• Journal of the Korean Society of Safety
• /
• v.29 no.4
• /
• pp.9-14
• /
• 2014

Self-piercing riveting(SPR) is a mechanical fastening technique which is put pressure on the rivet for joining the sheets. Unlike a spot welding, SPR joining does not make the harmful gas and $CO_2$ and needs less energy consumption. In this study, static and fatigue tests were conducted using tensile-shear specimens with Al-5052 plates for evaluation of fatigue strength of the SPR joints. During SPR joining process for the specimen, using the current sheet thickness and a rivet, the optimal applied punching force was found to be 21 kN. And, the maximum static strength of the specimen produced at the optimal punching force was 3430 N. During the fatigue tests for the specimens, interface failure mode occurred on the top substrate close to the rivet head in the most high-loading range region, but on the bottom substrate close to the rivet tail in the low -loading range region. There was a relationship between applied load amplitude $P_{amp}$ and lifetime of cycle N for the tensile-shear, $P_{amp}=3395.5{\times}N^{-0.078}$. Using the stress-strain curve of the Al-5052 from tensile test, the simulations for fatigue specimens have been carried out using the implicit finite element code ABAQUS. The relation between von-Mises equivalent stress amplitude and number of cycles was found to be ${\sigma}_{eq}=514.7{\times}N^{-0.033}$.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.5
• /
• pp.396-401
• /
• 1999

In this study, $Ar^+$ ion laser etching process of single/poly-crystalline Si with $CCl_2F_2$ gas is investigated for MEMS applications. In general, laser direct etching process is useful in microelectronic process, fabrication of micro sensors and actuators, rapid prototyping, and complementary processing because of the advantages of 3D micromachining, local etching/deposition process, and maskless process with high resolution. In this study, a pyrolytic method, in which $CCl_2F_2$ gasetches molten Si by the focused laser, was used. In order to analyze the temperature profile of Si by the focused laser, the 3D heat conduction equation was analytically solved. In order to investigate the process parameters dependence of etching characteristics, laser power, $CCl_2F_2$ gas pressure, and scanning speed were varied and the experimental results were observed by SEM. The aspect ratio was measured in multiple scanning and the simple 3D structure was fabricated. In addition, the etching characteristics of $6\mum$ thick poly-crystalline Si on the insulator was investigated to obtain flat bottom and vertical side wall for MEMS applications.

• Proceedings of the KSRS Conference
• /
• 2002.10a
• /
• pp.750-750
• /
• 2002

The Airship PKNU is a roughly 12 m (32 ft) long blimp, filled with helium, whose two-gasoline power(3hp per engine) are independently radio controlled. The motors and propellers can be tilted and are attached to the gondola through an axle and supporting braces. Four stabilizing fins are mounted at the tail of the airship. To fill in the helium, a valve is placed at the bottom of the hull. The inaugural flight was on jul. 31.2002 at the Pusan, S.korea Most environment monitoring system\ problem use satellite image. But, Low resolution satellite image (multi-spectral) : 1km ∼ 250 m ground resolutions is lows. So, detail information acquisition is hard at the complex terrain. High resolution satellite image (black and white) 30m : The ground resolution is high. But it is high price, visit cycle and delivery time is long So. We want make high accuracy airship photogrammetry system. This airship can catch picture Multi. spectral Aerial photographing (visible, Near infrared and thermal infrared), and High resolution (over 6million pixel). It can take atmosphere datum (Temperature (wet bulb, dew point, general), Pressure (static, dynamic), Humidity, wind speed). this airship is very Quickness that aircraft install time is lower than 30 minutes, it is compact and that conveyance is easy. High-capacity save image (628 cut per 1time (over 6million and 4band(R,G,B,NIR)) and this airship can save datum this High accuracy navigatin (position and rotate angle) by DGPS tech. and Gyro system. this airship will do monitor about red-tide, sea surface temperate, and CH-A, SS and etc.

• Nuclear Engineering and Technology
• /
• v.35 no.4
• /
• pp.356-368
• /
• 2003

Material properties such as coolant specific heat, film heat transfer coefficient, cladding thermal conductivity, surface diffusion coefficient of the multi-bubble are improved in MACSIS-Mod1. The axial power and flux profile module was also incorporated with irradiation history. The performance and feasibility of the updated driver fuel pin have been analyzed for nominal parameters based on the conceptual design for the KALIMER breakeven core by MACSIS-MOD1 code. The fuel slug centerline temperature takes the maximum at 700mm from the bottom of the slug in spite of the nearly symmetric axial power distribution. The cladding mid-wall and coolant temperatures take the maximum at the top of the pin. Temperature of the fuel slug surface over the entire irradiation life is much lower than the fuel-clad eutectic reaction temperature. The fission gas release of the driver fuel pin at the end of life is predicted to be $68.61\%$ and plenum pressure is too low to cause cladding yielding. The probability that the fuel pin would fail is estimated to be much less than that allowed in the design criteria. The maximum radial deformation of the fuel pin is $1.93\%$, satisfying the preliminary design criterion ($3\%$) for fuel pin deformation. Therefore the conceptual design parameters of the driver fuel pin for the KALIMER breakeven core are expected to satisfy the preliminary criteria on temperature, fluence limit, deformation limit etc.

• Journal of Surface Science and Engineering
• /
• v.47 no.5
• /
• pp.239-243
• /
• 2014

The electrical and optical properties of amorphous In-Tin-Zinc-Oxide(ITZO) deposited at room temperature using rf-magnetron sputtering were investigated. The amorphous ITZO thin films were obtained at the composition of In:Sn:Zn = 6:2:2, 4:3:3, and 2:4:4, but the ITZO (8:1:1) showed a crystalline phase of bixbyite structure of In2O3. The resistivity of ITZO could be controlled by oxygen pressure in the sputtering ambient. The resistivity of post-annealed ITZO thin films exhibited the dependence on the amount of Indium. Optical energy band gap and transmittance increased as the amount of indium in ITZO increased. For the device application with ITZO, the bottom-gated thin-film transistor using ITZO as a active channel layer was fabricated. It showed a threshold voltage of 1.42V and an on/off ratio of $5.63{\times}10^7$ operated with saturation field-effect mobility of $14.2cm^2/V{\cdot}s$.

• Journal of Ocean Engineering and Technology
• /
• v.30 no.4
• /
• pp.310-319
• /
• 2016

If a spoiler was attached to the pipeline investigated in a previous study, a strong flow and vortex at the lower part caused scouring and thus an asymmetric pressure distribution, which assisted in the analysis of the self-burial structure where a down force was applied to the pipe. However, only the fluid-pipe interaction was considered, excluding the medium (seabed), when practically burying the pipeline. Thus, this study applied a numerical model (LES-WASS-2D) to directly analyze the non-linear interactions among the fluid, pipe, and seabed in order to perform numerical simulations of a pipeline with a spoiler installed on the seabed. This allowed the self-burial mechanism of a pipeline with a spoiler to be analyzed in the same context as the previous study that considered only the fluid-pipe interaction. However, when a pipeline was installed on the seabed, a strong flow and vortex were found at the front of the bottom, and a spoiler accelerated the fluid resistances. This hydraulic phenomenon will reinforce the scouring and down force on the pipeline. In the general consideration of the numerical analysis results by the specifications and arrangements of the spoiler, a pipeline with a spoiler was found to be the most effective for the self-burial function.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.21 no.1
• /
• pp.72-83
• /
• 2017

A thermo-fluid dynamic analysis was performed through the numerical simulation of a missile canister. Calculation was made in a fixed analytical volume and fully evaporated water was used as a coolant. To analyze the interaction among the hot gas, coolant, and mixture flow, Realizable $k-{\varepsilon}$ turbulence and VOF(Volume Of Fluid) model were chosen and parametric study was performed with the change of coolant flow rate. It could be found that the pressure on the canister top nonlinearly increased with the increase of coolant flow rate. Temperature and coolant distribution were closely related to the flow behavior in canister. Temperature on the canister bottom indicated a decrease being proportional to coolant flow rate in early times but after a specific time, the temperature increased with the tendency being reversed. In addition, the early part of temperature showed a fluctuating phenomenon because of the overall circulatory flow of mixture gas.

• Corrosion Science and Technology
• /
• v.20 no.5
• /
• pp.308-314
• /
• 2021

Neutron dose level at bottom head of a reactor pressure vessel (RPV) was calculated using reactor vessel neutron transport for a Korean nuclear power plant A. At 34 EFPY with a 40-year (2042) design life after plating repair, irradiation fast neutron effect was 6.6x10¹⁵ n/cm². As helium(He) gas can be generated by Ni only at 1/10⁶ level of 5 × 10²¹ n/cm², He generation possibility in the Ni plating layer is very little during 40 years of operation (2042, 34 EFPY). Thermal neutrons can significantly affect the generation of He from Ni metal. At 10 years after a repair, He can be generated at a level of about 0.06 appm, a level that can add general welding repair without any consideration. After 40 years of repair, 9.8 appm of He may be generated. Although this is a rather high value, it is within the range of 0.1 to 10 appm when welding repair can be applied. Clad repair by Ni electroplating technology is expected to greatly improve the operation efficiency by improving the safety and shortening the maintenance period of the nuclear power plant.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.23 no.4
• /
• pp.28-34
• /
• 2019

In this study, pin-fin arrays, which are widely used for cooling turbine blades, were studied. The vortex generator in pin-fin arrays is located in front of the circular tube. The cross-section of the vortex generator is NACA-9410. The purpose of this study is to analyze heat transfer performance and flow characteristics of pin-fin arrays. The position of vortex generator is changed with the vertical flow direction on the bottom wall. Pin-fin arrays were calculated with 6000, 10000 and 15000 Reynolds number. The commercial program ANSYS v18.0 CFX and the turbulence model $k-{\omega}$ SST were used. As a result, the heat transfer performance increased up to 5.8% and pressure loss increased less than 1%.

• Journal of the Korean Geosynthetics Society
• /
• v.18 no.1
• /
• pp.55-65
• /
• 2019

This paper describes results of experimental and numerical analyses, in order to analyze a reinforcement effect of concrete mat on open cut restoration of underground cavity. The plate loading tests were conducted to evaluate a reinforcement effect of concrete mat, at reinforcement depths from the ground surface of 10 cm, 20 cm, and 30 cm. The result showed that the reduction ratio of stress (earth pressure) was about 60% at all reinforcement depth. The reinforcement effect considering ground surface settlement and reduction ratio of stress based on laboratory tests and numerical analysis was significant, at reinforcement depths from the ground surface of 10 cm~20 cm. LFWD test results showed that subgrade modulus was the largest when concrete mat was installed 20 cm below ground surface. Therefore, it is effective to reinforce concrete mat within 20 cm from the surface, when the underground cavity due to damage of underground utilities was formed in the height direction to the bottom of the pavement layer.