperature was studied using both salt spray test and potentiodynamic polarization experiment. The morphology and components of corrosion products on surface of STS 205 pipe welds were investigated using SEM/EDX. The tensile strength and yield strength values of STS 205 plate were 715 MPa and 369 MPa respectively. The microvickers hardness values of STS 205 pipe welds were slightly increased than that of STS 304 pipe welds. Corrosion current density($I_{corr.}$) and critical current density($I_{crit.}$) values of STS 205 pipe welds in 3.5% NaCl solution were $1.89{\times}10^{-6}$ $A/cm^2$ and $15.8{\times}10 ^{-6}$ $A/cm^2$. The corrosion resistance of SIS 205 pipe welds was similar to its STS 304 pipe welds. The STS 205 and 304 pipe welds passive films were chromium oxide. Especially, the STS 205 pipe welds showed good corrosion resistance in 0.1 N sulphuric acid. This is attributed to the forming of protective chromium oxide on the surface of STS 205 pipe welds.

• Applied Chemistry for Engineering
• /
• v.3 no.4
• /
• pp.663-669
• /
• 1992

Chromium oxide/zirconia catalysts were prepared by dry impregnation of $Zr(OH)_4$ powder with aqueous solution of $(NH_4)_2CrO_4$ followed by calcining in air. The redox behavior of prepared catalysts were investigated by reacting cumene as test material over catalysts. As a result it was found that $Cr^{6+}$ species(as chromate) on the surface of catalyst was responsible for the formation of strong acid site and the catalytic activity for the dealkylation of cumene. However, much of the $Cr^{6+}$ species was reduced to $Cr^{3+}$ species by $H_2$ formed during the catalytic reaction of cumene and the reduced $Cr^{3+}$ species was an active site for dehydrogenation of cumene to form ${\alpha}$-methyl styrene. The reduced $Cr^{3+}$ species was also reoxidized to a $Cr^{6+}$ species after treatment with $O_2$ and consequently the deoxidized catalyst exhibited catalytic activity for the dealkylation reaction of cumene.

• Journal of the Korean Magnetics Society
• /
• v.18 no.3
• /
• pp.89-93
• /
• 2008

Ferrimagnetic Copper-Iron-Chromium Oxide $CuFe_{0.9}Cr_{1.1}O_4$ has been investigated over a temperature range from liquid nitrogen temperature upto $N{\acute{e}}el$ temperature using the Mossbauer technique. Its $N{\acute{e}}el$ temperature is found to be 355 K. Above the $N{\acute{e}}el$ temperature the quadrupole splitting is found to be 0.50 mm/s. On the other hand, all the electric quadrupole shift values are zero below the $N{\acute{e}}el$ temperature within experimental error. These seemingly contradictory phenomena have been explained by the model that the magnetic hyperfine field is randomly oriented with respect to the principal axes of the electric-field-gradient tensor.