• Journal of Welding and Joining
• /
• 제35권1호
• /
• pp.68-73
• /
• 2017

During welding of Ni based superalloy, hot cracking was usually happen in the fusion zone of a weld. In this study, the laser weldability of Inconel 713C alloy for the turbocharger wastegate valve (WGV) was evaluated with various welding conditions, such as laser power, welding speed, shielding gas. Welding conditions were optimized by bead-on-plate (BOP) and butt joint welding. For the evaluation of laser weldability, bead shapes and weld microstructures were investigated and tensile test was conducted. The fracture surfaces were investigated for the understanding the cause of the fracture.

• Coupled systems mechanics
• /
• 제7권5호
• /
• pp.627-634
• /
• 2018

Laser beam welding is more advantageous compared to conventional methods. Titanium/Aluminium dissimilar alloy thin sheet metals are difficult to weld due to large difference in melting point. The performance of the weldment depends upon interlayer formation and distribution of intermetallics. During welding, aluminium gets lost at the temperature below the melting point of titanium. Therefore, it is needed to improve a new metal joining techniques between these two alloys. The present work is carried for welding TI6AL4V and AA2024 alloy by using Nd:YAG Pulsed laser welding unit. The performance of the butt welded interlayer structures are discussed in detail using hardness test and SEM. Test results reveal that interlayer fracture is caused near aluminium side due to low strength at the weld joint.

• Journal of Welding and Joining
• /
• 제13권1호
• /
• pp.156-166
• /
• 1995

Experimental models which are able to determine the deviation between weld line and weaving center by measuring the weld current during welding were proposed for the gas metal arc welding process. The models were used for developing a weld seam tracking system which controls the weaving speed of a welding torch. However, it was revealed that the tracking result of the system is affected by the welding conditions. Thus an arc sensor system was developed by using fuzzy control approach for overcoming the difficulty of modelling the nonlinear process. The rule base and parameters of the fuzzy control system were determined on the basis of the results of experiments. This fuzzy control system has shown the successful tracking capability for the wide operating range of welding conditions.

• 전력전자학회:학술대회논문집
• /
• 전력전자학회 1997년도 전력전자학술대회 논문집
• /
• pp.45-48
• /
• 1997

The low frequency pulsed MIG welding process of new current waveform control to switch over unit pulse conditions (pulse current, pulse duration) in the fixed cycle was developed and its effect were investigated for aluminium and its alloy. By using this new welding process, the bead appearance having clear ripple pattern, such as TIG welding bead can be obtained and the gap tolerance of lap and butt welding joint can be expanded.

• 대한기계학회논문집
• /
• 제5권3호
• /
• pp.199-206
• /
• 1981

This paper presents a method of calculation of the stresses, the strains and the deflections due to welding in L shape and in T shape. Using step by step method of plasticity and establishing the equilibrium conditions in section, we calculated thermal stresses and strains during welding and in the final step of calculation we got the residual stresses, strains and the deflections due to welding. Also we measured the stresses and the strains with hole-drilling method and compared the results with the method of calculation presented in this paper. Because of its symmetry of section, the deflection due to welding in T shape is generally much less than that in L shape. The residual stresses are tensile in welded joints and HAZ, and compressive in base metal as butt welding of plates, but the compressive stresses in base metal decrease repidly as the points are away from welded joint except horizontal plates of T shape. The theoretical method of calculaiton presented in this paper coincides faily well with the experiment.

• Journal of Welding and Joining
• /
• 제23권1호
• /
• pp.55-60
• /
• 2005

A three-dimensional Gaussian heat source model is modified to include the effects of the gap and thickness-difference for the laser keyhole welding. The gap of the butt joint influences the welding efficiency such that the melting area decreases linearly with the gap. When the different plate thickness is used such as the tailored blank welding, melting areas of the thick and thin plates are predicted by introducing the thickness-difference factor. The calculated results using the modified heat source show reasonably good agreements with the experimental results.

• 대한기계학회논문집A
• /
• 제28권9호
• /
• pp.1328-1336
• /
• 2004

According to our fatigue tests carried out at 20 Hz, R=0.1 on transversely butt-welded joints, fatigue strengths of as-welded specimens, that is, specimens having residual stress are higher than those of annealed specimens in short life range, but vice verse in long life range. This behavior seems to be concerned mainly with residual stress relaxation by applied loading. After analyzing the welding process, we conducted finite element analysis to quantify the degree of residual stress relaxation. By taking into account residual stress relaxation, modified Goodman diagram, and nominal stress, we evaluated the fatigue life of the welded joint from the S-N curve for the parent material. The estimated results are in a good agreement with the experimental results.

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 1996년도 춘계학술발표회논문집(3)
• /
• pp.92-97
• /
• 1996

The fatigue crack propagation behavior in SA106 Gr.C main steam pipe weld joint was investigated in air environment. Crack growth rate tests were conducted on base metal and weld metal at load ratio of 0.1 and 0.3 and at frequency of 10Hz. The fatigue crack growth rates of the base metal and the weld metal were above the ASME reference line and the fatigue crack propagation rate of the weld metal was higher than those of the base metal. Fatigue crack growth rate increased with increasing the load ratio and the effect of the load ratio was more significant in the weld metal. The post weld heat treatment increased the fatigue crack growth rates of the base metal by reducing compressive residual stress and decreased those of the weld metal by reducing weld defects.

• Journal of Welding and Joining
• /
• 제15권2호
• /
• pp.54-63
• /
• 1997

For the purpose of establishing laser welding condition (laser power, welding speed and beam focus) and of evaluating tailored blanks for two kinds of thin steel sheets SPCC and SK5M using in the thin plate structure such as automobile, train, and so on, investigated their $CO^2$ laser weldability under various initial welding conditions. SPCC thin sheet showed good weldability under some welding conditions. But, high carbon steel sheet SK5M needed heat treatment after welding to obtain ductility of the welded joint. And next, tailored blank was tested through deep drawing to evaluate reliability of their obtained laser welding conditions. The forming depths by tailored blank were SPCC+SPCC=22-25mm and SK5M+SK5M=13-25mm.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2008년도 춘계학술발표대회 개요집
• /
• pp.30-30
• /
• 2008