• Journal of Korean Society for Atmospheric Environment
• /
• v.19 no.3
• /
• pp.297-306
• /
• 2003

Works were focused on back pressure characteristics of ceramic fiber filter on DPF (Diesel Particulate Filter) system and experiments were performed to select appropriate filter which can filter particulates. Filters were installed on metal -support tube which has openings for exhaust gas flow. Ceramic fiber filters with high specific surface area and adequate high temperature strength are commercially available for filtration of diesel particulates and in -situ hot regeneration. Thus, ceramic blanket and ceramic board which are used as insulating media were applied to filter and filtration apparatus was installed on exhaust gas line connected to 2.0 L diesel engine. Alternating filter structure to adapt DPF system, collection efficiency test of diesel particulates was measured. In case of ceramic blanket, pressure drop was low, caused by the destruction of soft structures. Also, particulate collection efficiency was decreased depending on loading time. In case of ceramic board, structure design was altered to reduce back pressure on DPF system. Structure design was altered to induce Z-flow by making 10 mm and 5 mm holes on the surface of media. Alteration of 5 mm hole showed that media have low back pressure but particulate collection efficiency was 77%, while 10 mm hole showed that of 90%.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.32-38
• /
• 2010

Hybrid material(ceramic+metal) processes were developed for micro filter using ceramics coating at metal filter surface by thermal spray method, micro hole drilling at ceramic coated filter surface by femtosecond laser, and fiber laser direct welding of ceramic and metal (SUS304, SM45C) by capillary effect. Thermal spray process was used for ceramic powders and metal filters. The used ceramic powders were $Al_2O_3+40TiO_2$(Metco 131VF) powder of maximum particle size $5{\mu}m$ and ${Al_2O_3}99+$(Metco 54NS) power of maximum particle size 45m. Ceramic coated filters using thermal spray method had a great influence on powder material, particle size and coating thickness but had a fine performance as a micro filter. CW fiber laser was used to drill the top ceramic layer and melt the bottom metal layer for joining applications.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.989-994
• /
• 1995

Rigid porous carbon fiber composites with the uniform pore size distribution were prepared by vacuum forming from water slurries containing carbonized PAN fibers, a phenolic resin and ceramic binders. The composites were designed to use for highly efficient carbon fiber filters for particulate filtration and gas adsorption. As the as-received carbon fibers of 1mm in length were milled to an approximate average length of 300${\mu}{\textrm}{m}$, modulus of rupture (MOR) of the composite filter was increased from 1MPa to the value larger than 5 MPa. Modulus of rupture (MOR) for the composite filter fabricated using the milled carbon fiber was increased from 5 MPa to 10 MPa as the carbonization temperature of the PAN fiber was raised from 90$0^{\circ}C$ to 140$0^{\circ}C$. The air permeability and an average pore size of the composite filter were increased from 40 to 270cc/min.$\textrm{cm}^2$ and from 35 to 80${\mu}{\textrm}{m}$, respectively, as the apparent porosity increased from 80 to 95%. It was shown that the MOR of the carbon fiber composite filter was dependent primarily on the average length of carbon fiber, carbonization temperature and the type of bonding materials.

• Membrane Journal
• /
• v.8 no.4
• /
• pp.191-202
• /
• 1998

The emission standards for diesel particulates have been continued to become tighter. This article reviews the pore and how to filtering characteristics and how to design the ceramic honeycomb filter which is generally used for diesel particulate filter. And the properties and fabrication methods of other particulate filters, i.e. ceramic fiber candle filter, ceramic foam filter, ceramic cross-flow filter and metal filter, are presented in this review. The results show that though the various filters have been developed and tested in the field, the more efforts are needed for the commercilaization of the diesel particulate filter.

• The Korean Journal of Ceramics
• /
• v.5 no.3
• /
• pp.284-287
• /
• 1999

CuO catalyst-coated alumino-silicate fiber filters were prepared for the simultaneous removal of particulate matter and gaseous contaminants such as NOx and SOx. Hot gas cleaning experiments similar to Shell UOP process other than the catalyst supporting materials were carried out between 300 and $500^{\circ}C$ for the evaluation of the gas removal efficiency of the catalytic filter. Experimental results showed that removel efficiency for $SO_2$ was greater than 99% in the temperature range 450~$500^{\circ}C$ and more than 90% of NO was collected between 350 and $370^{\circ}C$. It was found that the higher the CuO content, the higher the removal efficiency for $SO_2$. Removal efficiency for NO was more affected by the gas cleaning temperature than by the CuO content in the catalyst-filter.

• Journal of the Korean Ceramic Society
• /
• v.45 no.8
• /
• pp.464-471
• /
• 2008

The electrolyte separator for thermal battery should be easily handled and loaded a large amount of the molten salt. Ceramic fibers, especially fibrous commercial glass filters were used as an electrolyte separator and the lithium based molten salts were infiltrated into the ceramic filters. The pore structures of the ceramic filter and the melting properties of the lithium salts affected to the electrolyte loading and leakage. During the infiltration, ions of $Li^+$ and $F^-$ in the molten salts were reacted with the glass fiber and caused to be weaken the fiber strength.

• Journal of Korean Society for Atmospheric Environment
• /
• v.20 no.3
• /
• pp.361-369
• /
• 2004

A metal fiber bed has seldom been applied to the practical filtration process despite its excellent mechanical and chemical stability. The filter-bed used in this work was highly porous with open structure, of which apparent porosity was 80 ∼ 90%. Although pressure loss across the filter-bed was very low, separation efficiency was found to be quite high. This paper focuses on the basic filtration mechanisms of a metal filter-bed and a thin ceramic filter from fly ash for reference. The experimental parameters were face velocity, dust loading and porosity of filter-bed. Pressure drop increased with increasing face velocity and dust feeding load for both filters. It also showed that dust particles deposited in the deep flow path, finally resulting in clogging the pore channels. It thereby indicates that the dominating mechanism of the metal filter-bed would be depth filtration. Meanwhile, the thin fly ash composite filters trapped the aerated dust mainly on the surface of the filter medium, so that the instantaneously formed dust layer might cause a steep increase of pressure drop across the filtration system.

• Journal of the Korean Ceramic Society
• /
• v.46 no.6
• /
• pp.648-652
• /
• 2009

Ceramic fiber separator is the promising material for thermal battery system because it reduces the production cost and offers the potential to a new application compared to a pellet type electrolyte. The electrolyte separator for thermal battery should be easily handled and loaded a large amount of the molten lithium salt. Ceramic fibers were used as an electrolyte separator and the lithium based molten salts were infiltrated into the ceramic filters. Leakage of molten salt (several lithium salts) leads to short-circuit during the thermal battery operation. In this study, a uniform and fine SiOC mat with fibers ranging from 1 to 3 ${\mu}m$ was obtained by electrospinning of polycarbosilane and pyrolysis. The optimum spinning conditions for obtaining fine diameters of SiOC fiber were controlled by the solution composition and concentration, applied voltage and spinning rate, release rate by porosity. The pore structures of the ceramic filter and the melting properties of the lithium salts affected to the electrolyte loading and leakage. The importance of the fiber size and porosity and their control was discussed and the mechanical properties were also discussed.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.04a
• /
• pp.129.1-129
• /
• 2003

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.1
• /
• pp.28-33
• /
• 2017

SiC fiber can be used up to $1800^{\circ}C$ in both inert and air atmosphere without any problems such as melting and oxidation. SiC fibers can be applied to dust filtering processes as a bag filter at a high temperature above $700^{\circ}C$, which is far beyond the temperature range of currently available industrial bag filter. However the studies for the degradation of SiC fibers were still lacked in the harsh environment of steel industries and thermoelectric power plants. In this study, SiC fibers were reacted with steel dust and thermal power plant dust at a high temperature of $500^{\circ}C$ or higher, and the degraded shape of the fiber surface was observed by SEM. Also the degree of oxygen diffusion on the surface and inside of SiC fiber was analyzed by EDS.