• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.1
• /
• pp.8-17
• /
• 2003

Fracture behaviors of pipes with local wall thinning are very important for the integrity of nuclear Power Plant. In Pipes of energy Plants, sometimes, the local wall thinning may result from severe erosion-corrosion (E/C) damage. However, the effects of local wall thinning on strength and fracture behaviors of piping system were not well studied. In this paper, the monotonic bending tests were performed of full-scale carbon steel pipes with local wall thinning. A monotonic bending load was applied to straight pipe specimens by four-point loading at ambient temperature without internal pressure. From the tests, fracture behaviors and fracture strength of locally thinned pipe were manifested systematically. The observed failure modes were divided into four types; ovalization. crack initiation/growth after ovalization, local buckling and crack initiation/growth after local buckling. Also, the strength and the allowable limit of piping system with local wall thinning were evaluated.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.25 no.1
• /
• pp.68-74
• /
• 2016

The Nd:YAG laser welding process is one of the most advanced manufacturing technologies owing to its high speed and penetration, and has increased the automation and flexibility of an entire industry. Laser welding of dissimilar metals has been widely used to improve the wear resistance and corrosion resistance of industrial parts. The objective of this research is to investigate the influence of process parameters on the welding of SM45C and STS304 with CW Nd:YAG lasers. Bead-on-plate welding tests were carried out for several combinations of the experimental conditions. In order to quantitatively examine the characteristics of the dissimilar welding, the welding quality of the cut section, strain-stress behavior, and hardness of the welded part were investigated.

• 한국신재생에너지학회:학술대회논문집
• /
• 2007.06a
• /
• pp.335-338
• /
• 2007

Cost effectiveness is an important parameter for producing DSSCs as compared to the widely used conventional silicon based solar cells. A fluorine-doped tin oxide (FTO) substrate coated with a catalytic amount of platinum is used as counter electrode in dye-sensitized solar cell. Carbonaceous materials are quite attractive to replace platinum due to their high electronic conductivity, corrosion resistance towards $I_{2}$, good catalytic effect and low cost. In this paper, the unit DSSCs with Pt and CNT as a counter electrode were connected in series-parallel externally, then the current-voltage curves were investigated to find out the connection characteristics of the DSSC with CNT counter electrode. The connection characteristics of the DSSC with CNT counter electrode is superior to that of the DSSC with Pt counter electrode. And a parallel connection of the DSSC with CNT counter electrode has higher efficiency than a series connection of that.

• Journal of the Korean Society of Industry Convergence
• /
• v.10 no.4
• /
• pp.201-206
• /
• 2007

Most of the fatigue fractures of various machine structures start at discontinuities or small defects. In this study property of crack growth of titanium alloy was also analyzed to investigate the difference compared with the carbon steel. Titanium alloy has very high specific strength, and the material is widely utilized in advanced engineering fields such as aerospace, atomic energy and ocean development because of its excellence in corrosion and heat resistance. Generally the machine structures experience irregular loadings rather than periodic forces. The prediction of the fatigue life therefore has been analyzed to provide fundamentals of the design and estimation of the machine structures under irregular loading conditions.

• Journal of Welding and Joining
• /
• v.27 no.2
• /
• pp.27-31
• /
• 2009

Ferritic stainless steels have a good heat resistance and economic advantage. They are used for applications such as automotive exhaust systems where resistance to general corrosion is superior to carbon steels. However, there are not enough research for ferritic stainless steels on weldability mainly used as automotive exhaust manifolds. In this study, mechanical and microstructure properties of as-welded STS 429L and STS 444 ferrite stainless steels were confirmed by tensile, bending, hardness test, optical microscopy and scanning electron microscopy. Tensile strength of the STS 444 is higher than the STS 429L when it is a raw material. In contrast to this fact, STS 429L indicated higher tensile strength after butt welded. In addition, the hardness have a increasing tendency as getting down on the bead.

• Transactions of the Korean hydrogen and new energy society
• /
• v.24 no.4
• /
• pp.311-319
• /
• 2013

A clear understanding on cell voltage-reversal behavior due to local hydrogen starvation in a stack is of paramount importance to operate the fuel cell vehicle (FCV) stably since it affects significantly the cell performance and durability. In the present study, a novel experimental method to simulate the local cell voltage-reversal behavior caused by local hydrogen starvation, which typically occurs only one or several cells out of several hundred cells in a stack of FCV, has been proposed. Contrary to the conventional method of overall fuel starvation, the present method of local hydrogen starvation caused the local cell voltage-reversal behavior in a stack very well. Degradation of both membrane electrode assembly (i.e., pin-hole formation) and gas diffusion layer due to an excessive exothermic heat under voltage-reversal condition was also observed clearly.

• Journal of the Korean Society for Precision Engineering
• /
• v.26 no.11
• /
• pp.55-61
• /
• 2009

The wall thinning defect of nuclear power pipe is mainly occurred by the affect of the flow accelerated corrosion (FAC) of fluid. This type of defect becomes the cause of damage or destruction of in carbon steel pipes. Therefore, it is very important to measure defect which is existed not only on the welding part but also on the whole field of pipe. This study use dual-beam Shearography, which can measure the out-of-plane deformation and the in-plane deformation by using another illuminated laser beam and simple image processing technique. And this study proposes Infrared thermography, which is a two-dimensional non-contact nondestructive evaluation that can detect internal defects from the thermal distribution by the inspection of infrared light radiated from the object surface. In this paper, defect of nuclear power pipe were, measured using dual-beam shearography and infrared thermography, quantitatively evaluated by the analysis of phase map and thermal image pattern.

• Journal of Korean Society of Water and Wastewater
• /
• v.28 no.5
• /
• pp.589-600
• /
• 2014

Tuberculation and slime accumulated in water mains play an important role in modifying water quality of drinking water. Therefore, in this study, it was investigated that what materials were accumulated, and what components were included in the tuberculation and slime of water mains. The Various tuberculation and slime sample were collected from the 12 water mains to analyze their physical and chemical properties and crystal structure. As a analysis method, VSS(Volatile suspended solid), SEM(scanning electron microscope), EDS(Energy Dispersive X-ray spectroscope), ICP(Inductively Coupled Plasma Mass Spectrometer) and XRD(X-Ray Diffractomete) were used. The results of analysis on the samples, the representative materials were verified such as iron corrosion products, the fine sand particles generated during backwash, fine particles of activated carbon, aluminum used in coagulation process, and manganese included in raw water.

• Journal of Environmental Health Sciences
• /
• v.32 no.5 s.92
• /
• pp.431-439
• /
• 2006

This research was conducted using a model home plumbing system composed of copper, stainless steel, galvanized iron, carbon steel, and PVC (polyvinyl chloride) pipe. The number of bacteria present in stainless steel pipe and PVC was higher than other pipes. High turbidity and zinc release were found in galvanized iron pipe material and detected during the first 6 months. Conversely, there was a decrease in turbidity and zinc release after 6 months resulting in levels similar to other pipes. Copper concentration decreased as operation times increased. In this experiment, the number of bacteria detected in biofilm for a copper pipe continued to increase. Pipe material influenced bacterial numbers in biofilm and water. This showed that elevated chlorine could not control bacterial growth in biofilm for galvanized iron and stainless steel systems. It also suggested that the dosing of chlorine might not be available for all kinds of pipes. Therefore, another complementary method should be introduced to manage biofilm effectively in water distribution systems.

• Computers and Concrete
• /
• v.19 no.4
• /
• pp.339-346
• /
• 2017

The main objective of this paper was to illuminate the effect of marine environmental condition on durability of reinforced concrete (RC)-corroded columns strengthened with carbon fiber reinforced polymer (CFRP) and glass fiber reinforced polymer (GFRP) layers. Small-scale columns were prepared and corroded by an accelerated corrosion process. After strengthening, compressive strength tests were carried out on control and weathered specimens. In this research, a marine simulator was designed and constructed similar to the tidal zone of marine environment in south of Iran which was selected as a case study in this research. Mechanical properties of wrapped specimens were studied after placing them inside the simulator for 3000 hours. Marine environment decreased ultimate strength by 4.5% and 26.3% in CFRP and GFRP-wrapped columns, respectively. In some corroded-columns, strengthening was carried out after replacing damaged cover by self-compacted mortar. In this method, by confining with one layer of CFRP and GFRP, 4.2% and 22.4% reduction in ultimate strength was observed, respectively, after exposure. Furthermore, the elastic-brittle behavior has been verified in this retrofit method. Also results of tension tests revealed, the ultimate tensile strength was degraded by 2% and 28.8% in CFRP and GFRP sheets, respectively, after applying marine exposure.