• Journal of the Korean Ceramic Society
• /
• v.35 no.6
• /
• pp.551-558
• /
• 1998

Detection of microcrack in {{{{ {Al }_{2 } {O }_{3 } }} ceramics were studided by AE(acoustic emission) technique with 4-point bending test in order to evaluate the fracture process and formation of microcrack. Fully-dense alu-mina ceramics having a different grain size were fabricated by varing the hot-pressing temperature. The grain size of alumina increased with increasing the hot-pressing temperature whereas the bending strength decreasd. The microcracks were observed by SEM and TEM. The generation of AE event increased with increasing the applied load and many AE event was generated at maximum applied load. Alumina with smaller grain size shows the generation of many AE event resulting in an increase of microcrack formation. An intergranular fracture is predominantly observed in fine-grained alumina whereas intragranular fracture occurs predominantly in coarse-grained alumina,. Analysis of micorstructure and AE prove that primary mi-crocracks occur within grain-boundaries of alumina. The larger microcracking were formed by the growth and/or coalesence of primary microcracks. Then the materials become to fracuture by main crack gen-eration at the maximum applied load.

• Journal of the Korean Ceramic Society
• /
• v.35 no.8
• /
• pp.850-856
• /
• 1998

The dynaamic fatigue behavior of alumina ceramics was observed at room temperature using four-point bending method. Dynamic fatigue fracture strength was observed as function of down speed and notch length. The crack growth exponent of the specimens was calculated from the fracture strength and lifetime in dynamic fatigue test. After loading the stresses in the range of 0% to 105% compared with the average in-ert strength the value of residual fracture strength was measured for unnotched and 0.5mm notched speci-mens at the 0.001 and 0.0005 mm/min down speed respectively. After the 95% stress of the average inert strength was applied repeatedly the value of rsidual fracture strength was measured for 0.5mm notched specimens at the 0.001 and 0.0005 mm/min down speed respectively. The material constant A was found to be almost the same and not to depend on the loading mode or the down speed for unnotched and notched specimen. The value of fracture strength with time calculated from the constants n and A was in good agreement with the measured value.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.4
• /
• pp.405-420
• /
• 2003

Purpose : The purpose of this study was to compare the fracture resistance of the IPS Empress ceramic crown with 1.0mm width rounded shoulder, which is usually recommended in all ceramic crown. and 0.5mm width chamfer finish lines on the maxillary central incisor. Material and method : After 15 metal dies were made for each group, the IPS Empress all ceramic crowns were fabricated and cemented with resin cement(Bistite resin cement, Tokuyama Soda Co. LTD., Japan) on the metal die. The cemented crowns were mounted on the positioning jig and the universal testing machine(Zwick Z020, Zwick Co. Germany)was used to measure the fracture strength with loading on the incisal edge. And also, three-dimensional finite element stress analysis was used to measure the stress distribution with the various types of the finish lines(1.0mm width rounded shoulder, 0.5mm width chamfer), the loading site(incisal edge, incisal $\frac{1}{3}$) and the type of loading(concentration loading, distribution loading). Results and conclusion : 1. In the fracture resistance experiment according to the finish line, the mean fracture strength of rounded shoulder(876N) and the mean fracture strength of chamfer(882N) did not skew any significant difference between each other(p>0.05). 2. The stress distribution of all ceramic crown in three dimensional finite element analysis showed concentration aspect at loading point and cervical area or labial surface. 3. In metal die, there were no differences in stress distribution between finish lines, but in natural teeth model, chamfer finish line showed higher stress than rounded shoulder finish line. 4. When force was loaded on the incisal edge the stress was concentrated on the incisal edge and the cervical area of labial surface. When force was loaded on the incisal $\frac{1}{3}$, the stress concentrated on the cervical area of labial surface and the cingulum area. 5. Generally, natural teeth model showed higher and various stress than the metal die.

• The Journal of Korean Academy of Prosthodontics
• /
• v.43 no.1
• /
• pp.30-40
• /
• 2005

Purpose. The purpose of this study was to compare the fracture strength of the IPS Empress ceramic crown according to the incisal reduction (2.0mm, 2.5mm, 3.0mm) and axial inclination ($4^{\circ}$, $8^{\circ}$, $12^{\circ}$) of the upper canine. Material and methods. After 10 metal dies were made for each group, the IPS Empress ceramic crowns were fabricated and each crown was cemented on each metal die with resin cement. The cemented crowns mounted on the testing jig were inclined 30 degrees and the universal testing machine was used to measure the fracture strength. Results. 1. The fracture strength of the ceramic crown with 3.0mm depth and $12^{\circ}$ inclination was the highest (839N) Crowns of 2.0mm depth and $12^{\circ}$ inclination had the lowest strength (559N). 2. There was no significant difference in the fracture strength by axial inclination in the same incisal reduction group. 3. The fracture mode of the crowns was similar. Most of fracture lines began at the loading area and extended through proximal surface perpendicular to the margin irrespective of incisal reduction.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.16 no.3
• /
• pp.237-245
• /
• 2000

The purpose of this study was to compare the fracture strength of the IPS Empress ceramic crown according to the incisal depth(2.0mm, 2.5mm, 3.0mm) and axial inclination($4^{\circ}$, $8^{\circ}$, $12^{\circ}$) of the upper central incisor. After 10 metal dies were made for each group, the IPS Empress ceramic crowns were fabricated and each crown was cemented on each metal die with resin cement. The cemented crowns mounted on the testing jig were inclined 30 degrees and a universal testing machine was used to measure the fracture strength. The results were : 1. The fracture strength of the ceramic crown with 2.5mm depth and $8^{\circ}$ inclination was the highest(965N). Crowns of 2.0mm depth and $4^{\circ}$ inclination had the lowest strength(713N). There were no significant differences of the fracture strength by axial inclination in same incisal depth group. 2. The fracture mode of the crowns was similar. Most of fracture lines began at the loading area and extended through proximal surface perpendicular to the margin irrespective of incisal depth. There had correlation between fracture strength and fractured surface area.

• Journal of the Korean Ceramic Society
• /
• v.36 no.10
• /
• pp.1123-1131
• /
• 1999

Alumina-glass composites which are considered as the material of the choice for all dental crown was prepared by aqeous-based tape casting and sintering for 2h at 1120$^{\circ}C$ followed by glass infiltration for 2h at 1100$^{\circ}C$ Biaxial strength and fracture toughness of the composites were evaluated to determine the optimum composition of the tape as a function of the amount of constituent such as alumina binder and plasticizer. The strength and the fracture toughness of the alumina tape increased with increasing the contents of alumina and binder. These observations are consistent with in fluence of the constituents on mean alumuna particle distance in tapes suggesting that high strength of the glass infiltrated alumina composites is related to toughening by crack bowing. The biaxial strength and the fracture toughness of the composite containing the optimum constituent composition were 523 MPa and 3.3 MPa$.$1/2 respectively.

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.232-237
• /
• 2004

The tension behavior of Nicalon/CAS glass-ceramic matrix composites was investigated. Infrared (IR) thermography was employed for two different types of $Nicalon^{TM}/CAS$ composites, i.e., cross-ply and unidirectional specimens. During tensile testing, an IR camera was used for in-situ monitoring of progressive damages of $Nicalon^{TM}/CAS$ samples. The IR camera provided the temperature changes during tensile testing. Microstructural characterization using scanning electron microscopy (SEM) was performed to investigate the fracture mechanisms of $Nicalon^{TM}/CAS$ composites. In this investigation, the thermographic NDE technique was used to facilitate a better understanding of the fracture mechanisms of the $Nicalon^{TM}/CAS$ composites during tensile testing.

• Journal of the Korean Ceramic Society
• /
• v.41 no.2
• /
• pp.143-150
• /
• 2004

Biaxial flexure strength (ball-on-3-ball) and fracture toughness (indentation microfracture) of heat-pressable glass-ceramics for dental use were investigated in this study. Crystal phase and microstructure of glass-ceramics were analyzed by XRD. SEM, and TEM. Crack propagation in specimens was not effectively arrested by dispersed crystalline particles. However, higher degree of crystallization probably contributes to strengthening of glass-ceramics. Better clinical reliability can be expected from lithium disilicate glass-ceramic because of its significantly higher biaxial flexure strength and fracture toughness.

• Journal of the Korean Ceramic Society
• /
• v.23 no.6
• /
• pp.59-65
• /
• 1986

Flexural strength fracture toughness and strengthening mechanisms of cordierite ceramics reinforced by SiC whiskers up to 40vol% were investigated. The specimens were hot pressed at Ar atmosphere. The porosity increased with the SiC whisker content. Flexural strength and single edge notch beam fracture toughness were measured up to 1,000$^{\circ}C$. Extrapolating to zero porosity the reinforced composites exhibited in-creasings in flexural strength and fracture toughness with the SiC whisker content. The composites were strengthened mainly by load transfer crack impediment and partially by crack deflection mechanisms. Impurities played an important role in determining the mechanical properties of the composites.

• Korean Journal of Materials Research
• /
• v.9 no.2
• /
• pp.132-138
• /
• 1999

In order to investigate the toughening characteristic by microcrack formation in ceramic composites, $Al_2$O$_3$/(0~20)vol% YAG composites containing equiaxed second grains were fabricated using$ Al_2$$O_3$ during hot-pressing. AE(acoustic emission) measurements have been coupled with fracture toughness experiments of SENB method, to evaluate the microcrack formation and the improvement in fracture toughness of ceramic composites. Formation of microcrack was detected by Ae. The generation of AE events increased with increasing of load when load was applied at specimen. The AE events are generated mainly around at maximum load. Specially, the detected AE evetns of composites are many as compared with monolithic $Al_2$$O_3$. Fracture toughness of composites was improved than that of monolithic alumina. $Al_2$O$_3$/YAG composites exhibit main toughening effects by microcracking, results from mutual coalesence of microcracks being generated under applied load. However, there are few toughening mechanism like microcracking in monolithic alumina.