• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.1
• /
• pp.66-78
• /
• 2004

The objective of this study was to apply the vibration technique to reduce the viscosity of bonding adhesives and thereby compare the bond strength and resin penetration in enamel and dentin achieved with those gained using the conventional technique and vibration technique. For enamel specimens, thirty teeth were sectioned mesio-distally. Sectioned two parts were assigned to same adhesive system but different treatment(vibration vs. non-vibration). Each specimen was embedded in 1-inch inner diameter PVC pipe with a acrylic resin. The buccal and lingual surfaces were placed so that the tooth and the embedding medium were at the same level. The samples were subsequently polished silicon carbide abrasive papers. Each adhesive system was applied according to its manufacture's instruction. Vibration groups were additionally vibrated for 15 seconds before curing. For dentin specimen, except removing the coronal part and placing occlusal surface at the mold level, the remaining procedures were same as enamel specimen. Resin composite(Z250. 3M. U.S.A.) was condensed on to the prepared surface in two increments using a mold kit(Ultradent Inc., U.S.A.). Each increments was light cured for 40 seconds. After 24 hours in tap water at room temperature, the specimens were thermocycled for 1000cycles. Shear bond strengths were measured with a universal testing machine(Instron 4465, England). To investigate infiltration patterns of adhesive materials, the surface of specimens was examined with scanning electron microscope. The results were as follows: 1. In enamel the mean values of shear bond strengths in vibration groups(group 2, 4, 6) were greater than those of non-vibration group(group 1, 3, 5). The differences were statistically significant except AQ bond group. 2. In dentin, the mean values of shear bond strengths in vibration groups(group 2, 4, 6) were greater than those of non-vibration groups(group 1, 3, 5). But the differences were not statistically significant except One-Up Bond F group. 3. The vibration group showed more mineral loss in enamel and longer resin tag and greater number of lateral branches in dentin under SEM examination.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.38 no.4
• /
• pp.348-354
• /
• 2011

Composite resin has been widely used for eroded enamel. But, as there have been many reports about the differences in physicochemical characteristics of eroded enamel compared with sound enamel, an additional effort was thought necessary to obtain the optimal bond strength. As a possible answer, we came to think about the application of infiltrant resin which is known to have an excellent penetration capacity into enamel. This study was performed for the purpose of comparing the bond strength of composite restoration with or without infiltrant resin under adhesives on the artificially eroded enamel. 60 extracted sound maxillary primary incisors were selected and divided into group 1, 2, 3 according to the number of artificial erosion cycling for 5 minute duration in 1% citric acid of pH 3.2 at $37^{\circ}C$. And the labial surfaces were divided into 3 areas; group A, only resin adhesive was used, group I, only infiltrant resin, group IA, infiltrant resin followed by resin adhesive. Afterwards, every specimen was restored with composite resin. Microtensile bond strength was measured and failure modes were observed. The obtained results were as follows: 1. In comparing the bond strength by the degree of enamel erosion, it was revealed the highest bond strength in group 1, followed by group 2 and 3, showing the lowest bond strength in most eroded group(p<0.05). 2. In comparing the bond strength by surface treatment methods, group IA and I showed higher value than group A(p<0.05), with unsignificant difference between group I and IA(p>0.05). 3. In observation of failure mode, it was shown higher frequency of cohesive failure in order of 1-2-3 and IA-I-A. Conclusively, it was shown decreasing tendency of bond strength as the enamel is more eroded, and infiltrant resin was thought helpful to replace or add to the resin adhesive for optimal bonding with eroded enamel.