• Korean Journal of Materials Research
• /
• v.13 no.11
• /
• pp.732-736
• /
• 2003

A CP-GFRP(Carbon Powder-Glass Fiber Reinforced Plastic) sensor was fabricated for fracture detection. The electric resistance of the sensor was measured on condition of various composition of carbon powders and thickness of bundle of glass fibers. The resistance of the sensor was decreased as the increase of the content of carbon powders and the TEX of the glass fibers. In the case of loading on CP-GFRP, because inner crack was propagated, the part of percolation structures was disconnected. These observations show the following results. The conduction of CP-GFRP sensor is due to percolation structure of carbon powders and increase of resistance is due to expansion of cracks.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.04a
• /
• pp.119-122
• /
• 2004

A CPGFRP(Carbon Powder Glass Fiber Reinforced Plastics) sensor was fabricated for fine crack detection of structures. The electrical resistance of the sensor was measured on condition of various composition of carbon powders and thickness of bundle of glass fibers. The resistance was decreased as the increase of the content of carbon powders and the TEX of the glass fibers. In the case of loading on CPGFRP sensor, because inner crack was propagated, the part of percolation structures was disconnected. The sensor is superior to carbon fiber for the detecting ability of fine crack.

• Macromolecular Research
• /
• v.12 no.4
• /
• pp.399-406
• /
• 2004

Glass-like carbon precursors shrink significantly during curing and carbonization, which leads to crack formation and bending. Cured furan resin powder and ethanol were added to furan resin to diminish the weight loss, to suppress the shrinkage and bending, and to readily release the gases evolved during polymerization and curing. Curing and carbonization were controlled by pressure and slow heating to avoid damage to the samples. The effect of the filler and ethanol on the fabrication process was examined by measuring the properties of the glass-like carbon, such as the specific gravity, bending strength, electrical resistivity, and microstructural change. The specific gravities of the filler-added glass-like carbons were higher than those of the ethanol-added samples because of the formation of macropores from the vaporization of ethanol during the curing and polymerization processes. Although the ethanol-added glass-like carbons exhibited lower bending strengths after carbonization than did the filler-added samples, the opposite result was observed after aging at 2,600$^{\circ}C$. We found that the macropores created from ethanol were contracted and removed upon heat treatment. The electrical resistivity of the glass-like carbon aged at 2,600$^{\circ}C$ was lower than those of the samples carbonized at 1,000$^{\circ}C$. We attribute this phenomenon to the fact that aging at high temperature led to well-developed microstructures, the removal of macropores, and the reduction of the surface area.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2002.05a
• /
• pp.47-50
• /
• 2002

This paper presents the results of fire resistance properties of high performance concrete varying with fiber kinds and the size of metal lath in order to verify the validities of fiber on the spatting resistance by fire. Metal lath, glass fiber and carbon fiber are used to confine the concrete. According to test results, plain concrete without lateral confinement and confined concrete with glass fiber and carbon fiber show entire failure after exposed to fire, while confined concrete with metal lath take place in the form of slight surface spatting by fire, which has favorable spatting resistance of concrete. As for the effect of the size of metal lath, when the size of metal lath is more than 1.2mm of thickness, the residual strength of concrete exposed to fire maintains more than 80% of its original strength. However, glass fiber and carbon fiber does not perform desirable spatting resistance by fire due to loss of lateral confinement of fiber exposed to fire caused by melting of fiber and reducing bond strength between concrete and fiber.

• Journal of the Korean Wood Science and Technology
• /
• v.50 no.6
• /
• pp.427-435
• /
• 2022

For effective applicability of reinforced cork, cork composites reinforced with metal, glass fiber, and carbon fiber were developed, and the effects of the reinforcing materials on the mechanical properties of cork composites were investigated. The bending moduli of elasticity (MOE) of cork composites were in the 32.7-35.9 MPa range, while the bending strength values were in the 1.62-1.73 MPa range. The strength performance decreased in the order cork-metal > cork-carbon fiber > cork-glass fiber. The bending MOEs were improved by 29%-41% compared with simple cork boards, while the bending strengths of reinforced cork were 35%-45% higher. The strength performance significantly improved following the incorporation of thin mesh materials into the middle layer of the studied cork composites. The bending strains of the cork composites were remarkably higher compared with oak wood, making them promising for applications that require bending processing, such as curved jointing. The internal bond strengths of the cork composites were 0.26-0.44 MPa, approximately 0.36-0.60 times lower compared with medium-density fiber boards.

• Journal of the Korea Concrete Institute
• /
• v.18 no.2 s.92
• /
• pp.275-282
• /
• 2006

Recently, Fiber Reinforced Polymers(FRP) has been emerged as an alternative material to solve the corrosion of steel reinforcement in reinforced concrete structures. FRP exhibits higher specific strength and lower weight compared to steel reinforcement. Moreover, good resistance to corrosion of the FRP may be useful in aggressive environments causing deterioration such as chloride environment. However, causes for higher initial cost of FRP than that of steel, little information on the long-term behavior of FRP, and brittle failure make the efforts to apply FRP in civil structures slow. Glass fiber among the fibers used to manufacture FRP can be seen as the most beneficial material with regard to initial costs. But its low elastic modulus, which attains barely a quarter of steel, nay thus lead to excessive deflections when used as reinforcement for flexural members. This research was carried out on the tensile properties of hybrid rods made with glass and carbon fibers to improve those of FRP rod made with glass fiber. Parameters were resin type and the arrangement of glass and carbon fibers. The tensile properties of hybrid rods were compared with those of rods manufactured with only glass or carbon fibers. The results indicated that the tensile properties of hybrid rod were good when the carbon fiber was arranged in the core.

• Composites Research
• /
• v.24 no.6
• /
• pp.25-30
• /
• 2011

This paper presents an experimental study on the enhancement of electromagnetic shielding (EMI) properties of glass fiber, carbon fiber, and glass-carbon fiber composites by adding layers of multi-walled carbon nanotubes (MWCNTs). In the case of glass-fiber composites, spraying 0.1~0.2 g of MWCNT over a fiber area of $200mm{\times}200mm$ (1.8~3.6 ${\mu}m$ in thickness) resulted in significant improvement in EMI shielding effectiveness (SE). Also, when applying multiple MWCNT layers, it was more effective to place the layers concentrated near the center of the composite rather than spreading them out. On the contrary, inherently conductive carbon fiber and glass-carbon fiber composites did not show appreciable improvement with the addition of MWCNT layers. In order to maximize the effectiveness of carbon nanomaterials as EMI shielding fillers, it is imperative to understand the effect of these materials on various EMI shielding mechanisms and their interactions.

• Carbon letters
• /
• v.10 no.3
• /
• pp.230-233
• /
• 2009

In this study, a low temperature growth of high-quality carbon nanotubes on glass substrate using a local surface heating without heating damage to substrate was tried and characterized. The local joule heating was induced to only Ni/Ti metal film on glass substrate by applying voltage to the film. It was estimated that local surface joule heating method could heat the metal surface locally up to around $1200^{\circ}C$ by voltage control. We could successfully obtain high-quality carbon nanotubes grown at $300^{\circ}C$ by applying 125 V for joule heating as same as carbon nanotubes grown at $900^{\circ}C$.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.11 no.3
• /
• pp.19-23
• /
• 2012

Glassy carbon is widely used for high temperature melting process such as quartz due to its thermal stability. For utilizing Classy Carbon to glass mold press(GMP) optical lens, brittleness of Glassy Carbon is main obstacle of ultraprecision machining. Thus authors investigated ductile machining of Glassy Carbon adopting turning and grinding process respectively. From the experiments, ultraprecision turning surfaces resulted brittle crack in all machining conditions and ultraprecision grinding surfaces showed semi-ductile mode in small undeformed chip thickness conditions.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.22 no.4
• /
• pp.190-193
• /
• 2012

Transparent diamond-like carbon (DLC) films were synthesized on glass using radio frequency plasma enhanced chemical vapor deposition method from the gas mixture of $CH_4$, $SiH_4$ and Ar. The pressure, the rf-power, $CH_4/SiH_4/Ar$ ratio, and the deposition time were 0.1Torr, 100W, 20 : 1 : 1, and 20 min, respectively. The optical transmittances of DLC-deposited glass and uncoated glass were compared with each other in the visible light regions. The DLC-deposited glass showed transmittance of approximately 83 % and 95 % as compared to the uncoated glass for the wavelength of 380 nm and 500 nm, respectively. The hardness and roughness of DLC-coated glass have been measured by nanoindentation and AFM, respectively. The DLC-coated glass showed a little less or similar optical transmittance compared to the uncoated glass, while the hardness of DLC-coated glass was 2.5 times higher than that of the uncoated glass. The deposited DLC film had the very smooth surface and was thicker than 150 nm after deposition for 20 min.