• 대한소아치과학회지
• /
• 제25권2호
• /
• pp.400-420
• /
• 1998

We already know that it is very difficult to obtain an "isolated field" for direct bonding during the surgical exposure of unerupted teeth. The aim of this in-vitro study is to simulate the clinical situation of forced eruption and to evaluate the tensile strengths of preligatured button with several types of contamination which can happen during the surgical exposure of unerupted teeth. Four orthodontic direct bonding systems were used. ($Ortho-One^{TM}$, $Rely-a-Bond^{(R)}$, $Ortho-Two^{TM}$, Phase $II^{(R)}$) Each material was divided into four groups(n=20) : Group 1. (Control, no contamination), Group 2. (Rinse etching agent with saline instead of water), Group 3. (Blood contamination of etched surface for 30 seconds), Group 4. (Blood contamination of primed surface for 30 seconds) 320 bovine anterior permanent teeth were divided into the above mentioned 16 groups. Enamel surface was flattened and ground under water coolant. Pre-ligatured buttons were prepared to the same form. (Cut 0.25 ligature wire 10 cm in length. Twist the ligature wire 30 times clockwise. Mark the wire 15mm and 35mm points from button. Make a loop sticking two points together and twist the loop 6 times counterclockwise.) The bonded specimens were stored at $37^{\circ}C$ saline solution for 3 days. Then the tensile strength of each sample was measured with Instron universal testing machine, crosshead speed of 0.5mm/min. The following results were obtained: 1. As compared to control groups (Group 1) of each material, Rely-a-Bond had a significantly lower mean tensile strengths than other material. (p<0.01) 2. In Group 2. of Ortho-One and Rely-a-Bond, the mean tensile strengths decreased about 7.7% and 11.1%, respectively with statistical significances. (p<0.05) 3. In Group 2. of Ortho-Two and Phase II, the mean tensile strengths did not decrease. 4. In Group 3. of Ortho-One, Rely-a-Bond, Ortho-Two, and Phase II, the mean tensile strengths decreased about 60.8%, 56.1%, 60.2%, and 46.0%, respectively with statistical significances. (p<0.01) 5. In Group 4. of Ortho-One and Rely-a-Bond, the mean tensile strengths did not decrease. 6. In Group 4. of Ortho-Two and Phase II, the mean tensile strengths were decreased about 20.95% and 22.28%, respectively with statistical significances. (p<0.01) There were formations of a hump shaped mass from bonding resin under blood contamination which disturbed direct bonding procedure. According to Reynolds, the proper bond strength for clinical manipulation should be at least 45N or about 4.5Kg.F. According to these results, it can be concluded that Ortho-One could be used during surgical exposure of unerupted teeth. In any case, blood contamination of the etched surface should be avoided, but the blood contamination of primed surface of Ortho-One may not decrease bond strength. Just 'blowing-out' is enough to remove blood from primed surface of Ortho-One. You can verify the clean surface of the primer of Ortho-One after blowing out the blood contamination.

• 대한소아치과학회지
• /
• 제37권1호
• /
• pp.35-43
• /
• 2010

본 연구는 젤라틴과 메틸셀룰로오스를 기저재로 한 불소겔을 제작하고 이들의 높은 점조도와 표면에 흡착하는 능력이 치면에 불소를 오랜 시간 저류시켜 법랑질 탈회를 효과적으로 억제할 수 있는지 살펴보고자 시행되었다소의 전치로 시편 80개를 제작하였으며, (1) APF gel (2) $CavityShield^{TM}$, (3) Gelatin F gel (4) Methyl cellulose F gel 이렇게 4개의 군으로 분류하였다. 모든 시편을 인공우식용액에 72시간동안 보관하여 법랑질을 탈회시킨 후, 표면미세경도 측정법과 편광 현미경하에서 병소의 탈회 깊이를 측정하는 두 가지 방법을 사용하여 탈회정도를 측정하였다. 연구결과는 다음과 같다. 1) 불소를 처리한 experimental side와 처리하지 않은 control side간 미세경도의 차이는 APF를 적용한 제1군에서 71.82(VHN)로 가장 작은 것으로 나타났다(p<0.05). 2) $CavityShield^{TM}$를 도포한 제2군에서 148.24(VHN)로 가장 큰 차이를 보여 불소바니쉬의 탈회억제효과가 가장 큰 것으로 나타났다(p<0.05). 3) Gelatin과 methyl cellulose F gel을 도포한 3군과 4군에서 control side와 experimental side간 미세경도의 차이는 1군보다는 높고 2군보다는 낮았으나 3군과 4군간에 유의한 차이는 없었다(p>0.05). 4) 인공탈회병소의 깊이를 측정한 결과 APF를 처리한 제1군에서 control side와 experimental side간 병소의 깊이차이는 $16.69\;{\mu}m$로 가장 적게 나타났다(p<0.05). 5) 2,3,4군 에서는 병소깊이 측정을 통해 탈회억제효과가 APF군에 비해 우수하게 나타났으나(p<0.05) 각 군 간에 차이는 검증되지 않았다(p>0.05). 이상의 결과를 종합하여 보면 실험적으로 제조된 두 가지 불소겔은 APF gel에 비해 법랑질 탈회 억제효과가 우수하다고할 수 있으며 이는 APF gel에 비해 gelatin이나 methyl cellulose 의 높은 점조도가 불소를 더 장시간 치면에 접촉시킨 것으로 생각된다. 현재 가장 우수한 치면 잔류시간을 보이는 것으로 인정되는 불소바니쉬와 비교하여도 이들의 효과가 크게 떨어지지 않는 것을 알 수 있었으며 이는 향후 천연고분자 화합물을 이용한 다양한 불소제제의 개발 가능성을 보여주는 것이라 사료된다.