• Composites Research
• /
• v.26 no.5
• /
• pp.289-294
• /
• 2013

A thinner is used to improve the multi-walled carbon nano-tube (CNT) and carbon black (CB) dispersion in a polymer matrix and to make a soft electrode. The electrical and mechanical properties of the soft electrodes are investigated as functions of CNT, CB and thinner content. The optimal mixing condition for the electrode is thinner 80, CNT 3.5, CB 18 (phr) on the basis of matrix (KE-12). The specific resistance of that is 73 (${\Omega}{\cdot}cm$), and tensile strength, tensile modulus, and elongation of that is 0.45 MPa, 0.21 MPa, and 184%, respectively. Also, a simple structure of the actuator with an optimized electrode and elastomer is fabricated and its characteristic is evaluated. At the operating voltage 25 kV, the displacement of an elastomer KE-12 is 2.24 mm, and that of an elastomer KE-12 with thinner 50 (phr) is 4.05 mm. It shows a higher displacement compared to that of 3M 4910 which has similar modulus. The actuator made with elastomer and electrode of the same material (KE-12) may have advantages for fatigue life and application.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2003.10a
• /
• pp.42-45
• /
• 2003

Nondestructive damage sensing and mechanical properties for acid-treated carbon nanotube (CNT) and nanofiber (CNF)/epoxy composites were investigated using electro-micromechanical technique and acoustic emission (AE). Carbon black (CB) was used to compare to CNT and CNF. The results were compared to the untreated case. The fracture of carbon fiber was detected by nondestructive acoustic emission (AE) relating to electrical resistivity under double-matrix composites test. Sensing for fiber tension was performed by electro-pullout test under uniform cyclic strain. The sensitivity for fiber damage such as fiber fracture and fiber tension was the highest for CNT/epoxy composites. Reinforcing effect of CNT obtained from apparent modulus measurement was the highest in the same content. For surface treatment case, the damage sensitivity and reinforcing effect were higher than those of the untreated case. The results obtained from sensing fiber damage were correlated with the morphological observation of nano-scale structure using FE-SEM. The information on fiber damage and matrix deformation and reinforcing effect of carbon nanocomposites could be obtained from electrical resistivity measurement as a new concept of nondestructive evaluation.

• Toxicological Research
• /
• v.30 no.2
• /
• pp.65-70
• /
• 2014

Recent episodes of severe air pollution in eastern Asia have been reported in the scientific literature and news media. Therefore, there is growing concern about the systemic effects of air pollution on human health. Along with the other well-known harmful effects of air pollution, recently, several animal models have provided strong evidence that air pollutants can induce liver toxicity and act to accelerate liver inflammation and steatosis. This review briefly describes examples where exposure to air pollutants was involved in liver toxicity, focusing on how particulate matter (PM) or carbon black (CB) may be translocated from lung to liver and what liver diseases are closely associated with these air pollutants.

• Elastomers and Composites
• /
• v.38 no.3
• /
• pp.235-242
• /
• 2003

A vulcanization reaction characteristics of an isoprene rubber (IR)-modified natural rubber/carbon black (NR/CB) composite was studied using in-situ electrical property measuring technique. Since the electrical conductivity of the sample composite would be changed continuously during the vulcanization reaction by rearranging of the carbon black particles within the sample, volume resistivity (${\rho}$) might be obtained as a function or reaction time. A stabilization time ($t_i$), maximum reaction speed time ($t_p$), and volume resistivity at that time(${\rho}_p$) were defined from the data for the Arrhenius analysis. Volume resistivity ${\rho}$ showed a comparatively high value of ${\sim}10^8$ order before the reaction started, and dramatically decreased to be stabilized within $1{\sim}2$ minutes as soon as the reaction started. As the more time elapsed, thereafter, ${\rho}$ decreased monotonously to a certain constant value through a peak, ${\rho}_p$ at time $t_p$, which was considered as the maximum reaction rate. As a result, while $t_i$ values were comparatively constant as $1{\sim}2$ minutes, $t_p$ values showed to become shorter and shorter as the reaction temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.215-216
• /
• 2007

Semiconducting layers are thin rubber film between electrical cable wire and insulating polymer layers having a volume resistivity of ${\sim}10^2{\Omega}cm$. A new semiconducting material was suggested in this study based on the carbon nanotube(CNT)-reinforced polymer nanocomposites. CNT-reinforced polymer nanocomposites were prepared by solution mixing with various polymer type and dual filler system. The mechanical, thermal and electrical properties were investigated as a function of polymer type and dual filler system based on CNT and carbon black. The volume resistivity of composites was strongly related with the crystallinity of polymer matrix. With decreased crystallinity, the volume resistivity decreased linearly until a critical point, and it remained constant with further decreasing the crystallinity. Dual filler system also affected the volume resistivity. The CNT-reinforced nanocomposite showed the lowest volume resistivity. When a small amount of carbon black(CB) was replaced the CNT, the crystallinity increased considerably leading to a higher volume resistivity.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.10a
• /
• pp.15-18
• /
• 2004

Nondestructive damage sensing and mechanical properties for thermal treated carbon nanotube(CNT) and nanofiber(CNF)/epoxy composites were investigated using electro-micromechanical technique. Carbon black (CB) was used only for the comparison. Electro-micromechanical techniques were applied to obtain the fiber damage and stress transferring effect of carbon nanocomposites with their contents. Thermal treatment and temperature affected on apparent modulus and electrical properties on nanocomposites due to enhanced inherent properties of each CNMs. Coefficient of variation (COV) of volumetric electrical resistance can be used to obtain the dispersion degree indirectly for various CNMs. Dispersion and surface modification are very important parameters to obtain improved mechanical and electrical properties of CNMs for multifunctional applications. Further optimized functionalization and dispersion conditions will be investigated for the following work continuously.

• Bulletin of the Korean Chemical Society
• /
• v.34 no.8
• /
• pp.2343-2347
• /
• 2013

In this work, manganese dioxide ($Mn_3O_4$)/carbon black (CB) composites (Mn-CBs) were prepared by an in situ coating method as electrical fillers and the effect of the Mn-CBs on the electrical performance of activated carbon (AC)-based electrodes was investigated. Structural features of Mn-CBs produced via in situ coating using a $KMnO_4$ solution were confirmed by XRD and TEM images. The electrical performances, including cv curves, charge-discharge behaviors, and specific capacitance of the ACs/Mn-CBs, were determined by cyclic voltammograms. It was found that the composites of $Mn_3O_4$ and CBs were successfully formed by in situ coating method. ACs/Mn-CBs showed higher electrical performance than that of AC electrodes fabricated with conventional CBs due to the pesudocapacitance reaction of manganese oxides in the aqueous electrolyte. Consequently, it is anticipated that the incorporation of $Mn_3O_4$ into CBs could facilitate the utilization of CBs as electrical filler, leading to enhanced electrochemical performance of AC electrodes for supercapacitors.

• Korean Chemical Engineering Research
• /
• v.57 no.4
• /
• pp.525-530
• /
• 2019

The performance and stability of solid oxide fuel cells (SOFCs) depend on the microstructure of the electrode and electrolyte. In anode, porosity and pore distribution affect the active site and fuel gas transfer. In an electrolyte, density and thickness determine the ohmic resistance. To optimizing these conditions, using costly method cannot be a suitable research plan for aiming at commercialization. To solve these drawbacks, we made high performance unit cells with low cost and highly efficient ceramic processes. We selected the NiO-YSZ cermet that is a commercial anode material and used facile methods like die pressing and dip coating process. The porosity of anode was controlled by the amount of carbon black (CB) pore former from 10 wt% to 20 wt% and final sintering temperature from $1350^{\circ}C$ to $1450^{\circ}C$. To achieve a dense thin film electrolyte, the thickness and microstructure of electrolyte were controlled by changing the YSZ loading (vol%) of the slurry from 1 vol% to 5 vol. From results, we achieved the 40% porosity that is well known as an optimum value in Ni-YSZ anode, by adding 15wt% of CB and sintering at $1350^{\circ}C$. YSZ electrolyte thickness was controllable from $2{\mu}m$ to $28{\mu}m$ and dense microstructure is formed at 3vol% of YSZ loading via dip coating process. Finally, a unit cell composed of Ni-YSZ anode with 40% porosity, YSZ electrolyte with a $22{\mu}m$ thickness and LSM-YSZ cathode had a maximum power density of $1.426Wcm^{-2}$ at $800^{\circ}C$.

• Transactions of the Korean hydrogen and new energy society
• /
• v.27 no.3
• /
• pp.276-282
• /
• 2016

The effects of conductive additives in a $La_{0.8}Sr_{0.2}MnO_3$ perovskite bifunctional electrode for oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) were investigated in an alkaline solution. Highly porous carbon black (CB) and Ni powder were added to the bifunctional electrodes as conductive additives. The surface morphologies of electrodes containing CB and Ni were observed by scanning electron microscopy (SEM). The current densities for both ORR and OER were changed by the addition of CB. The conductive additive changed physical properties of bifunctional electrodes such as the sheet conductance, gas permeability and contact angle. It was observed that the air permeability of electrode was most effective to enhance the currents for ORR and OER.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.4
• /
• pp.1361-1366
• /
• 2010

This research aims to develop polymer composites which can be used for PEMFC separators by injection molding process. Considering the moldability and stiffness, we used PPS(Poly(phenylene sulfide)) and PP(Polypropylene) as base resin. In order to improve electrical conductivity and physical properties, we chose glass fiber, carbon fiber, carbon black, and both expanded graphite and synthetic graphite. The 3 type composites are prepared for injection molding of PEMFC separators. and CAE(Computer Aided Engineering) analysis was conducted to optimize injection processing parameters(injection pressure, heat time, mold temperature etc.). We did successfully fabricate the separators by injection molding, and measure the electrical conductivity of the samples by using four point probe device. Conclusively, PP/SG/CB composite showed better both electrical conductivity and moldability than the others.