• Current Photovoltaic Research
• /
• v.7 no.2
• /
• pp.33-37
• /
• 2019

In this paper, we compared the performance of $Cu(In,Ga)(S,Se)_2$ (CIGSSe) thin film solar cell with CdS buffer layer deposited by irradiating 365 nm UV light with 8 W power in Chemcial Bath Deposition (CBD) process. The effects of UV light irradiation on the thin film deposition mechanism during CBD-CdS thin film deposition were investigated through chemical and electro-optical studies. If the UV light is irradiated during the solution process, the hydrolysis of Thiourea is promoted even during the same time, thereby inhibiting the formation of the intermediate products developed in the reaction pathway and decreasing the pH of the solution. As a result, it is suggested that the efficiency of the CdS/CIGSSe solar cell is increased because the ratio of the S element in the CdS thin film increases and the proportion of the O element decreases. This is a very simple and effective approach to control the S/O ratio of the CdS thin film by the CBD process without artificially controlling the process temperature, solution pH or concentration.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.2
• /
• pp.104-110
• /
• 2001

Structural, optical and electrical properties of Cd$_{1-x}$ Zn$_{x}$S films deposited by chemical bath deposition(CBD), which is a very attractive method for low-cost and large-area solar cells, are presented. Especially, in order to control more effectively the zinc component of the films, zinc acetate, which was used as the zinc source, was added in the reaction solution after preheating the reaction solution and the pH of the reaction solution decreased with increasing the concentration of zinc acetate. The films prepared after preheating and pH control had larger zinc component and higher optical band gap. The crystal structures of Cd$_{1-x}$ Zn$_{x}$S films was a wurtzite type with a preferential orientation of the (002) plane and the lattice constants of the films changed from the value for CdS to those for ZnS with increasing the mole ratio of the zinc acetate. The minimum lattice mismatch between Cd$_{1-x}$ Zn$_{x}$S and CdTe were 2.7% at the mole ratio of (ZnAc$_2$)/(CdAc$_2$+ZnAc$_2$)=0.4. As the more zinc substituted for Cd in the films, the optical transmittance improved, while the absorption edge shifted toward a shorterwavelength. the photoconductivity of the films was higher than the dark conductivity, while the ratio of those increased with increasing the mole ratio of zinc acetate. acetate.