• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2008년도 추계학술대회 논문집
• /
• pp.354-357
• /
• 2008

In this study, the casting process using forged insert was applied to manufacturing a knuckle, in order to prove that application of casting process using forged insert is likely to get the effect of light weight and superior mechanical characteristic compared with existing casting products. Firstly, in the forging experiment, it was confirmed that the optimal configuration of the forged insert could be predicted by FE analysis. And by using FVM (Finite Volume Method) software, it was verified that a proposed casting design was available. To identify the mechanical characteristic of the final casting product, the microstructual observation and hardness test were performed at the boundary zone between forging and casting part.

• 한국기계가공학회지
• /
• 제3권1호
• /
• pp.66-71
• /
• 2004

Magnesium alloys have been widely used for many structural components of automobiles and aircraft because of high specific strength and good cast-ability in spite of hexagonal closed-packed crystal structure of pure magnesium. In this study, it is studied about the forming characteristics of press forging of AZ31 magnesium alloy by MSC/MARC in case of material having one boss and MSC/Supeiforge in case of material having multi-boss with heat transfer analysis during deformation at elevated temperature. For these results it is simulated about temperature distribution, strain distribution, and stress distribution of AZ31 Magnesium alloy. During the press forging, foot regions of bosses showed greater temperature rise than other areas of AZ31 sheet. Finally the plastic strain of AZ31 sheet did not remarkably vary with increasing temperature from 373 to 473K, while it significantly increased as the forming temperature increased from 473 to 573K, which is related with the change in micro-structures, such as dynamic re-crystallization occurring during the deformation process.

• 한국재료학회지
• /
• 제14권3호
• /
• pp.168-174
• /
• 2004

The aim of this study is to investigate the effect of process conditions on the microstructual changes and mechanical properties of large 7175 aluminum die forgings. The cast billets of 370 and 720 mm in diameter were homogenized and die forged after direct chill casting. The size and volume fraction of second phase particles in 720 mm billet were larger than those of 370 mm billet. The interdendritic sites containing the second phase particles was considered to be a crack initiation region in the process of cold upsetting. The tensile and yield strength of die forged specimens of 720 mm billet in the direction of Land L T were higher than those of 370 mm billet. However, the tensile strength of these specimens were 5 to 10% lower than that of American military specification. The plane strain fracture toughness of die forged specimens of 370 mm cast billet showed almost the same level of 720 mm billet, which was die forged after free forging.

• 한국주조공학회지
• /
• 제27권5호
• /
• pp.212-216
• /
• 2007

과공정 Al-15wt.%Si 합금의 주단조 공정의 적용을 위해 주조 예비성형체를 제작하는 과정에서 P와 Sr을 첨가하여 과공정 Al-Si 합금의 응고과정에서 발생하는 초정 Si과 공정 Si의 미세화 개량처리를 행하였다. 미세화 조직의 변화에 따른 기계적성질 및 단조성을 조사하였으며, 미세화제로 첨가된 0.075wt.% Sr과 0.1wt.% P의 첨가에서 가장 효과적인 미세한 조직을 얻을 수 있었고, 인장강도와 연신율은 이들 첨가원가의 증가에 따라 향상되는 결과를 보였으나 일정 이상의 첨가에서는 더 이상의 향상은 없었다. 단조성 평가를 위한 열간가공 재현실험에서는 $450^{\circ}C$에서 약60N/mm2의 하중이 필요함을 알 수 있었다. 열간단조 및 열처리 후의 인장강도와 연신율은 보다 많은 향상을 가져왔으며, 이는 압축가공에 의한 주조 예비성형체 내부에 잔존하던 주조결함의 제어와 열처리에 의한 조직의 개량 및 균질화 효과에 의한 것으로 판단된다.

• 소성∙가공
• /
• 제19권6호
• /
• pp.378-386
• /
• 2010

Nowadays there has been great interest in using heat treated cast material for press dies due to several advantages like reduction in die production costs. However, in hot press forming processes H13 forged tool steel is mostly used. Cooling performance of dies in hot press forming processes is considered as an important factor of study and also the IHTC parameter between cast material die and sheet metal should be considered as an essential. In the present study, the IHTC was calculated for the sheet metal in the hot press forming process with cast and forged material dies. The temperature measurements were performed for the sheet metal, casting and forged material dies by applying various contact pressure in hot press forming. IHTC was calculated and studied by adopting the inverse heat convection method in DEFORM-2D. Each IHTC was considered as a function of contact time and contact pressure. The experimental data were compared with calculated data obtained from the proposed equation and references.

• 보존과학연구
• /
• 통권23호
• /
• pp.131-147
• /
• 2002

Kkonmoe relic located in Jangan-gu, Suwon-si, Gyeonggi-do Provinceis an example of the wide chronology from the Three Kingdoms Period to Joseon Dynasty. Examinations on a forged iron ax, a cast iron ax and an iron sickle excavated from this relic revealed the microstructure structure of the metal and the manufacturing technologies. Microstructure investigation was carried out with a metallurgical microscope and a Vickers hardness tester was used to measure the hardness of the micro structures. The test results show that the forged iron ax has a ferrite and pearlitestructure. It is made of low carbon steel and then carbonized to increase carbon content. After carbonization, the surface grains are reworked and the surface decarbonized. In case of the iron sickle, it is forged from low carbon steel, then carbonized and hardened, to increase overall strength. The sickle blade is carbonized and quenched after forging, resulting in afirm, solid blade. Heat treatment to remove brittleness is not applied to the cast ironartifact, which is manufactured by solidifing hypo-eutectic cast iron with a3-4% carbon content and white cast iron. All artifacts are produced from steel and subjected to a carbonization process. To increase hardness of the blade, additional heat treatment is applied.

• 소성∙가공
• /
• 제28권2호
• /
• pp.63-70
• /
• 2019

This study investigates the effects of multi-axial diagonal forging (MADF) processing number on the microstructures of AA1100 fabricated using MADF processes. The cast AA1100 was annealed at $400^{\circ}C$ for 3hrs in $N_2$ atmosphere and cut into $25mm^3$ cubes for the MADF processes. The MADF process consist of plane forging with a thickness reduction of 30% and a diagonal forging with a diagonal forging angle of 135 degrees. In order to analyze the microstructural variations based on the number of repetitions, 1, 2, 3 and 4 cycles of the MADF process were performed. AA1100 specimens were successfully deformed without cracking of the surface for up to 4 cycles of MADF. The grain size, average misorientation and average grain orientation spread (GOS) of MADF processed materials were analyzed using EBSD technique. The results showed that MADF process effectively refined the microstructure of AA1100 with an initial average grain size of $337.4{\mu}m$. The average grain sizes of specimens which were MADF processed for 2, 3, 4 cycles were refined to be $1.9{\mu}m$, $1.6{\mu}m$, $1.4{\mu}m$, respectively. The grain refinement appeared saturated when AA1100 got MADF processed over 2 cycles. When the specimen was subjected to two or more cycles of MADF, the degree of decrease in the average grain size drastically decreased with an increase in the number of cycle due to the softening phenomena such as dynamic recovery or dynamic recrystallization during processing.

• 열처리공학회지
• /
• 제17권1호
• /
• pp.10-16
• /
• 2004

The aim of this study is to investigate the process conditions on the microstructual changes and mechanical properties of large 7175 aluminum ring roll forgings. The billets range from 370 mm to 720 mm in diameter were homogenized and ring roll forged after direct chill casting. The tensile properties of ring roll forged specimen manufactured with ${\Phi}370mm$ billets were superior to those of ${\Phi}720mm$ billets under $T_6$ condition. Also, these properties showed better than those of military specification under $T_{74}$ treatment. The impact value of ring roll forged specimen under $T_{74}$ treatment increased up to 20% than that of $T_6$ condition. The fracture toughness of ring roll forged specimen manufactured with ${\Phi}370mm$ cast billet showed nearly same level of ${\Phi}720mm$ billet which was processed using MF or Cog free forging followed by ring roll forging.

• 한국분말재료학회지
• /
• 제5권4호
• /
• pp.340-344
• /
• 1998

Along with the growth of conventional ferrous powder metallurgy (PM), PM of aluminum alloys has been intensively investigated in Japan. Although rapidly solidified aluminum alloy powder was first used in the USA,/sup 1)/ commercialization for consumer market was first realized in Japan./sup 2)/ In order to achieve the viable cost-performance including Near Net Shape (NNS) formability, we developed three processes, powder extrusion, powder forging and sintering. The new powder extrusion process does not use either capsulation or vacuum degassing. The new powder forging does not need lateral flow. The new sintering process does not use liquid phase. The performance achieved by the processes is outstanding mechanical or physical properties that has potential to substitute cast iron, steel, titanium Metal Matrix Composite (MMC) or Ingot Metallurgy (IM) aluminum alloys. Cooperation with customers, powder suppliers and research associations contributed to the advancement of PM aluminum alloys in Japan.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2005년도 추계학술대회 논문집
• /
• pp.350-353
• /
• 2005

Microstructures according to experimental conditions (pouring temperature, stirring current and stirring time) and hardness according to aging time were investigated for A356 cast aluminum alloy and 7075 wrought aluminum alloy. In pouring temperature control, grains became larger and non-uniform at high temperature, however dendritic shapes were shown at lower temperature. In stirring current control, dendritic grains were not destroyed enough at lower current, however fine grains were agglomerated at higher current. And, in stirring time control, grains were more globular but grew larger and larger with the stirring time increasing.