• Fire Science and Engineering
• /
• v.19 no.2 s.58
• /
• pp.75-80
• /
• 2005

This dissertation is about the development of PTC(Positive Temperature Coefficient) thermistor by composition method. A multilayer-type PTC samples were fabricated under optimal conditions after setting the experimental composition equation as $(0.90Ba+0.05Sr+0.05Ca)TiO_3+0.01TiO_3+0.01SiO_2+0.0008MnO_2+0.0018Nb_2O_5$ and their testing results were analyzed. The fabrication method of SMD(Surface Mounted Device) multilayer -type sample based on the composition ratio has the advantages in lowering its resistivity at room temperature, considerably, and increasing maximum current level, as needed. Although there is a disadvantage of peak resistivity drop by the multilayer, causing the increasement of thermal capacity. and thereby, increasing the switching delay time, a high applying voltage can increase the peak resistivity and shorten the switching delay time. The voltage-current characteristic showed that the more multilayers increased the initial maximum current and the transition voltage that increased the resistivity abruptly according to the curie point. The element it could be applied with the sensor for the fire detector.

• Korean Journal of Organic Agriculture
• /
• v.23 no.3
• /
• pp.595-604
• /
• 2015

Soil chemical properties in paddy fields were found to be varied depending upon different cultivation methods such as environmentally-friendly, conventional, and two-crop farming systems and different topographical regions, namely plain, middle mountainous, and reclaimed land regions. Overall soil pH was found to be in optimal range (pH 5.5~6.5) for rice cultivation, except with conventional cultivation fields of the reclaimed lands in Jeonnam province. Electrical conductivity (EC) was relatively higher in the two-crop cultivation fields than in others. However, the concentrations of available phosphate as $P_2O_5$ were exceptionally higher in the two-crop farming fields, thus in submerged paddy condition the phosphate could be released into streams and rivers. Soil organic matter (SOM) contents were mostly in optimal range ($25{\sim}30g\;kg^{-1}$) for paddy field in Jeonbuk province, but in Jeonnam province they were slightly higher values of the range. The concentrations of available silicate ($SiO_2$) were mostly depended on the cultivation methods and the region, but some of paddy fields contained extremely high $SiO_2$ concentration. Statistical relationships among the soil chemical properties showed as follows: Correlations between EC values and exchangeable cation concentrations, between SOM contents and CEC values, and between available $SiO_2$ concentrations and pH, EC, exchangeable cations, and CEC values were positively significant, whereas total nitrogen concentrations were significantly negatively correlated with the concentrations of exchangeable K and Mg. These results might be very useful to establish benchmark paddy fields contained with certain levels of soil fertility.

• Journal of the Korean Magnetics Society
• /
• v.9 no.3
• /
• pp.149-153
• /
• 1999

Frequency and temperature dependence of magnetic loss has been investigated in Mn-Zn ferrites containing the sesistive temary compounds of $SiO_2-CaO-V_2O_5$. The Mn-Zn ferrite with the composition of $MnO:ZnO:Fe_2O_3=36:11:53$(by mol %) are prepared by self-propagating high-temperature synthesis. From the results of frequency dependence of core loss, it has been found that the hysteresis loss is dominant at low frequency and the eddy current loss becomes more dominant as the frequency increases. With the addition of resistive compound, the frequency dependence of core loss, it has been found that the hysteresis loss is dominant at low frequency and the eddy current loss becomes more dominant as the frequency increases. With the addition of resistive compound, the frequency region where the hysteresis loss is dominant becomes wide. The core-loss minimum occurs at about 4$0^{\circ}C$ in the specimens with the additive because of the reduction in eddy current loss.

• KOREAN JOURNAL OF CROP SCIENCE
• /
• v.31 no.2
• /
• pp.195-203
• /
• 1986

In order to clarify the trend of change in mineral nutrients in rice plant on various ripening process, P$_2$O$\sub$5/, K$_2$O, MgO, CaO, SiO$_2$ and ash contents were determined for the grain, internode, leaf-5heath and leaf blade respectively for 9 times at an week interval after heading. Four rice cultivars with different maturity and ecotype were grown under normal cultural conditions for the trial. The contents of mineral nutrients in the brown rice were in the order of Ash, P$_2$O$\sub$5/, K$_2$O and MgO. CaO and SiO$_2$ were found in minute quantity in the brown rice. The hull contained SiO$_2$ in large quantity, and it also contained the mineral nutrients in the order of K$_2$O, P$_2$ O$\sub$5/O. The CaO content of hull was extremely minute.

• Journal of Conservation Science
• /
• v.22
• /
• pp.43-60
• /
• 2008

This study is investigated the characteristics and the comparison on blackware and whiteware at Gilmyeong-ri kilns, located Poncheon-si, Geonggi province at AD 19c using scientific analysis. It is measured by scientific analysis classified as microstructure observation, physical methods which involved chromaticity, specific gravity, absorption ratio and porosity, and chemical analysis of components of body and glaze. As a result, a particle and a pore of body surface appeared differently by the degree of vitrification. In glaze, Blackware have better on good vitrification than whiteware in the microstructure observation. The physical characteristics of chromaticity, specific gravity, absorption ratio and porosity differed according to degree of vitrification rather than porcelain types. In composition, body of blackware have higher ratio of $Fe_2O_3$ and $TiO_2$ than of whiteware. Also glaze of blackware have higher ratio of $Fe_2O_3$ and $TiO_2$, and lower ratio of $SiO_2$ and $Al_2O_3$ than whiteware. Especially, blackware have higher ratio in the composition of CaO and $P_2O_5$ by which ash is used or not.

• Korean Journal of Soil Science and Fertilizer
• /
• v.25 no.1
• /
• pp.38-43
• /
• 1992

A field experiment was conducted to find out the effect level of nitrogen fertilization on the yield and quality of hop (Hallertau variety) emphasis given to ${\alpha}$-acid content. Nitrogen was applied by the rates of 0, 12, 18, 24, 30 and 36kg per 10a. Results were summarized as follows. 1. Stages of cone-hair developing and coneripening were delayed with increment of nitrogen applied. Number of nodes and length of vine increased with nitrogen applid by up to 24kg N/10a. 2. Yield was the highest in the 24kg N/10a plot and cone weight had high significant correlations with yield without regard to the years of growth. No.of flower per side blanch and weight of 100 cones had a significant correlation with yield in the four-year old and five-year old Hop plants. 3. Nutrient content in Hop plants was in the order of CaO, total nitrogen, $K_2O$, MgO and $P_2O_5$. Content of total nitrogen, CaO and MgO was high in leaves while that of $P_2O_5$ and $K_2O$ was high in cone. Nitrogen, phosphorus and magnesium increased with increment of nitrogen fetilized while potassium and calcium decreased. 4. As for the distribution of nutrients in cone developing stage $SiO_2$ content was higher in lower part than in the upper part while $P_2O_5$ contetn was higher in upper part than in lower part of the plant. And content of nitrogen and potassium was higher in middle height than in upper and lower part. 5. The optimum levels of nitrogen application were 19.3kg for 2 years, 24.3kg for 3-year, 27.9kg for 4 years and 31.8kg/10a for 5-year old Hop, respectively. 6. Nitrogen uptake in cone showed a positive correlation with the content of ${\alpha}$-acid and ${\beta}$-acid in cone.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1998.06a
• /
• pp.105-109
• /
• 1998

Langasite({{{{ { La}_{ 3} {Ga }_{5 } {SiO }_{14 } , LGS}}}}) powder was prepared by a polymerized complex method based on the Pechini-type reaction. A mixed solution of ethylene glycol(EG), cotric acid(CA), lanthanum, gallium and silicon ions, with a molar ratio of EG:CA:La:Ga:Si=100:25:3:5:1, was polymerzed to from a transparent resin, which was used as a precursor for the synthesis of LGS. X-ray diffraction(XRD) patterns indicated that the LGS phase could be formed by the heat-treatment in air at 1000$^{\circ}C$ for 3hrs

• The Journal of the Petrological Society of Korea
• /
• v.12 no.3
• /
• pp.119-134
• /
• 2003

Yuksipryeong two-mica granite presents strongly peraluminous characteristics in both mineralogy and geochemistry. It has high aluminum saturation index with 1.15∼l.20 and high corundum with 2.20∼2.98 wt% CIPW norm. As the color index is <16% and FeO$\^$T/+ MgO + TiO$_2$is average 1.9 wt％, it corresponds to leucogranite. Yuksipryeong two-mica leucogranite shows negative linear trend for TiO$_2$, Al$_2$O$_3$, FeO, Fe$_2$O$_3$, MgO, CaO, K$_2$O, P$_2$O$\_$5/, Rb, Ba, and Sr as SiO$_2$increases, and the positive relation of Zr and Th, which result from feldspar, biotite, apatite and zircon fractionation. Pegmatitic dike has higher SiO$_2$and P$_2$O$\_$5/, but lower another major elements. Yuksipryeong two-mica leucogranite has lower Rb, but higher Ba and Sr than Manaslu, Hercynian two-mica leucogranites, and S-type granites in Lachlan Fold Belt. Pegmatitic dike has higher Rb and Nb but lower Ba, Sr, Zr, Th, and Pb contents than Yuksipryeong two-mica leucogranite, resulting in removing or mobilizing for some trace elements from the granitic melt. Yuksipryeong two-mica leucogranite has total REEs with 95.7∼l23.3 ppm, and chondrite-normalized REE pattern is very steep ((La/Yb)$\_$N/ = 6.9∼24.8), light REEs (LREEs)-enriched End heavy REEs (HREEs)- depleted pattern with low to moderate Eu anomalies (Eu/Eu＊= 0.7∼0.9). While pegmatitic dike has low total REEs with 7.0 ppm, and chondrite-normalized REE pattern is flat-pattern ((La/Yb)$\_$N/ = 2.1) with strong negative Eu anomalies (Eu/Eu＊= 0.2). The melt compositions having formed two-mica leucogranites depend on not only the source rock but also the amounts of the residual remaining after melting of source rocks. The CaO/Na$_2$O and Rb/Sr-Rb/Ba ratios depend mainly on the composition of source rocks in the strongly peraluminous granite, that is, plagioclase/clay ratio of the source rocks. Yuksipryeong two-mica leucogranite has higher CaO/Na$_2$O and lower Rb/Sr-Rb/Ba ratios than Manaslu and Hercynian two-mica leucogranites (Millevaches and Gueret) derived from clay-rich, plagioclase-poor (polite), which suggest that the probable source rocks for Yuksipryeong two-mica leucogranite is clay-poor, plagioclase-rich quartzofeldspathic rocks. As the concentrations of Al$_2$O$_3$remain nearly constant but those of TiO$_2$increases as increasing temperature in the strong peraluminous melt, the Al$_2$O$_3$/TiO$_2$ratio may reflect relative temperature at which the melts have formed. Comparing the polite-derived Manaslu and Hercynian two- mica leucogranites, Manaslu two-mica leucogranite has higher Al$_2$O$_3$/TiO$_2$ratio than latter, and its melt have formed at relatively lower temperature ($\leq$ 875$^{\circ}C$) than Hercynian two-mica leucogranites. Likewise, comparing the quartzofeldspathic rock-derived granites, Yuksipryeong two-mica granite has higher Al$_2$O$_3$/TiO$_2$, ratio than S-type granites in Lachlan Fold Belt (>875$^{\circ}C$). The melt formed Yuksipryeong two-mica leucogranite are considered to have been formed at temperature at below the maximum 875$^{\circ}C$C$.

• Journal of the Mineralogical Society of Korea
• /
• v.18 no.1
• /
• pp.11-17
• /
• 2005

Na-A zeolite were synthesized from melting slag of the incinerated ash by the alkaline activation processes. The experiments were performed in stainless steel vessels, with continuous stirring during the reaction periods. The silica-rich solution, a starting material, which was the waste of crystal growth factory, contains 5.7 wt% SiO₂ and 3.2 wt% Na₂O. And NaAlO₂ was made by the reaction of aluminium dross and NaOH solution and its molar ratios were Na₂O/Al₂O₃= 1.2 and H₂O/Na₂O=9. During the residence time of 7∼8 h at 80℃, the mixing of the silica-rich solution, NaAlO₂ and melting slag yields the production of homogeneous Na-A zeolite. The optimal reactant composition in molar ratio of Na₂O:Al₂O₃:SiO₂ was 1.3∼l.4 : 0.8∼0.9 : 2 and mixing ratio of solution and slag was 1/7∼10 (g/cc). Synthesized Na-A zeolite has cubic form uniformly and its size ranges about 1 ㎛. Ca/sup 2+/ ion exchange capacity of the Na-A was about 180∼210 meq/100g, corresponding approximately 80% to the commercial detergent builder.

• Bulletin of the Korean Chemical Society
• /
• v.16 no.6
• /
• pp.539-542
• /
• 1995

The crystal structure of K92-X (K92Al92Si100O384), a=25.128(1) Å, dehydrated at 360 ℃ and 2X 10-6 Torr, has been determined by single-crystal X-ray diffraction techniques in the cubic space group Fd&bar{3} at 21(1) ℃. The structure was refined to the final error indices R1=0.044 and Rw=0.039 with 242 reflections for which I<3σ(I). In this structure, ninety-two K+ ions are located at the five different crystallographic sites. Sixteen K+ ions are located at the centers of the double six rings (site I; K(1)-O(3)=2.65(2) Å and O(3)-K(1)-O(3)=92.0(6)°). About twelve K+ ions lie at site I' in the sodalite cavity opposite double six rings (D6R's) and these K+ ions are recessed ca. 1.62 Å into the sodalite cavity from their O(3) plane (K(2)-O(3)=2.74(2) Å, O(3)-K(2)-O(3)=88.5(8)°). About thirty-two K+ ions are located at the site II in the supercage and these K+ ions are recessed ca. 1.20 Å into the supercage from their O(2) plane (K(3)-O(2)=2.64(2) Å, and O(2)-K(3)-O(2)=101(1)°). About twenty-two K+ ions lie at the site III in the supercage opposite 4-ring ladder and the remaining ten K+ ions lie at the site III' near the 4-ring ladder in the supercage (K(4)-O(4)=2.88(3) Å, O(4)-K(4)-O(4)=79.8(9)°, K(5)-O(4)=2.8(2) Å, and O(4)-K(5)-O(4)=68(5)°).