• Journal of the Korean Society for Precision Engineering
• /
• v.14 no.9
• /
• pp.30-36
• /
• 1997

In this study, the development of an aluminum forged piston was tried to substitute the cast piston, in which there were internal defects such as blow hole and shrink pipe. A gasoline engine piston was chosen as an example for developing the forged piston. Before aluminum forging, model, material (plasticine) test was carried out to investigate the forgeability and internal flow pattern of the forged piston at room temperature. From the result of model material test, an aluminum piston to be forged was redesigned. The aluminum pistion was forged in hot process. The quality of a forged piston was compared with that of a cast piston in the point of mechanical properties, internal defect and microstructure. It was proved that the forged piston was superior to the cast piston.

• Transactions of Materials Processing
• /
• v.16 no.4 s.94
• /
• pp.293-298
• /
• 2007

Recently, there is a need to produce a large forged part for the flight, shipping, some energies, and military industries, etc. Therefore, an open die forging technique of cast ingots is required to obtain higher quality of large size forged parts. Cogging process is one of the primary stages in many open die forging processes. In the cogging process prior to some open die forging processes, internal cavities have to be eliminated for defect-free. The present work is concerned with the elimination of the internal cavities in large ingots so as to obtain sound products. In this study, hot compression tests were carried out to obtain the flow stress of cast microstructure at different temperature and strain rates. The FEM analysis is performed to investigate the overlap defect of cast ingots during cogging stage. The measured flow stress data were used to simulate the cogging process of cast ingot using the practical material properties. Also the analysis of cavity closure is performed by using the $DEFORM^{TM}-3D$. The calculated results of cavity closure behavior are compared with the measured results before and after cogging, which are scanned by the X-ray scanner. From this result, the criteria for deformation amounts effect on the cavity closure can be investigated by the comparison between practical experiment and numerical analysis.

• Transactions of Materials Processing
• /
• v.18 no.6
• /
• pp.458-464
• /
• 2009

Thermal energy control is a important factor to control properties of large sized product in ingot-forging. Good control of thermal energy helps to increase characteristics and eliminate defects of large cast-forged part, such as large sized forged shell. We have studied about not only large size ring forging process and after heat treatment process by FEM simulation. Changes of temperature and microstructure for forged shell were predicted according to different heat treatment conditions. Therefore, we can choose the proper heat treatment condition by FEA. The sectional properties confirmed by practical experiment and evaluation have presented possibilities of process design by computational analysis.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1995.10a
• /
• pp.113-116
• /
• 1995

In this experimental study,aluminum hotforging was conduct to get superior pistion to cast piston. Cast structure of billet is destroyed, harmful defects is removed by forging process. We proposed the direction od die design by observing formability of product according to die shape. The microstructure of forged products with different preform was investigated to determine inital billet shape. We proposed appropriate heat treatment condition for improvement of mechanical properties.

• Journal of Korea Foundry Society
• /
• v.33 no.5
• /
• pp.210-214
• /
• 2013

Recently, the automotive industry has replaced cast iron to lightweight materials like aluminum for engine efficiency of automobiles and an emission control by government. In this paper we studied two auto parts manufacturing methods using an alloy of A356. That is gravity casting and H-NCM Rheo-diecasting forging. We analyzed the microstructure and mechanical properties for this method. In Microstructure analysis results, H-NCM Rheo-diecasting forging has more finer microstrucre and better forging effect. Resulting in better mechanical properties than gravity forging.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.102-106
• /
• 2009

Thermal energy control is a important factor in a large size casting and forging. Good control of thermal energy makes characteristics and defect of large cast-forged part, such as large sized forged shell. We have studied about not only large size ring forging process and after heat treatment by FEM simulation. Also, changes of temperature and microstructure for forged shell were predicted. Therefore, we can choose the proper heat treatment condition by FEA. The sectional properties confirmed by practical experiment and evaluation have presented possibilities of process design by computational analysis.

• Journal of Power System Engineering
• /
• v.17 no.6
• /
• pp.115-121
• /
• 2013

This study was carried out to investigate the effect of hot forging on the hardness and impact value of ultra high carbon low alloy steel. With increasing hot forging ratio, thickness of the network and acicular proeutectoid cementite decreased, and than were broken up into particle shapes, when the forging ratio was 80%, the network and acicular shape of the as-cast state disappeared. Interlamellar spacing and the thickness of eutectoid cementite decreased with increasing forging ratio, and were broken up into particle shapes, which then became spheroidized. With increasing hot forging ratio, hardness, tensile strength, elongation and impact value were not changed up 50%, and then hardness rapidly decreased, while impact value rapidly increased. Hardness and impact value was greatly affected by the disappeared of network and acicular shape of proeutectoid cementite, and became particle shape than thickness reduction of proeutectoid and eutectoid cementite.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1997.10a
• /
• pp.138-141
• /
• 1997

CFM(Cast Forge Method) is widely used in manufacturing industry to produce aluminium parts with good mechanical properties and low production cost. CFM is the process which produces a final products by forging from the initial billet by casting. The study on this paper covers the automatic design method which finds a pertinent shape for initial billet using Fast Fourier Transform, low-pass frequency filtering and FEM simulation of the nonisothermal forging process by DEFORM. These works will give us an information to enhance the low strength of a aluminium casting.

• Korean Journal of Materials Research
• /
• v.13 no.12
• /
• pp.812-818
• /
• 2003

The aim of this study is to investigate the fabrication processes on the microstructual changes and mechanical properties of large 7175 aluminum die forgings. The billets range from 370 to 720 mm in diameter were homogenized and hot forged after direct chill casting. The strength and elongation of the homogenized cast billets were revealed nearly same level independent of the billet diameter. However, these properties of ø370 mm cast billet were superior to those of $\Pie720$ mm billet under$ T_{6}$ / condition. The tensile strength of die forged specimens under $T_{6}$ condition increased up to 20% than that of solution treatment, however, the elongation was reduced to 50%. The fracture toughness of die forged specimens under $T_{6}$ condition was 35.6∼39.0 MPa$.$$m^{1}$2 irrespective of the billet size and free forging processes, but this property increased up to 10% by$V_{74}$ treatment. The fracture toughness of die forged specimen manufactured with ø370 mm cast billet showed nearly same level of ø720 mm billet which was processed using MF or Cog free forging followed by die forging.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.05a
• /
• pp.160-164
• /
• 2007

In the steel industry, there is a need to produce large forged parts for the automobile industries, the flight and shipping industries ad military industries. In the steel-industry application, a cogging technique for cast ingots is required, because the major parts are needed as one large body in order to obtain higher quality. Therefore, cogging process is the primary step in manufacturing of practically large open-die forging. In the cogging process, internal voids have to be eliminated as defects, The present work is concerned with the elimination of the internal voids in large ingots so as obtain sound products. In this study, hot compression tests were carried out to obtain the flow stress of cast microstructure at different temperature and strain rates. The FEM analysis are performed to investigate the overlap defect of cast ingots during cogging stage. The measure flow stress data were used to simulate the cogging process of cast ingot using the practical material properties. Also the analysis of void closure are performed by using the $DEFORM^{TM}$-3D. The calculated results of void closure behavior are compared with the measured results before and after cogging, which are scanned by the X-ray scanner. From this result, the criteria for deformation amounts effect on the void closure can be investigated by the comparison of practical experiment and numerical analysis.