• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제43회 하계 정기 학술대회 초록집
• /
• pp.386-386
• /
• 2012

For white light emitting diode (LED) applications, it has been reported that Y3Al5O12:Ce3+ (YAG:Ce) in nano-sized phosphor performs better than it does in micro-sized particles. This is because nano-sized YAG:Ce can reduce internal light scattering when coated onto a blue LED surface. Recently, there have been many reports on the synthesis of nano-sized YAG particles using bottom-up method, such as co-precipitation method, sol-gel process, hydrothermal method, solvothermal method, and glycothermal method. However, there has been no report using top-down method. Top-down method has advantages than bottom-up method, such as large scale production and easy control of doping concentration and particle size. Therefore, in this study, nano-sized YAG:Ce phosphors were synthesized by a high energy beads milling process with varying beads size, milling time and milling steps. The beads milling process was performed by Laboratory Mill MINICER with ZrO2 beads. The phase identity and morphology of nano-sized YAG:Ce were characterized by X-ray powder diffraction (XRD) and field-emission scanning electron microscopy (FESEM), respectively. By controlling beads size, milling time and milling steps, we synthesized a size-tunable and uniform nano-sized YAG:Ce phosphors which average diameters were 100, 85 and 40 nm, respectively. After milling, there was no impurity and all of the peaks were in good agreement with YAG (JCPDS No. 33-0040). Luminescence and quantum efficiency (QE) of nano-sized YAG:Ce phosphors were measured by fluorescence spectrometer and QE measuring instrument, respectively. The synthesized YAG:Ce absorbed light efficiently in the visible region of 400-500 nm, and showed single broadband emission peaked at 550 nm with 50% of QE. As a result, by considering above results, high energy beads milling process could be a facile and reproducible synthesis method for nano-sized YAG:Ce phosphors.

• 한국산업보건학회지
• /
• 제8권2호
• /
• pp.196-208
• /
• 1998

To improve the quality of environmental measurements and evaluation of the workplace air in the pigment manufacturing industries, we analyzed metal(chromium, cadmium, lead, iron, cobalt, manganese, antimony, titanium, arsenic, and selenium) concentrations by ICP-AES in sixty seven samples of inorganic bulk pigments which are produced and/or used in Korea. We also collected MSDS which has to be supplied by manufacturer and/or supplier and posted in the workplace according to the Hazard Communication Standards, and compared the number of metals listed in each MSDS with the number of metals determined by ICP-AES. Results were as followed; 1. Among seventeen yellowish-colored samples, chromium(2~19%) and lead(0.1~61%) were the two major metals. In thirteen reddish-colored samples, iron was the major component with 37~81%. Cobalt and manganese were detected in blue-colored samples with less than 1%, while antimony and titanium were the major two metals in white-colored pigments with 178~300 ppm and with 36~65%, respectively. 2. In area samples collected in workplace air(one pigments producing factory and five retailer stores), iron and manganese were detected but the concentrations not exceeded the TLVs(1 and $5mg/m^3$, respectively). In three of fifteen samples, the concentrations of lead exceeded the TLV ($0.05mg/m^3$). 3. Two out of seven companies provided MSDS, and the average provision rate was 22.4%. And the coincidence rate of the number of metals referenced in MSDS and determined by ICP-AES mostly accorded, but in one sample, different metal was detected from MSDS. In summary, metals have to be concerned in evaluation of the workplace air dealing with compounds of inorganic pigments dust are cobalt, chromium, iron, manganese, lead and antimony, and these are simultaneously determined by ICP-AES. Taking this opportunity, it is needed to reinforce that the personnel is to be concerned about prevention of workers' ill health regarding to provision of MSDS.