• The korean journal of orthodontics
• /
• v.37 no.5
• /
• pp.376-385
• /
• 2007

Esthetic brackets which resemble the color of natural teeth have been widely used. But the frictional resistance of ceramic brackets, a typical esthetic bracket, is greater than that of metal brackets. The purpose of this study was to measure the frictional resistance of the new calcium phosphate brackets (CPB) which were recently developed and to evaluate its clinical usability by comparing the frictional differences of CPB with metal brackets and metal slot inserted ceramic brackets. Methods: Experimental groups were CPB (Hyaline II, Tomy, Tokyo, Japan), metal bracket (Kosaka, Tomy, Tokyo, Japan) and metal slot inserted ceramic bracket (Clarity, 3M Unitek, Monrovia, CA, USA). All of the brackets had 0.022-inch slot sizes. The brackets were tested with $0.019\;{\times}\;0.025$ inch stainless steel wire (3M Unitek, Monrovia, CA, USA). A biologic model was used to simulate the situation which would occur during orthodontic treatment with fixed appliances. Retraction force was applied at a speed of 5 mm/min for 30 seconds. The frictional resistance was measured on a universal testing machine (Instron 4467, Instron, Norwood, MA, USA). Results: CPB showed significantly higher friction than metal brackets (p < 0.05) and lower friction than metal slot inserted ceramic brackets (p < 0.01). Conclusions: CPB can be considered to be a useful orthodontic esthetic bracket with respect to frictional resistance, as its friction is remarkably lower than that of metal slot inserted ceramic brackets.

• The korean journal of orthodontics
• /
• v.42 no.1
• /
• pp.17-22
• /
• 2012

Objective: To study and compare the effects of different demineralization-inhibition methods on the shear bond strength (SBS) and fracture mode of an adhesive used to bond orthodontic brackets to demineralized enamel surfaces. Methods: Eighty freshly extracted, human maxillary premolars were divided into 4 equal groups and demineralized over the course of 21 days. Brackets were bonded to the demineralized enamel of teeth in Group 1. In Group 2, bonding was performed following resin infiltration ($ICON^{(R)}$, DMG, Hamburg, Germany). Before bonding, pre-treatment with acidulated phosphate fluoride (APF) or solutions containing casein phosphopeptide-amorphous calcium phosphate with 2% neutral sodium fluoride (CPP-ACP/wF) was performed in Groups 3 and 4, respectively. The SBS values of the brackets were measured and recorded following mechanical shearing of the bracket from the tooth surface. The adhesive remnant index (ARI) scores were determined aft er the brackets failed. Statistical comparisons were performed using one-way ANOVA, Tukey's post-tests, and G-tests. Results: Significant differences were found in some of the intergroup comparisons of the SBS values (F = 39.287, p < 0.001). No significant differences were found between the values for the APF-gel and control groups, whereas significantly higher SBS values were recorded for the resin-infiltrated and CPP-ACP/wF-treated groups. The ARI scores were also significantly different among the 4 groups (p < 0.001). Conclusions: Tooth surfaces exposed to resin infiltration and CPP-ACP/wF application showed higher debonding forces than the untreated, demineralized surfaces.

• The korean journal of orthodontics
• /
• v.43 no.1
• /
• pp.23-28
• /
• 2013

Objective: The purpose of this study was to evaluate the effect of casein phosphopeptide amorphous calcium phosphate (CPP-ACP) on the shear bond strength (SBS) of brackets bonded to non-demineralized teeth with either phosphoric acid etching or self-etching primer. Methods: Sixty human premolars were randomly assigned to 1 of 4 treatment groups (n = 15 each): phosphoric acid etching (group 1); self-etching primer (group 2); CPP-ACP for 2 weeks + phosphoric acid etching (group 3), and CPP-ACP for 2 weeks + self-etching primer (group 4). After bonding of the maxillary premolar metal brackets, specimens were subjected to shear forces in a testing machine. Scanning electron microscopy was used to observe etching patterns on the enamel surfaces of all teeth. A 2-way analysis of variance was used to test for effects of CPP-ACP and etching system on SBS. Results: Significantly higher mean SBSs were observed in groups subjected to phosphoric acid etching (i.e., groups 1 and 3; p < 0.05). On the other hand, SBSs did not appear to be influenced by CPP-ACP (i.e., groups 3 and 4; p > 0.05). We observed a uniform and clear etched pattern on the enamel surface of the phosphoric acid etching groups. Conclusions: CPP-ACP does not significantly affect the SBS of orthodontic brackets bonded to non-demineralized teeth, regardless of which adhesive method is used to bond the brackets.