• Journal of the Korean Ceramic Society
• /
• v.53 no.4
• /
• pp.406-410
• /
• 2016

Carbon-coated sodium iron pyrophosphate ($Na_2FeP_2O_7$) was prepared by a simple and low-cost pyro-synthesis route for further use as the cathode for Na-ion batteries. The X-ray diffraction (XRD) pattern of the sample annealed at $650^{\circ}C$ confirmed the pure triclinic phase of $Na_2FeP_2O_7$. Electron microscopy studies revealed a cross linked plate shape morphology of the $Na_2FeP_2O_7$ sample. When tested for application in Na-ion battery, the $Na_2FeP_2O_7$ cathode showed two redox pairs in the potential window of 2.0-4.0 V. The cathode registered initial discharge and charge capacities of 80.85 and 90 mAh/g, respectively, with good cycling performance.

• Carbon letters
• /
• v.9 no.3
• /
• pp.210-217
• /
• 2008

Petroleum pitch and coke with wet mixture method or with dry mixture method were investigated to develop the composite anodic carbon material of high power lithium ion battery. Cokes coated with pitch were obtained by the heat treatment of mixture of cokes and pitch with different weight ratios at $800{\sim}1200^{\circ}C$. The charge and discharge characteristic of the consequent composite anodic carbon material assembled in batteries was tested. Cokes with wet mixture method have a smooth surface and their capacity changed little with changing temperature and content as compared to the cokes with dry mixture method. Although the reversible capacities showed different values by the anode manufacturing method, the composite anode with the mixture of 20 wt% of petroleum pitch and 80 wt% of coke showed the higher power capability and initial efficiency than the pitch based anode. However, the reversible capacity of the composite anode showed the reduced value as compared with the pitch based anode.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.9
• /
• pp.849-854
• /
• 2006

In this study, the hybrid electrodes, composed of the activated carbon powders and $LiCoO_{2}$ powders, were prepared as a cathode for the high-capacitance type hybrid capacitor, and the electrochemical properties of the hybrid electrodes were examined in terms of the weight composition and the milling time of $LiCoO_{2}$ powders. The specific volumetric capacities were increased with increasing of the composition of $LiCoO_{2}$ powders in the hybrid electrodes. On the other hand the coin cell capacitors, using the hybrid electrodes with $LiCoO_{2}$ poweders milled for 200 h, have exhibited the lower internal resistivities and the better capacity retention after 100 charge-discharge cycle than those of the coin cell capacitors using the hybrid electrodes with raw $LiCoO_{2}$ powders.

• Journal of Applied Reliability
• /
• v.17 no.1
• /
• pp.66-71
• /
• 2017

Purpose: Polymer capacitors are known to have very high reliability as compared with liquid electrolytic capacitors, but their capacity has been reported to decrease in charge and discharge at low temperature. The purpose of this study to clarify these characteristics. Methods: In order to clarify these characteristics, charging-discharging tests were carried out for 200 hours with three different capacities and at 5 different temperature from $5^{\circ}C$ to $100^{\circ}C$. Results: As a result of the test, it was confirmed that the capacity of the polymer capacitor was decreased with higher capacity and lower temperature. Conclusion: Such a failure phenomenon was caused by the shrinkage and expansion characteristics of the polymer used therein, it is presumed that this failure phenomenon is due to the complex pore structure made by etching.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.4
• /
• pp.361-366
• /
• 2002

Spinel $LiMn_{2-y}M_yO_4$ and $LiMn_{2-y}M_yO_4$ (M=Mg, Zn) powders were synthesized by solid-state method at $800^{\circ}C$ for 37h. Crystal structure and electrochemical properties were analyzed by X-ray diffraction, charge-discharge test, cyclic voltammetry and ac impedance to $LiMn_{2-y}M_yO_4$. All cathode material showed spinel structure in X-ray diffraction. Ununiform distortion which calculated by (111) face and (222) face was almost constant in spite of the change of the kind and the substituting ratio of the metal cation in $LiMn_{2-y}M_yO_4$ (M=Mg, Zn). $LiMn_{1.9}Mg_{0.05}Zn_{0.05}O_4/Li$ cell substituted $Mg^{+2}$ and $Zn^{+2}$ showed excellent discharge capacities than other cells, which it presented about 120mAh/g at the 1st cycle and about 73mAh/g at the 250th cycle, respectively. AC impedance of $LiMn_{2-y}M_yO_4/Li$ cells showed the similar resistance of about 65~110$\Omega$ before cycling.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.2
• /
• pp.284-291
• /
• 1997

The electrode characteristics of two kinds of metal hydride electrodes using V-Ti (V-rich) based alloy were studied, in which one electrode was prepared by sintering the mixture of V-Ti alloy and Ni powders by a rapid thermal annealing technique and the other one was prepared using V-Ti-Ni ternary alloy, The discharge capacities of all electrodes during the charge-discharge cycling were completely deteriorated within 10 cycles. It appeared that the deterioration of the electrodes was caused by the dissolution of V in the near-surface region into the electrolyte and the formation of $TiO_2$ layer on the alloy particle surface. This degradation mechanism was supported by the facts that V is main hydride forming element and $TiO_2$ has very low electrical conductivity and hydrogen diffusivity.

• Journal of the Korean Electrochemical Society
• /
• v.22 no.3
• /
• pp.122-127
• /
• 2019

In this study, we investigate the electrochemical performance of lithium terephthalate (LTA) battery using graphite coated metal current collector to overcome the disadvantages of organic batteries which is high interfacial resistance between current collector and electrode. The LTA anode material is synthesized by acid-based ion exchange reaction without impurities. The contact properties between stick-type LTA-based electrode and graphite coated current collector are estimated by the cross-section SEM and EIS. The graphite coated current collector significantly reduced the interfacial resistance of the LTA battery. The second discharge capacities of bare current collector LTA and graphite coated current collector LTA batteries are 107.6 mAh/g and 148.8 mAh/g at 0.1C, respectively. The graphite coated current collector LTA batteries show higher cycle life, higher discharge capacity, and higher rate-capability than bare LTA batteries.

• Journal of the Korean Electrochemical Society
• /
• v.15 no.4
• /
• pp.222-229
• /
• 2012

We studied the electrochemical phenomena and increase of capacity according to the polymer composite electrode of two different polymeric materials with different the voltage range and capacity. Polyaniline (PANI) with relatively high voltage and small capacity and poly [1,2] bis-thio[1,8]-naphthylidine (PTND) with slightly low voltage and large capacity were used as polymer composite electrode materials. After PTND was synthesized, PANI was synthesized on the surface of PTND. The synthesis and the fine structure were analyzed by FT-IR, XPS, FE-SEM, and FE-TEM. Charge/discharge capacity and cyclic voltammetry measurements were carried out for the electrochemical performance as a polymer cathode active material for lithium secondary batteries. The discharge capacities of PANI/PTND after 1,5, and 10 cycles at 1.3~4.0 V voltage range and room temperature 167 mAh/g, 90 mAh/g, and 81 mAh/g. When we compared with PANI (80, 67, and 62 mAh/g), the discharge capacity after 10 cycles was improved about 30%. After 50 cycles, the discharge capacity of PANI/PTND was 67 mAh/g.

• Korean Journal of Materials Research
• /
• v.19 no.2
• /
• pp.73-78
• /
• 2009

This study investigated the dependence of the various sputtering conditions (Ar pressure: $2{\sim}10\;mTorr$, Power: $50{\sim}150\;W$) and thickness ($50{\sim}1200\;nm$) of Si thin film on the electrochemical properties, microstructural properties and the capacity fading of a Si thin film anode. A Si layer and a Ti buffer layer were deposited on Copper foil by RF-magnetron sputtering. At 10 mTorr, the 50 W sample showed the best capacity of 3323 mAh/g, while the 100 W sample showed the best capacity retention of 91.7%, also at 10 mTorr. The initial capacities and capacity retention in the samples apart from the 50W sample at 10 mTorr were enhanced as the Ar pressure and power increased. This was considered to be related to the change of the microstructure and the surface morphology by various sputtering conditions. In addition, thinner Si film anodes showed better cycling performance. This phenomenon is caused by the structural stress and peeling off of the Si layer by the high volume change of Si during the charge/discharge process.

• Korean Journal of Materials Research
• /
• v.18 no.9
• /
• pp.457-462
• /
• 2008

Through the electrostatic interaction between the poly-diallydimethylammonium chloride (PDDA) modified Multi-walled carbon nanotube (MWNT) and $SnO_2$ suspension in 1mM $NaNo_3$ solution, MWNT-$SnO_2$ nanocomposites (MSC) for anode electrodes of a Li-ion battery were successfully fabricated by colloidal heterocoagulation method. TEM observation showed that most of the $SnO_2$ nanoparticles were uniformly deposited on the outside surface of the MWNT. Galvanostatic charge/discharge cycling tests showed that MSC anodes exhibited higher specific capacities than bare MWNT and better cyclability than unsupported nano-$SnO_2$ anodes. Also, after 20 cycles, the MSC anode fabricated by heterocoagulation method showed more stable cycle properties than the simply mixed MSC anode. These improved electrochemical properties are attributed to the MWNT, which adsorbs the mechanical stress induced from volume change and increasing electrical conductivity of the MSC anode, and suppresses the aggregation between the $SnO_2$ nanoparticles.